Abstract

The present invention provides system and apparatus for use in processing wafers. The new system and apparatus allows for the production of thinner wafers that at same time remain strong. As a result, the wafers produced by the present process are less susceptible to breaking. The unique system also offers an improved structure for handling thinned wafers and reduces the number of processing steps. This results in improved yields and improved process efficiency.

Description

CROSS-REFERENCE TO RELATED APPLICATIONS [0001] This Application is a Division of U.S. patent application Ser. No. 10 / 923,131 filed Aug. 20, 2004, now pending. Priority to this Application is claimed under 35 U.S.C. § 121. The above-identified Application is also incorporated herein by reference.TECHNICAL FIELD [0002] The invention relates to a process and apparatus for use with workpieces, such as semiconductor wafers, flat panel displays, rigid disk or optical media, thin film heads or other workpieces formed from a substrate on which microelectronic circuits, data storage elements or layers, or micro-mechanical elements may be formed. These and similar articles are collectively referred to herein as a “wafer” or “workpiece.” Specifically, the present invention relates to a process and apparatus for use in thinning semiconductor workpieces. BACKGROUND OF THE INVENTION [0003] State of the art electronics (e.g., cellular phones, personal digital assistants, and smart cards) demand th...

AI Technical Summary

Benefits of technology

"The present invention provides a method and apparatus for processing wafers. The new system allows for the production of thinner wafers that remain strong, reducing the likelihood of breaking. The unique system also simplifies the handling of thinned wafers and reduces the number of processing steps, resulting in improved yields and efficiency. The invention includes a chuck for securely holding and processing wafers, with a groove or aperture for receiving the rim of the wafer and a compressible member for creating a seal between the chuck and the rim. The invention also provides several processes for thinning semiconductor workpieces, including steps of securing the workpiece to the chuck and then using a mechanical retainer or vacuum seal to thin the back side of the workpiece."

Problems solved by technology

In addition, advanced packaging of semiconductor devices (e.g., stacked dies or “flip-chips”) provide dimensional packaging constraints which require an ultra-thin die.

Moreover, as operating speeds of ICDs continue to increase heat dissipation becomes increasingly important.

This is in large part due to the fact that ICDs operated at extremely high speeds tend to generate large amounts of heat.

However, conventional back grinding processes have drawbacks.

Mechanical grinding induces stress in the surface and edge of the wafer, including micro-cracks and edgechipping.

This induced wafer stress can lead to performance degradation and wafer breakage resulting in low yield.

In addition, there is a limit to how much a semiconductor wafer can be thinned using a back grinding process.

Additionally, chemical etching after back grinding thins the semiconductor wafer beyond conventional back grinding capabilities.

Although methods for thinning semiconductor wafers are known, they are not without limitations.

For example, mounting a semiconductor wafer to a submount or “chuck” (as it is commonly known) so that the wafer can be thinned requires expensive coating and bonding equipment and materials, increased processing time, and the potential for introducing contaminates into the process area.

Additionally, adhesives for bonding a wafer to a chuck that may be useful in a mechanical grinding process will not withstand the chemical process fluids used in wet chemical etching.

Furthermore, the current use of a photoresist or adhesive tape fails to provide mechanical support for very thin wafers either during the back grind process or in subsequent handling and processing.

The use of tape also creates obstacles in the removal process.

For example, tape removal may subject a wafer to unwanted bending stresses.

In the case of a photoresist, the material is washed off the device side of a wafer with a solvent, adding to the processing time and use of chemicals, and increasing the risk of contamination.

The use of taping and protective polymers are also costly, since both equipment and materials are necessary to apply and remove the protective media.

Further, thinned semiconductor wafers are prone to warping and bowing.

And because thinned semiconductor wafers can be extremely brittle, they are also prone to breakage when handled during further processing.

Thinned semiconductor wafers (e.g., below 250 microns) also present complications in automated wafer handling because, in general, existing handling equipment has been designed to accommodate standard wafer thicknesses (e.g., 650 microns for 150 mm wafer and 725 microns for 200 and 300 mm wafers).