Cast steel and method for preparing same

A technology of cast steel and molten steel, applied in the field of cast steel and the preparation of the cast steel, can solve the problems of easy deformation, low strength and elongation of cast steel, unable to meet market requirements, etc., and achieve high elongation and high strength elongation. rate effect

Inactive Publication Date: 2007-08-08
CHINA NATIONAL HEAVY DUTY TRUCK GROUP
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the automobile axle housings are stamped axle housings. This kind of axle housing is prone to deformation and oil leakage under the condition of large impact load, which cannot meet the market requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

Specific Example 1

[0010] This specific embodiment is a cast steel containing the following chemical components by weight percentage: C: 0.21%, Si: 0.42%, Mn: 1.06%, Ni: 0.49%, Cr: 0.16%, Mo: 0.04%, P= 0.023%, S=0.020%, the balance is iron, and the carbon equivalent is 0.458%.

[0011] The preparation method of the low-alloy cast steel in this specific embodiment includes the following steps: 1. According to the chemical composition range given, use scrap steel and pig iron as ingredients; 2. Load the prepared materials into an electric arc furnace for smelting and smelting During the process, ferrosilicon, ferromanganese, electrolytic nickel, and ferrochrome are added to adjust the chemical composition; 3. The molten steel obtained by smelting is poured into castings; 4. Normalizing treatment. To measure, its mechanical properties are: σ b =576Mpa,σ s =371Mpa, δ=19.8%, Brinell hardness HB=171.

Example Embodiment

Specific Example 2

[0012] This specific embodiment is a cast steel containing the following chemical components by weight percentage: C: 0.19%, Si: 0.40%, Mn: 1.10%, Ni: 0.48%, Cr: 0.12%, Mo: 0.04%, P= 0.026%, S = 0.022%, the balance is iron, and the carbon equivalent is 0.436%.

[0013] The preparation method of the low-alloy cast steel in this specific embodiment includes the following steps: 1. According to the chemical composition range given, use scrap steel and pig iron as ingredients; 2. Load the prepared materials into an electric arc furnace for smelting and smelting During the process, ferrosilicon, ferromanganese, electrolytic nickel, and ferrochrome are added to adjust the chemical composition; 3. The molten steel obtained by smelting is poured into castings; 4. Normalizing treatment. To measure, its mechanical properties are: σ b =573Mpa,σ s =375Mpa, δ=20.4%, Brinell hardness HB=166.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cast steel and making method, which comprises the following parts: 0.18-0.22% C, 0.30-0.60% Si, 0.90-1.25% Mn, 0.48-0.55% Ni, 0.10-0.25% Cr, not more than 0.10% Mo, not more than 0.040% P, not more than 0.040% S and Fe (0.42-0.48% C). The making method comprises the following steps: 1. allocating; 2. fusing; 3. casting; 4. normalizing. The invention possesses high-strength and high-extending rate, which is fit for casting steel case.

Description

(1) Technical field [0001] The invention relates to a cast steel, in particular to a high-strength and high-elongation cast steel and a preparation method of the cast steel. (2) Background technology [0002] In recent years, with the requirements of social development, all kinds of engineering vehicles, especially heavy-duty dump trucks, must adapt to the harsh conditions of large tonnage and poor road conditions. In particular, the requirements for the axle housing are getting higher and higher. At present, the automobile axle housings are stamped axle housings. This kind of axle housing is prone to deformation and oil leakage under the condition of large impact load, which cannot meet the market requirements. Therefore, it is necessary to use a welded axle housing. The existing cast steel It is not suitable to make the axle housing of welded structure, because the strength and elongation of the current cast steel are low. (3) Contents of the invention [0003] The tec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/40C22C38/44C22C33/04
Inventor 安波代方正
Owner CHINA NATIONAL HEAVY DUTY TRUCK GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap