Ultraviolet curing paint for sealing pine turpentine and preparation method thereof

A technology for curing coatings and turpentine, applied in polyester coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems such as unsatisfactory sealing effect and inability to seal turpentine well, achieve good and lasting sealing effect, reduce Risk of delamination and peeling of paint film, effect of improving sealing effect

Inactive Publication Date: 2020-04-28
珠海展辰新材料股份有限公司 +1
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a UV-curable coating for sealing pine turpentine and a preparation method thereof, aiming to solve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultraviolet curing paint for sealing pine turpentine and preparation method thereof
  • Ultraviolet curing paint for sealing pine turpentine and preparation method thereof
  • Ultraviolet curing paint for sealing pine turpentine and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] On the other hand, the embodiment of the present invention also provides a kind of preparation method that is used for sealing the ultraviolet curing coating of pine turpentine, comprises the following steps:

[0031] S01, each component is weighed according to the formula of the UV-curable coating of pine wood turpentine described in the embodiment of the present invention;

[0032] S02, subjecting the water-soluble UV resin, polyester acrylate resin, polyurethane acrylate, wetting agent, defoamer and leveling agent to a first mixing treatment to obtain a first mixing product;

[0033] S03. Add the photoinitiator and active monomer into the first mixture, and perform a second mixture treatment to obtain the UV-curable coating of sealed pine turpentine.

[0034] The preparation method of the UV-curable coating for sealing pine wood turpentine provided by the embodiment of the present invention has the characteristics of simple process, low cost and high efficiency; when...

Embodiment 1

[0038] The content of each component by weight of the UV-curable coating provided in this embodiment is shown in Table 1:

[0039] Table 1

[0040]

[0041]

[0042] In the above table 1, the polyester acrylate resin is Boxing Chemical B522; the wetting agent is BYK-190; the defoamer is non-silicon defoamer Tego-920; the leveling agent is BYK-358N; It is Ciba's trademark 1173; the active monomer is Cytec's polyacrylic acid monomer.

[0043] The preparation method of the UV-curable coating provided in this embodiment is as follows:

[0044] S11: Weigh the raw materials of each component according to the components contained in the UV-curable coating in the above Table 1 and their parts by weight;

[0045] S12: Stir the above-mentioned water-soluble UV resin, polyester acrylate resin, polyurethane acrylate, wetting agent, defoamer, and leveling agent at a temperature below 50°C and a speed of 800-1000 rpm for 10-15 minutes.

[0046] S13: Then add photoinitiator and some...

Embodiment 2

[0054] The content of each component of the UV-curable coating provided in this embodiment is shown in Table 3 (in parts by weight).

[0055] table 3

[0056] Component parts by weight Water-soluble UV resin 35.0 copies Polyester acrylate resin 20.0 copies urethane acrylate 15.0 copies Defoamer 0.1 part D 1.5 servings leveling agent 1.0 copies Photoinitiator 3.0 copies active monomer 24.4 copies

[0057] In the above table 3, the polyester acrylate resin is Boxing Chemical’s B522; the wetting agent is Rohm and Haas’ water-based paint wetting and dispersing agent; 358N; the photoinitiator is Ciba company brand 1173; the active monomer is the polyacrylic acid monomer of Cytec. The preparation method of the UV-curable coating provided in this embodiment is basically the same as that in Embodiment 1, and will not be repeated here.

[0058] The above-mentioned UV-curable coating is sprayed on the surface of p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of paint, and particularly relates to an ultraviolet curing paint for sealing pine turpentine and a preparation method thereof. The ultraviolet curing paint comprises the following components in parts by weight: 10-60 parts of water-soluble UV resin; 5-30 parts of polyester acrylate; 5-20 parts of urethane acrylate; 2-4 parts of a photoinitiator; 1-2 parts of a wetting agent; 0.05-0.2 parts of a defoaming agent; 0.1-2 parts of a leveling agent; and 5-30 parts of an active monomer. According to the ultraviolet curing paint for sealing the pine turpentine, the sealing effect of the turpentine in pine wood can be improved, the risk of delaminating and falling of a paint film is reduced, and the decorative effect of a product is improved.

Description

technical field [0001] The invention belongs to the technical field of coatings, in particular to an ultraviolet curing coating for sealing pine turpentine and a preparation method thereof. Background technique [0002] In furniture painting, some woods contain heavy oils, such as pine containing turpentine. Due to the oil contained in these woods, it is difficult to guarantee the adhesion of the paint when the furniture is painted. In places with heavy oil, there may be no adhesion, and the paint may directly delaminate and fall off. [0003] At present, water-based UV (ultraviolet light) coatings are more effective in sealing pine turpentine, but due to the low solid content during construction, generally less than 40%, the filling is not enough, and the sealing effect is relatively poor in places where turpentine is heavier. Difference. Therefore, the prior art needs to be improved. Contents of the invention [0004] The purpose of the present invention is to provide...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D201/00C09D175/14C09D167/06
CPCC08L2201/08C08L2205/035C09D201/00C08L75/14C08L67/06
Inventor 汪汉军陈寿生郭玉朱强刘志刚
Owner 珠海展辰新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap