Al2O3-SiO2-SiC-based jet material for foundry ladle

A technology of al2o3-sio2-sic and spraying material, which is applied in the field of Al2O3-SiO2-SiC refractory materials, can solve the problems of unreasonable micro-powder combination and reduce the corrosion resistance of materials, and achieve good thermal shock stability, high strength, The effect of promoting sintering

Inactive Publication Date: 2012-10-10
BAOSHAN IRON & STEEL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The goal of this patent is to be used for permanent lining. Although the injection material has achieved high strength, if it is used for working lining, the fine powder combination is unreasonable, and the addition of a large amount of high-alumina fine powder will reduce the erosion resistance of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Al2O3-SiO2-SiC-based jet material for foundry ladle
  • Al2O3-SiO2-SiC-based jet material for foundry ladle
  • Al2O3-SiO2-SiC-based jet material for foundry ladle

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] Table 4 and Table 5 have listed the composition ratio of each invention example and comparative example, because the injection material contains cement, can introduce CaO, and Fe 2 o 3 The presence of other impurities, therefore, Al 2 o 3 , SiO 2 The sum of SiC and SiC is less than 100%.

[0032] Table 6 and Table 7 are the performances of each inventive example and comparative example.

[0033] Proportioning 1 (wt %) of table 4 invention examples

[0034]

[0035] Proportioning 2 (wt %) of table 5 invention examples

[0036]

[0037] Performance 1 of table 6 invention examples

[0038]

[0039] Performance 2 of table 7 invention examples

[0040]

[0041] It can be seen from the above properties that although the present invention adopts ultra-low cement binding, the appropriate combination of the three micropowders makes the spray material have high medium and high temperature strength while having good pumpability. The flexural strength of A2, A3,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to an Al2O3-SiO2-SiC-based refractory material, in particular to an Al2O3-SiO2-SiC-based jet material for wet jet construction of a foundry ladle. The Al2O3-SiO2-SiC-based jet material for the foundry ladle comprises the following components in percentage by weight: 45 to 65 percent of sintered mullite, 5 to 15 percent of SiC, 7 to 18 percent of brown aluminium oxide or special-grade alumina, 5 to 10 percent of Al2O3 super-micro powder, 4 to 8 percent of high-aluminum micro powder, 2 to 5 percent of silicon micro powder, 1.5 to 3 percent of calcium aluminate cement, and 6 percent of balance. The granularity of the Al2O3 super-micro powder is leas than or equal to 2 microns; the purity of Al2O3 in the high-aluminum micro powder is more than or equal to 88 percent, and the granularity is less than or equal to 5 microns; and the purity of SiO2 in the silicon micro powder is more than or equal to 92 percent, and the granularity is less than 1 micron. The balance comprises 3 percent of andalusite and 3 percent of cyanite. The jet material has high strength and good thermal shock stability and corrosion resistance, and ensures good self-flowing property and pumping property.

Description

technical field [0001] The present invention relates to an Al 2 o 3 -SiO 2 - SiC refractory materials, especially Al for ladle wet spraying construction 2 o 3 -SiO 2 -SiC injection material. Background technique [0002] The wet spraying construction of refractory materials can be used not only to construct new refractory linings, but also to repair old linings, and wet spraying construction has many advantages, so this method has been more and more widely used in the iron and steel industry in recent years . [0003] The ladle is an important tool for transferring molten iron. When the molten iron is dumped, the lower part of the ladle and the refractory lining at the bottom will be strongly scoured. During the production process, the molten iron contained in the ladle will continue to scour and wear the lining. During slag removal, slag removal and pouring of molten iron, the ladle mouth refractory material is extremely vulnerable to wear. In addition, frequent loa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66C04B7/32C04B14/04
Inventor 姚金甫方善华田守信汪宁伍春芳陈向东
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products