A method for preparing artificial high-strength lightweight aggregate ceramsite sand by using perlite

A technology of ceramsite sand and light aggregate, which is applied in the preparation of ceramsite sand and the field of artificial light aggregate and high strength ceramsite, can solve the problems of low cylinder compressive strength, difficulty in applying structural concrete, and heavy environmental burden, so as to reduce production costs. , Great design direction and flexibility, the effect of reducing energy consumption

Active Publication Date: 2022-04-19
NANJING UNIV OF SCI & TECH +1
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This invention has the following deficiencies: (1) adopts two sintering treatments, prolongs the production process, increases energy consumption, and is a big burden on the environment
(2) The cylinder compressive strength of ceramsite is low, so it is difficult to apply to structural concrete
This invention also has the following problems: (1) the sintering temperature is relatively high, which not only requires higher production equipment, but also consumes a lot of energy
(2) This preparation method needs to add auxiliary agent additionally, has increased production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing artificial high-strength lightweight aggregate ceramsite sand by using perlite
  • A method for preparing artificial high-strength lightweight aggregate ceramsite sand by using perlite
  • A method for preparing artificial high-strength lightweight aggregate ceramsite sand by using perlite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0084] 1. Known cement density ρ 水泥 =3150kg / m 3 , expanded perlite particle size 0.1-1.5mm, apparent density ρ 珍珠岩 =348kg / m 3 , fly ash apparent density ρ 粉煤灰 =2200kg / m 3 , Density ρ of absorbent resin 吸水树脂 ≈1000kg / m 3

[0085] In this embodiment, the amount of each material used per cubic meter is used as the basis for calculation, and the volume ratio and addition amount of each raw material are shown in Table 2 below.

[0086] In table 2 embodiment 1, each material admixture per cubic meter, unit kg, m 3

[0087]

[0088] The formula is calculated theoretically to obtain the finished ceramsite sand, and the apparent density of the ceramsite sand is 1782.23kg / m 3 .

[0089] 2. First take 0.01m 3 The expanded perlite is pre-wetted to reach saturation and the surface is dry for later use, according to 0.07m 3 Weigh cement by volume fraction, weigh 50kg of pre-wet water-absorbent resin (absorb water more than 20 times its own mass), calculate the amount of fly as...

Embodiment 2

[0099] 1. Known cement density ρ 水泥 =3150kg / m 3 , expanded perlite particle size 0.1-1.5mm, apparent density ρ 珍珠岩 =348kg / m 3 , fly ash apparent density ρ 粉煤灰 =2200kg / m 3 , Density ρ of absorbent resin 吸水树脂 ≈1000kg / m 3

[0100] Each material of the present invention cooperates and adopts the consumption per cubic meter as calculation basis, and wherein each raw material volume ratio and admixture are as follows Table 3.

[0101] The amount of each material added per cubic meter in the embodiment 2 of table 3, unit kg, m 3

[0102]

[0103] The formula is calculated theoretically to obtain the finished ceramsite sand, and the apparent density of the ceramsite sand is 1488.67kg / m 3 .

[0104] 2. First take 0.25m 3 The expanded perlite is pre-wetted to reach saturation and the surface is dry for later use, according to 0.08m 3 The volume fraction weighs cement, weighs 20kg of pre-wet water-absorbing resin (water-retaining state), and calculates the amount of fly as...

Embodiment 3

[0113] 1. Known cement density ρ 水泥 =3150kg / m 3 , perlite particle size 0.1-1.5mm, apparent density ρ 珍珠岩 =348kg / m 3 , fly ash apparent density ρ 粉煤灰 =2200kg / m 3 , Density ρ of absorbent resin 吸水树脂 ≈1000kg / m 3

[0114] Each material of the present invention cooperates and adopts the consumption per cubic meter as calculation basis, and wherein each raw material volume ratio and admixture are as follows table 4.

[0115] Each material admixture per cubic meter in table 4 embodiment 3, unit kg, m 3

[0116]

[0117] The formula is calculated theoretically to obtain the finished ceramsite sand, and the apparent density of the ceramsite sand is 1217.85kg / m 3 .

[0118] 2. First take 0.45m 3 The expanded perlite is pre-wetted to reach saturation and the surface is dry for later use, according to 0.09m 3 The volume fraction weighs cement, weighs 10kg of pre-wet water-absorbing resin (water-retaining state), and calculates the amount of fly ash according to the formula...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing artificial high-strength lightweight aggregate ceramsite sand by using perlite, which includes pre-wetting and stirring of the mixture, nucleation of sand particles, ball growth, ceramsite sand static stop pre-cultivation, hydrothermal reaction, and product Screening six-step process. Specifically, the pre-wet expanded perlite powder, pre-wet water-absorbing resin, fly ash, cement and other raw materials are pre-wetted and stirred to make a mixture, and the mixture is sent into a rolling ball disc, and the diameter is formed by centrifugal rolling. Small ball core, the ball core rolls and bonds powder in the ball forming plate, and then grows into a ball to make ceramsite sand. The larger diameter is ceramsite, and the smaller diameter is ceramsite. The ceramsite sand is statically Stop maintenance and hydrothermal reaction to further increase the strength of the ceramsite, and finally sieve the product to obtain light and high-strength ceramsite and ceramsite.

Description

technical field [0001] The invention relates to a preparation method of artificial lightweight aggregate high-strength ceramsite and ceramsite, which belongs to the technical field of concrete materials. Background technique [0002] Ceramsite sand, ceramsite with a larger diameter of 5-30mm, and ceramsite with a smaller diameter below 5mm, as a kind of artificial aggregate, plays an important role in improving the performance of concrete. Adding an appropriate amount of ceramsite sand to concrete can firstly reduce the amount of cement and reduce production costs, and secondly, it can improve the workability of cement mortar during mixing and improve the working performance of concrete. In addition, after adding ceramsite sand to the concrete, the bleeding phenomenon of the concrete is reduced, the hydration of the cement is promoted, and the water retention performance of the concrete is improved. The ceramsite sand can be adjusted according to the particle gradation requ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B18/02C04B28/04C04B38/08C04B38/06
CPCC04B18/027C04B28/04C04B38/08C04B38/06C04B14/185C04B2103/0051C04B18/08C04B22/002
Inventor 崔崇任许乐崔晓昱王朋涛李天君
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com