Chrome fluxing agent for steel ladles and preparation method thereof

A draining agent, chrome technology, applied in the field of refractory materials, can solve the problem of low casting rate of chrome draining agent

Active Publication Date: 2011-11-23
攀枝花市银江金勇工贸有限责任公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the prior art, the present invention aims to solve the problem that the pouring rate of the chromium drainage agent in the above-mentioned documents is still not high, and provides a chromium drainage agent with a higher casting rate, lower production cost and a more friendly use environment and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Preparation of ladle chrome drainage agent:

[0036] A, prepare materials according to the following parts by weight and raw material requirements:

[0037] a: parts by weight:

[0038] 68 parts chrome ore

[0039] Silica with a particle size of 1-2mm 11 parts

[0040] Silica with a particle size of 0.5-1mm 6 parts

[0041] Potassium feldspar 4 parts

[0042] Carbon black 0.004 parts

[0043] Flake graphite 0.002 parts

[0044] f 4 Binder 0.0005 parts

[0045] Water 0.0001 part;

[0046] f 4 The binder is made by mixing maltodextrin and carboxymethyl cellulose at a ratio of 1:0.2.

[0047] b. The composition requirements of each component:

[0048] Cr in chrome ore 2 o 3 The weight percentage is 90%, containing Al 2 o 3 2% by weight, containing 1% by weight of MgO, containing T Fe (full iron) weight percentage is 2%;

[0049] Silica contains SiO 2 The weight percentage is 99%;

[0050] Potassium feldspar contains SiO 2 The weight percentage is 80%, c...

Embodiment 2

[0057] Preparation of ladle chrome drainage agent:

[0058] A, prepare materials according to the following parts by weight and raw material requirements:

[0059] a: parts by weight:

[0060] 72 parts chrome ore

[0061] Silica with a particle size of 1-2mm 22 parts

[0062] Silica with a particle size of 0.5-1mm 10 parts

[0063] Potassium feldspar 7 parts

[0064] Carbon black 0.008 parts

[0065]Flake graphite 0.004 parts

[0066] f 4 Binder 0.001 part

[0067] 0.0003 parts of water;

[0068] f 4 The binder is made by mixing maltodextrin and carboxymethyl cellulose in a ratio of 1:3.

[0069] b. The composition requirements of each component:

[0070] Cr in chrome ore 2 o 3 The weight percentage is 46%, containing Al 2 o 3 12% by weight, containing 10% by weight of MgO, containing T Fe (full iron) weight percentage is 18%;

[0071] Silica contains SiO 2 The weight percentage is 99.9%;

[0072] Potassium feldspar contains SiO 2 The weight percentage is 7...

Embodiment 3

[0079] Preparation of ladle chrome drainage agent:

[0080] A, prepare materials according to the following parts by weight and raw material requirements:

[0081] a: parts by weight:

[0082] 70 parts chrome sand

[0083] Particle size is 1-2mm silica 17 parts

[0084] Silica with a particle size of 0.5-1mm 8 parts

[0085] Potassium feldspar 6 parts

[0086] Carbon black 0.006 parts

[0087] Flake graphite 0.003 parts

[0088] f 4 Binder 0.0007 parts

[0089] 0.0002 parts of water;

[0090] f 4 The binder is made by mixing maltodextrin and carboxymethyl cellulose in a ratio of 1:1.2.

[0091] b. The composition requirements of each component:

[0092] Cr in chrome ore 2 o 3 The weight percentage is 68%, containing Al 2 o 3 7% by weight, containing 6% by weight of MgO, containing T Fe (full iron) weight percentage is 9%;

[0093] Silica contains SiO 2 The weight percentage is 99.5%;

[0094] Potassium feldspar contains SiO 2 The weight percentage is 76%, c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a chrome fluxing agent for steel ladles and a preparation method thereof and belongs to the field of refractory materials. The chrome fluxing agent for the steel ladles is prepared from the following raw materials in parts by weight: 68-72 parts of chrome ore, 11-22 parts of silicate rock with the particle size of 1-2 mm, 6-10 parts of silicate rock with the particle sizeof 0.5-1 mm, 4-7 parts of potassium feldspar, 0.004-0.008 part of carbon black, 0.002-0.004 part of crystalline flake graphite, 0.0005-0.001 part of F4 binding agent and 0.0001-0.0003 part of water. The chrome fluxing agent for steel ladles is prepared through the steps of material preparation, metering, mixing, material discharge, packaging, and the like. Through adding the new F4 binding agent and a lubricating agent (crystalline flake graphite) into the fluxing agent provided by the invention, a new chrome fluxing agent for steel ladles, which is higher in open-casting rate, lower in production cost and friendlier to application environment, is produced.

Description

Technical field [0001] The present invention involves a drainage agent and its preparation method, especially a steel -wrap chromium drooling agent and its preparation method, which belongs to the field of refractory materials. Background technique [0002] Chrome drainters are mainly used for steel bag drainage. At this stage, small and medium -sized steel bag drainage mainly uses silicon drainters. The steel drainage of large and medium -sized steel bags mainly use chromium drainters, which has achieved good results.But there are also some problems: [0003] 1. The opening rate is not high, up to about 90%. [0004] 2. It often needs drainage that cannot be poured, that is, using oxygen guns to burn in the sliding water mouth, which not only wastes time affecting the efficiency of steelmaking production, but also has great hidden safety hazards. [0005] On December 4, 2002, the State Intellectual Property Office released a patent number 02109237.0, named "Chrome Dutch", which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 何金勇宋国菊许华林何源蒲芝明
Owner 攀枝花市银江金勇工贸有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap