Method for producing water reducer of cement concrete

A manufacturing method and technology of water reducing agent, applied in the field of building materials, can solve problems such as high price, difficult construction, complex ingredients, etc., and achieve the effects of simple production equipment, easy control of process, and high water reducing efficiency

Inactive Publication Date: 2006-07-26
冯乃谦
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the mixture on the coagulation is easy to bleed, resulting in segregation and delamination, which makes construction difficult and affects the strength and durability of concrete.
Due to the large amount of phenol used in this type of water reducer, the cost is high
The existing ingredients of this type of water reducer are complex, and the production temperature exceeds 100°C (actually 110°C), and it is not easy to control
[0005] High-efficiency polycarboxylate superplasticizers are expensive, expensive, and complicated to produce

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] In 600 ml of water at 85°C, add 55 grams of calcium lignosulfonate, 86 grams of p-aminobenzenesulfonic acid, and 25 grams of phenol, stir for 30 minutes, add 22 grams of sodium hydroxide, and adjust the pH of the solution to 7-8 , at 85°C, drop 100 grams of formaldehyde, react at this temperature for 9 hours, cool to obtain a liquid superplasticizer (water agent), with a solid content of about 24%, and then dry to obtain a powdery superplasticizer ( powder).

[0028] Measurement results of fluidity of cement slurry

[0029] Initially

Embodiment 2

[0031] At 90°C, in 1000 ml of water, add 55 grams of calcium lignosulfonate, 86 g of p-aminobenzenesulfonic acid, and 55 grams of phenol, stir for 30 minutes, add 23 grams of sodium hydroxide, and adjust the pH value of the solution to 8. ℃, drop 120 grams of formaldehyde, react at this temperature for 10 hours, and cool to obtain a liquid superplasticizer (water agent), with a solid content of about 24%. After drying, a powdery high-efficiency water reducer is obtained.

[0032] Fluidity of cement paste and its change over time

[0033] Example 1 of the combination of cement slurry

[0034] Superplasticizer content

Embodiment 3

[0036] At 90 DEG C, 90 grams of calcium lignosulfonate and 260 grams of p-aminobenzenesulfonic acid were dropped into 1000 milliliters of water. Phenol 140 grams. Stir for 30 minutes, add 68 grams of sodium hydroxide, adjust the pH value of the solution to 8, drop in 360 grams of formaldehyde at a temperature of 90 ° C, react at this temperature for 10 hours, and cool to obtain a liquid superplasticizer (water agent). The solid content is about 30%, and then dried to obtain a powdery high-efficiency water reducer.

[0037] Fluidity of cement paste and its change over time

[0038] Mixing ratio of cement paste:

[0039] Superplasticizer content

[0040] Comparison of the fluidity of the high-efficiency water-reducer of the present invention with that of the current naphthalene-based high-efficiency water-reducer:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to the production process of water reducer for cement and concrete, and belongs to the field of building material technology. The water reducer consists of calcium lignosulfonate, p-aminobenzenesulfonic acid, phenol, alkali and formaldehyde, and is produced into water preparation via adding water in 1-3 times. The production process includes heating water to 85-100 deg.c, adding the said materials successively via stirring, cooling to room to form water preparation, or further drying to form powder preparation. The present invention has the advantages of low temperature and normal pressure production, easy control of technological process, no environmental pollution, high function of controlling flowability loss of cement slurry and concrete and no harm to concrete durability.

Description

technical field [0001] The invention relates to a method for manufacturing a cement concrete water reducer, which uses p-aminobenzenesulfonic acid, lignin sulfonate, phenol, alkali and formaldehyde as raw materials to prepare a high-efficiency water reducer, belonging to the technical field of building materials. Background technique [0002] my country's concrete output is about 1.3 billion m 3 / year. The total output of superplasticizer is about 250,000 tons / year. The main varieties of superplasticizers are naphthalene series and melamine series. The former accounts for 90% of the superplasticizer consumption. In recent years, a small amount of polycarboxylate water reducer has been used in engineering. [0003] The main technical requirements of concrete to water reducing agent are: (1) high water reducing rate to reduce the water consumption of single concrete; (2) good dispersibility to cement and reduce water-cement ratio; (3) function of controlling slump loss Go...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/18C04B24/20
Inventor 冯乃谦王湘才张智峰丁宏李崇智
Owner 冯乃谦
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap