A combination of type and syrup technology, applied in the direction of casting molding equipment, molds, cores, etc., can solve the problems of high cost, poisoning of staff, etc., and achieve the effect of cost reduction
Inactive Publication Date: 2010-05-12
HAICHENG ZHONGXING HEAVY MACHINERY
View PDF0 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] (1) There is a pungent smell released during mixing, molding and baking, which is toxic to the workers on the production and use sites;
[0005] (2) High cost
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0026] The syrup-bonded molding sand used for foundry is made from the following ingredients in proportions by weight:
[0027] Naturally selected silica sand 100 parts
[0028] Syrup binder 15 parts
[0029] Enhancer boric acid 0 parts
[0030] A small amount of alcohol as an auxiliary material can be ignited to burn the syrup.
[0031] The technological process is as follows: according to the above-mentioned raw material composition and weight ratio, add syrup and boric acid to the natural wind-selected silica sand, mix and stir, after molding, spray alcohol, ignite and grill, and shape.
Embodiment 2
[0033] The syrup-bonded molding sand used for foundry is made from the following ingredients in proportions by weight:
[0034] Naturally selected silica sand 100 parts
[0035] Syrup binder 12 parts
[0036] Enhancer boric acid 1 part
[0037] Appropriate amount of alcohol
[0038] The technological process is as follows: according to the above-mentioned raw material composition and weight ratio, add syrup and boric acid to the natural wind-selected silica sand, mix and stir, after molding, spray alcohol, ignite and grill, and shape.
Embodiment 3
[0040] The syrup-bonded molding sand used for foundry is made from the following ingredients in proportions by weight:
[0041] Naturally selected silica sand 100 parts
[0042] Syrup binder 10 parts
[0043] Enhancer boric acid 2 parts
[0044] A small amount of alcohol
[0045] The technological process is as follows: according to the above-mentioned raw material composition and weight ratio, add syrup and boric acid to the natural wind-selected silica sand, mix and stir, after molding, spray alcohol, ignite and grill, and shape.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
flexural strength
aaaaa
aaaaa
rate of change
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to syrup-combined type sand which is used for casting ferrous metal produced by adopting edible or medicinal syrup as a bonding agent. The syrup-combined type sand is prepared from the following components in part by weight: 100 parts of naturally-winnowed silica sand, 3 to 15 parts of syrup bonding agent, 0 to 3 parts of boric acid serving as a reinforcing agent and small amount of alcohol serving as an auxiliary material; the process comprises the following follows: according to the material components and weight ratio, adding the syrup and the boric acid in the naturally-winnowed silica sand, mixing and stirring the mixture, shaping the mixture, spraying and brushing the alcohol, firing and roasting, and molding. The syrup-combined type sand has the advantages that: the cost is greatly reduced; as the syrup belongs to hydrocarbon, no impurity remains after being burned so as not to influence the regeneration and utilization of the used casting sand; and the syrup-combined type sand is environment-friendly and does not harm the health of workers.
Description
technical field [0001] The invention relates to a ferrous metal foundry sand produced by using edible or medicinal syrup as a binding agent. Background technique [0002] The molding sand binders widely used in the foundry industry at home and abroad mainly use the following three types: the first is bentonite series mineral fine powder (add water); the second is glass water (through CO 2 gas curing); the third is liquid phenolic resin (ammonia curing agent). [0003] The disadvantage of the first and second types of binders is that the impurities brought in affect the recycling of the used molding sand. The third type of liquid phenolic resin (ammonia curing agent) combined with the molding sand can be recycled without bringing in impurities, but it is a common problem. yes: [0004] (1) There is a pungent odor released during mixing, molding and baking, which is toxic to the workers on the production and use sites; [0005] (2) The cost is high. Contents of the invent...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more