Granulated powder and method for producing granulated powder
A manufacturing method and powder technology, applied in the field of granulated powder and granulated powder manufacturing, can solve the problems of poor mechanical properties, high price, high operating capital, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0146] First, 2% Ni-Fe alloy powder (manufactured by EPSON ATMIX Co., Ltd., with a true density of 7.827 g / cm3) with an average particle diameter of 6 μm produced by a water spray method was prepared. 3 ) as raw material powder. In addition, the composition of the 2% Ni-Fe alloy is: C: 0.4% by weight to 0.6% by weight, Si: 0.35% by weight or less, Mn: 0.8% by weight or less, P: 0.03% by weight or less, S: 0.045% by weight or less, Ni: 1.5% by weight to 2.5% by weight, Cr: 0.2% by weight or less, Fe: the remainder.
[0147] On the other hand, as an organic binder, polyvinyl alcohol (Kuraray Co., Ltd. RS-1717), glycerin (Wako Pure Chemical Industries, Ltd.), and an alkylamine derivative (acetate) were prepared. In addition, ion-exchanged water was prepared as a solvent. The amount of solvent added was 50 g of solvent per 1 g of organic binder. Furthermore, the degree of saponification of polyvinyl alcohol was 93, and the degree of polymerization was 1700.
[0148] Next, po...
Embodiment 2~9
[0156] Except that the addition amount of glycerin was shown in Table 1, the other was the same as in Example 1, and a granulated powder was obtained.
Embodiment 10~15
[0158] Except that the addition amounts of organic amines are shown in Table 1, the others were the same as in Example 3, and granulated powder was obtained.
PUM
Property | Measurement | Unit |
---|---|---|
degree of polymerization | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com