Nano composite fiber and manufacturing method thereof

A technology of nanocomposite fiber and chitosan solution, which is applied in fiber treatment, fiber chemical characteristics, conjugated synthetic polymer artificial filament, etc. Spinability and shape issues

Inactive Publication Date: 2020-12-11
邵阳县合和工业材料有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The electrospinning of chitosan composite nanofibers has problems such as pure spinning difficulties. By adding polymer polymer polyvinyl alcohol and adjusting process parameters, chitosan/polyvinyl alcohol composite

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano composite fiber and manufacturing method thereof
  • Nano composite fiber and manufacturing method thereof
  • Nano composite fiber and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The implementation mode of the present invention is illustrated by specific specific examples below, and those who are familiar with this technology can easily understand other advantages and effects of the present invention from the contents disclosed in this description. Obviously, the described embodiments are a part of the present invention. , but not all examples. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0026] It should be noted that, in the description of the present invention, terms such as "middle", "upper", "lower", "horizontal", "inner" and other indicated directions or positional relationships are positional relationships, which are only for convenience Describes, but does not indicate or imply that the device or element must have a particular orientation, be constructed in a particular or...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a nano composite fiber. The nano composite fiber is prepared by the following steps: chitosan is dissolved in an acetic acid aqueous solution to prepare a chitosan solution withthe concentration of 5.5%-5.9%; and 28-45 parts of a 11%-15% polyvinyl alcohol solution is added into 85-120 parts of the chitosan solution and blended, then uniform ultrasonic dispersion is conducted, and still standing and defoaming are conducted to obtain a spinning solution. The invention also provides a preparation method of the nano composite fiber. According to the nano composite fiber, the weight part ratio of the chitosan solution to the polyvinyl alcohol solution is given, so that the nano composite fiber with smooth morphology and strong interaction can be obtained; and by improving process parameters, the spinning performance of chitosan is improved, and the morphological characteristics of the nano composite fiber can be improved.

Description

technical field [0001] The invention relates to the technical field of nanocomposite fiber preparation, in particular to a nanocomposite fiber and a preparation method. Background technique [0002] The electrospinning of chitosan composite nanofibers has problems such as pure spinning difficulties. By adding polymer polymer polyvinyl alcohol and adjusting process parameters, chitosan / polyvinyl alcohol composite nanofibers were prepared, which significantly improved the chitosan composite nanofibers. Spinning performance of sugar, but polyvinyl alcohol is difficult to dissolve, which affects the spinnability and shape of the fiber. Contents of the invention [0003] The nanocomposite fiber provided by the invention provides the ratio of chitosan solution and polyvinyl alcohol solution in parts by weight, and can obtain the nanocomposite fiber with smooth appearance and strong interaction. [0004] The invention also provides a preparation method of the nanocomposite fiber...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F8/10D01F8/18D01D5/00
CPCD01F8/18D01F8/10D01D5/003D01D5/0092
Inventor 莫加委
Owner 邵阳县合和工业材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap