Preparation method of camel hair protein fibers

A protein fiber and camel hair technology, which is applied in the field of camel hair protein fiber preparation, can solve the problems of fiber physical performance index deterioration, failure to reflect potential value, high protein fiber defects, etc., to achieve high value of excited negative oxygen ions, reduced quantity, The effect of high camel hair protein content

Inactive Publication Date: 2021-08-27
郑州诺肯新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Camel hair is a natural animal protein fiber, which is rich in resources in our country. However, due to the lag of research and the imperfection of textile technology, it is only used in low-end industries such as woolen spinning, which cannot reflect its potential value, resulting in a large resource. waste
At present, most of the cellulose fibers with modified functions are added to the fibers by blending effective additives. This process will cause partial loss of protein due to the double diffusion process of the coagulation bath during the spinning process, resulting in raw material waste
During production in the hot summer, the pre-configured protein raw materials will be denatured due to high temperature, and should not be stored for a long time, resulting in difficult and unstable production
By injection before blending, if too much protein is added, the spinnability of the fiber will be affected, resulting in high defects in the protein fiber and the deterioration of the physical performance index of the fiber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of camel hair protein fibers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0036] Embodiment: a kind of preparation method of camelid protein fiber, described preparation method comprises the following steps:

[0037] (1) Preparation of Camelin Crosslinking Liquid

[0038] Add 250 g of hydrolyzed camel hair protein to 800 g of deionized water, heat up to 40° C., stir for 2 hours, and then filter through a 200-mesh filter to obtain a hydrolyzed camel hair protein solution.

[0039] Heat up 600g of cross-linking agent to 40°C, add it into the hydrolyzed camelid protein solution, stir and mix the two at a constant temperature of 40°C for 45 minutes at a stirring speed of 40r / min, and let stand for 8 hours after stirring; adjust the temperature to 25 ℃, filtered once with an 80-mesh filter to prepare the camelid protein cross-linking liquid.

[0040] (2) Pre-opening treatment of viscose fiber

[0041] The viscose fiber is opened by an opener and beaten into loose viscose fiber.

[0042] (3) Spraying treatment of viscose fiber

[0043] The viscose fib...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
breaking strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of camel hair protein fibers. The preparation method comprises the following steps of (1) preparing a camel hair protein extract solution; (2) pre-opening treatment of viscose fibers; (3) spraying treatment of viscose fibers; (4) curing; and (5) post-treatment. Hydrolyzed camel hair protein powder is evenly dispersed in deionized water, a cross-linking agent is added to prepare camel hair protein cross-linking liquid, and then camel hair protein fibers are prepared in a spraying mode; according to the method, no strong acid or strong alkali is involved in the process that camel hair protein extract is adsorbed, high temperature is not needed, amino acid in camel hair protein cannot be damaged, the prepared fibers are high in camel hair protein extract content, and the prepared composite fibers have the advantages of being light, soft, fluffy, high in negative oxygen ion excitation value and the like; and the addition amount of the hydrolyzed camel hair protein is greatly increased, the fibers are not damaged under the condition that the addition amount is increased, the defects of the fibers are greatly reduced, and various indexes of the fibers are guaranteed.

Description

technical field [0001] The invention belongs to the field of light industry textiles, and in particular relates to a preparation method of camel hair protein fibers. Background technique [0002] The textile industry is a traditional industry in China. With the rapid development of clothing, household and industrial textiles, the differentiation and individualization of textile products have become the focus of the development of various enterprises. Functional fibers as high-grade textile raw materials are generally improved by means of physical modification, chemical modification and molecular design to obtain fibers with specific properties, so that the original viscose fibers are stable in light and heat, conductive, Flame retardant, dyeing, antistatic, moisture absorption, fluffy, anti-pilling, anti-fouling and other aspects have been greatly improved. Camel hair is a natural animal protein fiber, which is rich in resources in our country. However, due to the lag of re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/15D06M15/333D06M101/06
CPCD06M15/15D06M15/333D06M2101/06D06M2200/50
Inventor 骆祥伟张涛邱纯利
Owner 郑州诺肯新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products