Silicon-aluminium-calcium composite deoxidant and its preparing method

A composite deoxidizer, silicon-alumina technology, applied in the field of metallurgy, can solve the problems of increased oxidation reaction probability, lower aluminum yield, lower deoxidation effect, etc., to eliminate nozzle blockage, reduce inclusions, and increase yield Effect

Inactive Publication Date: 2005-10-05
张敏修 +2
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, directly adding aluminum to molten steel will increase the probability of reaction between aluminum and oxides in slag, and even roll on the slag

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0017] [Example 1]

[0018] Weigh each raw material (unit: kg): silicon-calcium alloy (containing 55% silicon, 30% calcium) 20, aluminum ingot 10, ferrosilicon (75% silicon) 26, and steel scrap 44. The above raw materials are remelted in an intermediate frequency electric furnace. The percentage content of each component in the obtained product is: silicon 30.5%, aluminum 10%, calcium 6%, and the balance is iron.

Example Embodiment

[0019] [Example 2]

[0020] Weigh each raw material (unit: kg): silicon-calcium alloy (containing 55% silicon and 30% calcium) 40, aluminum ingot 27, ferrosilicon (75% silicon) 23, and steel scrap 10. The above raw materials are remelted in an intermediate frequency electric furnace. The percentage content of each component in the obtained product is: silicon 39.25%, aluminum 27%, calcium 12%, and the balance is iron.

Example Embodiment

[0021] [Example 3]

[0022] Weigh each raw material (unit: kg): silicon-calcium alloy (containing 55% silicon, 30% calcium) 34, aluminum ingot 25, ferrosilicon (75% silicon) 24, and swarf 7. The above raw materials are remelted in an intermediate frequency electric furnace. The percentage content of each component in the obtained product is 36.7% silicon, 25% aluminum, 10.2% calcium, and the balance is iron.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

This invention discloses a new compound deoxidization agent for steel-smelting use, and this agent comprises the following components: silicon 30-42%, aluminum 10-28%, Ca 6-12%, and Te the rest. This invention can fast deoxidize the steel, can effectively remove the impurities in the steel melt to improve the flow ability of steel melt, and advance the quality of the product and the use method is very convenient.

Description

technical field [0001] The invention relates to a composite deoxidizer for steelmaking, in particular to a silicon-aluminum-calcium composite deoxidizer for steelmaking and a preparation method thereof, belonging to the field of metallurgy. Background technique [0002] At present, in the process of steelmaking production, the main measure to reduce inclusions in molten steel is to use aluminum for deoxidation treatment. After deoxidation with aluminum, molten steel will produce Al 2 o 3 inclusions, resulting in solid Al in continuous casting production 2 o 3 The inclusions are deposited on the wall of the nozzle to block the nozzle. For this reason, the molten steel must be treated with calcium in the later stage of smelting to denature the inclusions and improve the nozzle flow. In addition, directly adding aluminum to molten steel will increase the probability of reaction between aluminum and oxides in slag, and even roll on the slag surface and oxidation reaction bet...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21C7/06
Inventor 张敏修李猛王念俊
Owner 张敏修
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap