A manufacturing method and catalyst technology, applied in the direction of catalyst activation/preparation, physical/chemical process catalysts, chemical instruments and methods, etc., can solve the problems of producers and users, environmental hazards, unstable catalyst performance, high catalyst S content, etc. , to achieve the effect of coherent production mode, improved reactivity and selectivity, and stable quality

Inactive Publication Date: 2012-05-09
KUN SHAN DOTOP METAL TECH CO LTD
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the partially oxidized ternary copper powder catalyst is mainly made by chemical methods or in combination with physical methods: it is made of CuSO 4 ·5H 2 O is the raw material, which is obtained after spray drying, dehydration, reduction, and partial oxidation. This method is due to the use of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst produced through water atomization and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A catalyst produced by water atomization is prepared from cathode electrolytic copper plate as the initial raw material, after high temperature melting, high water pressure spray atomization, precipitation, high temperature drying and oxidation, screening, and ball milling oxidation. It not only has porous and In addition to the large specific surface area of ​​the traditional single-substance flake copper powder catalyst, it also has the characteristics of containing the ternary components of metallic copper, cuprous oxide and copper oxide. The ratio of the ternary components is:

[0024] Metal copper 19.0% Cuprous oxide 66.2% Copper oxide 14.8%

[0025] Further, a method for manufacturing a catalyst produced by water atomization includes the following steps:

[0026] Step 1) Selection of raw materials: it must be 1# cathode electrolytic copper, whose copper purity is greater than

[0027] 99.95%.

[0028] Step 2) High temperature melting: Put the raw materials into the interme...

Embodiment 2

[0035] A catalyst produced by water atomization is prepared from cathode electrolytic copper plate as the initial raw material, after high temperature melting, high water pressure spray atomization, precipitation, high temperature drying and oxidation, screening, and ball milling oxidation. It not only has porous and In addition to the large specific surface area of ​​the traditional single-substance flake copper powder catalyst, it also has the characteristics of containing the ternary components of metallic copper, cuprous oxide and copper oxide. The ratio of the ternary components is:

[0036] Metal copper 12.6% Cuprous oxide 52.0% Copper oxide 35.4%

[0037] Further, a method for manufacturing a catalyst produced by water atomization includes the following steps:

[0038] Step 1) Selection of raw materials: it must be 1# cathode electrolytic copper, whose copper purity is greater than

[0039] 99.95%.

[0040] Step 2) High temperature melting: Put the raw materials into the interme...

Embodiment 3

[0047] A catalyst produced by water atomization is prepared from cathode electrolytic copper plate as the initial raw material, after high temperature melting, high water pressure spray atomization, precipitation, high temperature drying and oxidation, screening, and ball milling oxidation. It not only has porous and In addition to the large specific surface area of ​​the traditional single-substance flake copper powder catalyst, it also has the characteristics of containing the ternary components of metallic copper, cuprous oxide and copper oxide. The ratio of the ternary components is:

[0048] Metal copper 6.6% Cuprous oxide 82.6% Copper oxide 10.8%

[0049] Further, a method for manufacturing a catalyst produced by water atomization includes the following steps:

[0050] Step 1) Selection of raw materials: it must be 1# cathode electrolytic copper, whose copper purity is greater than

[0051] 99.95%.

[0052] Step 2) High temperature melting: Put the raw materials into the intermed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a catalyst produced through water atomization and a manufacturing method thereof. The catalyst is prepared by melting a cathode electrolytic copper plate serving as a primary raw material at high temperature, performing high water pressure spray atomization, precipitation, high-temperature drying oxidization, selection and ball milling oxidization on the copper plate. Besides the characteristics of multiple pores, and large specific surface area of a traditional elemental sheet copper powder catalyst, the catalyst also has the property of containing three element components, namely copper, cuprous oxide and copper oxide. Due to the characteristics of multiple pores, sheet shape and large specific surface area, absorption and contact area between the catalyst and silica powder are increased, more Si and Cu alloy and eta phase can be formed, and the reaction activity of a contact is improved. The disadvantages that the content of S in the three-element copper catalyst produced by a chemical method using CuSO4.5H2O as a raw material is relatively high and the S does harm to producers, users and environments are overcome. The catalyst is continuous in production way, good in controllability and stable in quality.

Description

Technical field [0001] The copper powder catalyst and the manufacturing method thereof involved in the present invention specifically relate to a novel copper powder catalyst and a manufacturing method used in the production of organic silicon monomer by a water atomization method. Background technique [0002] Silicone is widely used as an "industrial monosodium glutamate". Its downstream and processed products are widely used in chemical, light industry, textile, medical, construction, electronic and electrical fields, and with the increase in the variety and quantity of downstream products of silicone , Its application areas will also continue to expand and develop. [0003] Organosilicon monomers are the foundation of the organosilicon industry, and the production level of monomers directly reflects the level of development of the organosilicon industry. Silicone monomers are needed to prepare silicone oil, silicone resin, silicone rubber and other silicone products. Many kind...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J23/72B01J37/00C07F7/16
Inventor 朱胜利
Owner KUN SHAN DOTOP METAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap