A kind of composite hydrogel wound dressing and preparation method thereof

A composite hydrogel and wound dressing technology, applied in bandages, medical science and other directions, can solve the problems of long gelation time, cumbersome cross-linking steps, uneven hydrogel, etc., and achieve stable performance, good antibacterial performance, and preparation simple method effect

Active Publication Date: 2022-06-24
FUZHOU UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The prepared fish skin collagen-chitosan composite alginate hydrogel dressing can effectively shorten the healing period, eliminate wound inflammation, and inhibit scar formation, and has a good prospect and application direction in wound care. There are many defects, as follows: (1) Sodium alginate, fish skin collagen, polyvinyl alcohol and glycerin are used to prepare the gel solution, polyvinyl alcohol is an organic compound, which is harmful to the human body; Place it under the condition of ℃ for 2 hours, and then add the cross-linking agent prepared by chitosan and anhydrous calcium chloride to carry out the cross-linking reaction. The whole cross-linking process usually takes several hours to realize gelation. production efficiency, and the cross-linking steps are cumbersome, which increases uncertainties; (3) Compared with other hydrogels, Ca 2+ The hydrogel prepared by cross-linking has the characteristics of unevenness, hardness and brittleness, which is not conducive to the comfort of the wound
In addition, the incorporation of calcium ion impurities has a certain impact on wound healing; (4) chitosan, as a natural antibacterial agent, has poor antibacterial effect compared with antibiotics, and the antibacterial concentration and antibacterial concentration of chitosan The performance is closely related to its preparation process, molecular weight and molecular structure. At present, chitosan is mainly obtained through extraction methods, which requires high control of raw materials and production processes, making it difficult to grasp the production stability of chitosan, which also leads to The antibacterial effects of chitosan products on the market are uneven, which increases the trouble of screening chitosan

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite hydrogel wound dressing and preparation method thereof
  • A kind of composite hydrogel wound dressing and preparation method thereof
  • A kind of composite hydrogel wound dressing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0037] 1. Preparation of aminated collagen: Dissolve 5 g of fish scale collagen in 200 mL of PBS buffer solution, add ethylenediamine in a mass-to-volume ratio of 1:1 after dissolving, mix well and adjust the pH to 5.5; then press The mass ratio to collagen was 1:1, 1-ethyl-(3-dimethylaminopropyl) carbodiimide hydrochloride was added and reacted for 6 h to obtain a reaction solution, which was dialyzed and frozen. After drying, the aminated fish scale collagen was obtained, and the grafting rate was 27%.

[0038] 2. Preparation of oxidized sodium alginate:

[0039] (1) Disperse 5 g of sodium alginate in 50 mL of anhydrous ethanol to obtain a sodium alginate solution, dissolve 5 g of sodium periodate in 100 mL of deionized water and slowly pour it into the sodium alginate solution, and then put it in 100 mL of deionized water. The reaction was carried out in the dark at 25 °C for 6 h, and then 5 mL of ethylene glycol was added to terminate the reaction to obtain a reaction sol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
tensile strengthaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention provides a composite hydrogel wound dressing and a preparation method thereof, which is based on aminated collagen and oxidized sodium alginate, and is loaded with two polypeptides of polymyxin B sulfate and bacitracin Antibiotics, AC / OSA‑PB composite hydrogel dressings are prepared by Schiff base reaction, the preparation method of the present invention is simple to operate, and has low requirements on reaction conditions, and can be gelled in a short time, which is beneficial to large-scale production, and the obtained The wound dressing not only has a good bactericidal effect, but also can maximize the HSF cell migration rate and HSF cell proliferation rate, has an excellent ability to promote wound healing, and also has mechanical properties and mechanical properties suitable for skin wounds.

Description

technical field [0001] The invention belongs to the technical field of biomedical materials, in particular to a composite hydrogel wound dressing and a preparation method thereof. Background technique [0002] Skin wound repair is one of the major challenges facing the medical field. According to statistics from the World Health Organization, millions of people around the world suffer from skin injuries every year, and about 180,000 of them die from burns rather than fatal burns. is the main causative factor. Large-scale non-lethal wounds destroy the normal physiological function of the skin. Without timely and effective treatment, the wound is likely to be invaded by microorganisms and become infected, thereby delaying the healing of the wound, and in severe cases, it will be life-threatening. Therefore, effective control of wound infection and rapid wound healing are important ways to reduce patient mortality. Full-thickness skin wound tissue undergoes a complex process ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/075C08L89/00C08L5/04C08B37/04C08H1/00A61L26/00
CPCC08J3/075C08B37/0084C08H1/00A61L26/008A61L26/0033A61L26/0023A61L26/0047A61L26/0066A61L26/0061A61L2300/404A61L2300/252C08J2389/00C08J2405/04C08J2305/04C08J2489/00C08L89/00C08L5/04
Inventor 郑允权冯晓莲石贤爱杨建民
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products