Water-based aerogel efficient fire extinguishing agent and preparation method thereof
An aerogel and fire extinguishing agent technology, which is applied in the field of water-based aerogel high-efficiency fire extinguishing agent, can solve the problems of weak flame retardant performance, narrow application range of fire extinguishing objects, low fire extinguishing efficiency, etc., and achieves improved efficiency, good fire protection function and Flame retardant function, the effect of increasing uniformity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0029]Example 1
[0030]The water-based aerogel high-efficiency fire extinguishing agent of this embodiment, based on the total amount of raw materials prepared, includes the following raw material components with quality content:
[0031]
[0032]Such asfigure 1 The preparation flow chart shown, the preparation method of the water-based aerogel high-efficiency fire extinguishing agent in this embodiment, includes the following steps:
[0033](1) Preparation of aerogel sol: firstly modify the surface of silica aerogel powder, heat treatment at 220°C under clean nitrogen for 4 hours; then mix it evenly with the selected amount of template agent and fully grind it 4 Hours; after milling and mixing uniformly, add an appropriate amount of deionized water and stir for 2.5 hours, the amount of deionized water is not less than 25wt% of the total, control the rotation speed of the mixer to 120-150r / min to obtain an aerogel sol, ready for use ;
[0034](2) Preparation of water-based flame retardant: In add...
Example Embodiment
[0036]Example 2
[0037]The water-based aerogel high-efficiency fire extinguishing agent of this embodiment, based on the total amount of raw materials prepared, includes the following raw material components with quality content:
[0038]
[0039]Such asfigure 1 The preparation flow chart shown, the preparation method of the water-based aerogel high-efficiency fire extinguishing agent in this embodiment, includes the following steps:
[0040](1) Preparation of aerogel sol: firstly modify the surface of silica aerogel powder, heat treatment for 3 hours under the condition of purifying nitrogen at 250℃; then uniformly mix with selected amount of template agent and fully grind 4 Hours; after milling and mixing uniformly, add an appropriate amount of deionized water and stir for 2.5 hours. The amount of deionized water is not less than 30wt% of the total amount. Control the rotation speed of the mixer to 150-180r / min to obtain an aerogel sol. ;
[0041](2) Preparation of water-based flame retardant: ...
Example Embodiment
[0043]Example 3
[0044]The water-based aerogel high-efficiency fire extinguishing agent of this embodiment, based on the total amount of raw materials prepared, includes the following raw material components with quality content:
[0045]
[0046]Such asfigure 1 The preparation flow chart shown, the preparation method of the water-based aerogel high-efficiency fire extinguishing agent in this embodiment, includes the following steps:
[0047](1) Preparation of aerogel sol: firstly modify the surface of silica aerogel powder, heat treatment for 5 hours under clean nitrogen at 200℃; then mix it evenly with the selected amount of template agent and fully grind 3 Hours; after milling and mixing uniformly, add an appropriate amount of deionized water and stir for 2.5 hours, the amount of deionized water is not less than 25wt% of the total, control the rotation speed of the mixer to 120-150r / min to obtain an aerogel sol, ready for use ;
[0048](2) Preparation of water-based flame retardant: In additio...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap