Packaging-integrated nuclear track anti-counterfeiting disk and manufacturing method thereof

A manufacturing method and nuclear track technology, applied in the packaging integrated nuclear track anti-counterfeiting tape and its manufacturing field, can solve the problems of high production cost, complicated process, and inability to realize the integration of anti-counterfeiting materials and target object packaging, etc. Achieve the effect of wide applicability and expanding application fields

Active Publication Date: 2014-11-26
TSINGHUA UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the existing nuclear track anti-counterfeiting labels are made of nuclear track anti-counterfeiting film and paper or plastic backing materials. When users check the anti-counterfeiting performance, they need to peel off the nuclear track anti-counterfeiting film and the backing material, and there is a problem of peeling off the film. Difficult problem, at the same time, the existing positioning marks are made by accurate printing, the equipment used is very expensive, the production cost is high, and the process is complicated; therefore, it can only be used to make anti-counterfeiting labels, but cannot realize the packaging of anti-counterfeiting materials and objects The disadvantage of integration, so it is difficult to popularize and apply on many products that require exquisite packaging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Packaging-integrated nuclear track anti-counterfeiting disk and manufacturing method thereof
  • Packaging-integrated nuclear track anti-counterfeiting disk and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Laser nuclear track anti-counterfeiting thermal transfer film dribbling:

[0025] 1) Irradiate a 15 μm thick PET film with reactor fission fragments;

[0026] 2) On the irradiated PET film, make a printing plate according to the required pattern;

[0027] 3) Print the adhesive layer 2 (hot melt) on the PET film with a gravure printing machine;

[0028] 4) Print an acrylic release layer 3 on a PET film with an irradiated latent track, wherein the printing thickness is 0.8g / m 2 ;

[0029] 5) Coat 5.0g / m on the release layer 2 Water-soluble pressure-sensitive adhesive (self-adhesive), then compounded with another PET film with an adhesive layer 2 to form a composite film;

[0030] 6) Chemical etching: use 8N NaOH at 80°C to chemically etch the above composite film for 15 minutes, so that the radiation damage in the area without a protective layer is enlarged from a few nanometers to a few micrometers, and it is composed of a large number of micrometer-scale micropores....

Embodiment 2

[0038] Partial laser nuclear track anti-counterfeiting thermal transfer film dribbling

[0039] 1) Accelerator-accelerated 10MeV / u Ar-40 irradiates 50μPVDF polyvinylidene fluoride film;

[0040] 2) Make a printing plate according to the required pattern;

[0041] 3) Gravure printing hot melt on PVDF;

[0042] 4) Print an acrylate release layer on the irradiated PVDF polyvinylidene fluoride, the printing thickness is 1g / m 2 ;

[0043] 5) Coat 8.0g / m on the release layer 2 Water-soluble pressure-sensitive adhesive (self-adhesive), and then compounded with printed hot-melt PVDF film to form a composite film;

[0044] 6) Chemical etching: 8N NaOH at 80°C, chemically etch the above composite film for 12 minutes, so that the radiation damage in the area without a protective layer is enlarged from a few nanometers to a few micrometers, and it is composed of a large number of micrometer-sized pores that are visible to the naked eye The pattern area 8 of the non-pattern area 7 is ...

Embodiment 3

[0052] Partial laser nuclear track anti-counterfeiting thermal transfer film dribbling:

[0053] 1) Accelerator-accelerated 20MeV / u Kr-84 irradiates 50μBET polyester film;

[0054] 2) Make a printing plate according to the required pattern;

[0055] 3) Gravure printing hot melt on 20μ PETT, printing thickness 1g / m 2 ;

[0056] 4) Print the acrylate release layer on the irradiated BET, the printing thickness is 1g / m 2 ;

[0057] 5) Coat 3.0g / m on the release layer 2 Water-soluble pressure-sensitive adhesive (self-adhesive); then compounded with PETT film of printed hot-melt to form a composite film;

[0058]6) Chemical etching: 8N NaOH at 80°C, chemically etch the above composite film for 20 minutes, so that the radiation damage in the area without a protective layer is enlarged from a few nanometers to a few micrometers, and it is composed of a large number of micrometer-sized pores that are visible to the naked eye The pattern area 8 of the non-pattern area 7 is coated ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a packaging-integrated nuclear track anti-counterfeiting disk and a manufacturing method thereof, belonging to the technical field of nuclear track anti-counterfeiting. The nuclear track anti-counterfeiting disk comprises a rubber layer, a release layer, a one-layer nuclear track anti-counterfeiting film label, a laser layer or a metallic coating layer which are sequentially overlapped on a plastic film bottom belt, wherein the laser layer or metallic coating layer is thermally or cold transferred locally or completely on a hot melting gel layer. The one-layer nuclear track anti-counterfeiting film is punched according to the size of an anti-counterfeiting pattern and then waste is eliminated, and a composite material is coiled and trimmed, thus the packaging-integrated nuclear track anti-counterfeiting disk is manufactured. The laser layer can be used as a location marker when industrialized automatic hot-pasting is carried out, a nuclear track anti-counterfeiting film is industrially automatically positioned and thermally transferred to any package material by using the characteristic of hot melting transfer of the transfer laser layer, thus the industrial production integration of the nuclear track anti-counterfeiting film and the package materials is solved, and the nuclear track anti-counterfeiting film has the advantages of attractiveness and wide use and applicability.

Description

technical field [0001] The invention belongs to the technical field of nuclear track anti-counterfeiting, and in particular relates to a package-integrated nuclear track anti-counterfeiting tape and a manufacturing method thereof. Background technique [0002] Most of the existing nuclear track anti-counterfeiting labels are made of nuclear track anti-counterfeiting film and paper or plastic backing materials. When users check the anti-counterfeiting performance, they need to peel off the nuclear track anti-counterfeiting film and the backing material, and there is a problem of peeling off the film. Difficult problem, at the same time, the existing positioning marks are made by precise printing, the equipment used is very expensive, the production cost is high, and the process is complicated; therefore, it can only be used to make anti-counterfeiting labels, but cannot realize the packaging of anti-counterfeiting materials and objects The disadvantage of integration makes it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/08B32B27/30B32B27/36B32B15/04B32B15/20B32B7/12G09F3/02G09F3/10
Inventor 王玉兰徐世平陈靖王建晨
Owner TSINGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap