A kind of antibacterial varnish for color plate and color plate production process

A production process, antibacterial cleaning technology, applied in the field of antibacterial varnish for color plates and color plate production technology, can solve problems such as poor antibacterial properties of color plates, and achieve the effects of improving antibacterial performance, improving ion exchange efficiency and high stability

Active Publication Date: 2021-10-26
合肥河钢新材料科技有限公司 +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The above-mentioned existing technical solutions have the following defects: the surface spray paint disclosed in the above-mentioned invention patent and the bottom surface roller paint formula do not contain components with antibacterial properties, and the color plates prepared by the above-mentioned process have poor antibacterial properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Embodiment 1 is an antibacterial varnish for a color plate disclosed by the present invention and a production process for a color plate. The antibacterial varnish comprises the following components by mass fraction: 27.5% of polyester resin, 20% of methanol-modified melamine formaldehyde resin, propylene glycol methyl ether acetic acid 15% ester, 10% 2-methylpropanol acetate, 10% solvent naphtha, 2.5% cyclohexanone, 5% xylene, 8% octanol and nano silver-loaded silicone with a particle size of 100nm %;

[0039] The preparation method of nano silver-loaded silicone is as follows: 1) Weigh 0.01g modified silicone gel and disperse it in 40mL distilled water, add 10mL silver ammonia solution (concentration is 0.075mol / L) to it, and magnetically stir Disperse for 12 hours; 2) Transfer the dispersion liquid into the reaction bottle, add 30mL of absolute ethanol, and electric stir (constant speed 400r / min) for 30min at 25°C; 3) Add 3mL NaOH aqueous solution (concentration: 0....

Embodiment 2

[0052] Embodiment 2 is an antibacterial varnish for color plates disclosed by the present invention and a production process for color plates. The antibacterial varnish comprises the following components by mass fraction: 29% of polyester resin, 30% of methanol-modified melamine formaldehyde resin, propylene glycol methyl ether acetic acid 10% ester, 5% 2-methyl propanol acetate, 10% solvent naphtha, 2% cyclohexanone, 2% xylene, 10% octanol and nano silver-loaded silicone with a particle size of 100nm %;

[0053] The preparation method of nano silver-loaded organosilicon is the same as embodiment 1;

[0054] Modified organosilicon gel modification method is the same as embodiment 1;

[0055] Color plate production process is the same as embodiment 1.

Embodiment 3

[0056] Embodiment 3 is an antibacterial varnish for color plates disclosed by the present invention and a production process for color plates. The antibacterial varnish comprises the following components in mass fractions: 15% polyester resin, 30% methanol-modified melamine formaldehyde resin, propylene glycol methyl ether acetic acid 15% ester, 15% 2-methyl propanol acetate, 10% solvent naphtha, 5% cyclohexanone, 5% xylene, 4% octanol and nano silver-loaded silicone with a particle size of 100nm %;

[0057] The preparation method of nano silver-loaded organosilicon is the same as embodiment 1;

[0058] Modified organosilicon gel modification method is the same as embodiment 1;

[0059] Color plate production process is the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an antibacterial varnish for color plates and a production process for color plates. The antibacterial varnish contains the following components in mass fractions: polyester resin 15-40%, methanol-modified melamine formaldehyde resin 10-30%, propylene glycol methyl ether acetate 0~15%, 2-methyl propanol acetate 0~15%, solvent naphtha 0~10%, cyclohexanone 0~5%, xylene 0~5%, octanol 1~10% and Nano silver-loaded silicone 1-2%; color plate production process includes the following steps: S1. Material preparation (including S1-1 substrate uncoiling and S1-2 primer, back paint, intermediate paint, ink and antibacterial varnish preparation); S2. Substrate pretreatment; S3. Primer coating; S4. Back paint coating; S5. Intermediate coating; S6. Ink printing; S7. Varnish coating. The antibacterial varnish prepared by the invention has good antibacterial performance, so that the colored steel plate prepared by using the antibacterial varnish has good antibacterial performance.

Description

technical field [0001] The invention relates to the technical field of film coating on the surface of steel plates, in particular to an antibacterial varnish for color plates and a production process for color plates. Background technique [0002] Colored steel plate, also known as color coated steel plate, is a product made of cold-rolled steel plate, electro-galvanized steel plate, hot-dip galvanized steel plate or galvanized steel plate as the substrate after various surface treatment processes and then baked. [0003] The traditional method of producing colored steel plates is usually to perform pretreatment such as degreasing on the substrate before passivation treatment. After the passivation film is formed on the surface of the substrate, the substrate is sprayed with primer, dried, sprayed with topcoat, and dried in sequence. , color ink printing or color film lamination and other processes to prepare color steel plates that meet production standards. Color steel pl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/00C09D161/32C09D5/14B05D7/26B05D7/00B05D5/00
CPCB05D5/00B05D7/26B05D7/576B05D2320/00B05D2401/10B05D2501/00B05D2508/00B05D2518/00C09D5/14C09D161/32C09D167/00C09D7/67C09D7/68C08L61/32C08K9/12C08K3/015C08K5/0058C08L67/00B05D2425/01
Inventor 周同春赵秀娟邹炎斌付强孙良涛代玉江
Owner 合肥河钢新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com