Aqueous lubricating liquid for stamping, stretching and forming cell phone battery shell, preparation method and application method thereof

A mobile phone battery, stamping and stretching technology, applied in the direction of lubricating composition, petroleum industry, etc., to achieve long-term stability of lubricating performance and cleaning performance, excellent cooling lubricity, and long service life

Active Publication Date: 2012-11-14
AMER TECH CO LTD
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, the object of the present invention is to provide a water-based mobile phone battery case stamping and stretching forming lubricating liquid, a preparation method and a method of use. The lubricating liquid has excellent cooling lubricity and solves the problem of aluminum The problem of effective settlement of the powder, while ensuring that there are no scratches and strains on the surface of the workpiece; the working fluid does not contain nitrite, f

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The water-based mobile phone battery shell stamping and stretching forming lubricating fluid of the present embodiment, the lubricating fluid raw material comprises the following components by weight: 50 parts of No. 45 transformer oil, 6 parts of nonionic emulsifier, 20 parts of water-based extreme pressure lubricant, 1.2 parts Boric acid, 1 part of aluminum powder sedimentation agent, 2 parts of triethanolamine, 6 parts of isopropanolamine, 5 parts of synthetic petroleum sodium sulfonate, 1 part of branched chain phosphate aluminum material protection agent, 3 parts of dicarboxylate-based compound anti-corrosion Rust agent, 3 parts of monobutyl ether coupling agent, 1 part of anti-hard water agent, 0.2 part of defoamer, 20 parts of distilled water;

[0020] The raw material of the water-based extreme pressure lubricant comprises the following components in parts by weight: 10 parts of pentaerythritol, 3 parts of adipic acid, and 4 parts of ricinoleic acid.

[0021] Th...

Embodiment 2

[0027] The water-based mobile phone battery shell stamping and stretching lubricating fluid of the present embodiment, the raw material of the lubricating fluid comprises the following components by weight: 15 parts of No. 45 transformer oil, 3 parts of nonionic emulsifier, 10 parts of water-based extreme pressure lubricant, 1 part of Boric acid, 0.5 parts of aluminum powder sedimentation agent, 2 parts of triethanolamine, 3 parts of isopropanolamine, 3 parts of synthetic petroleum sodium sulfonate, 0.5 parts of branched chain phosphate aluminum material protection agent, 1.5 parts of dicarboxylate-based compound anti-corrosion Rust agent, 2 parts of monobutyl ether coupling agent, 0.3 part of anti-hard water agent, 0.1 part of defoamer, 8 parts of distilled water;

[0028] The raw material of the water-based extreme pressure lubricant comprises the following components in parts by weight: 8 parts of pentaerythritol, 1 part of adipic acid, and 2 parts of ricinoleic acid.

[00...

Embodiment 3

[0035] The water-based mobile phone battery shell stamping and stretching lubricating fluid of the present embodiment, the lubricating fluid raw materials include the following components by weight: 50 parts of No. 45 transformer oil, 10 parts of nonionic emulsifier, 20 parts of water-based extreme pressure lubricant, 2 parts Boric acid, 2 parts of aluminum powder sedimentation agent, 5 parts of triethanolamine, 10 parts of isopropanolamine, 8 parts of synthetic petroleum sodium sulfonate, 1.5 parts of branched chain phosphate aluminum material protection agent, 5 parts of dicarboxylate-based compound anti-corrosion Rust agent, 5 parts of monobutyl ether coupling agent, 1 part of anti-hard water agent, 0.3 part of defoamer, 20 parts of distilled water;

[0036] The raw material of the water-based extreme pressure lubricant comprises the following components in parts by weight: 12 parts of pentaerythritol, 5 parts of adipic acid, and 6 parts of ricinoleic acid.

[0037] The pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses aqueous lubricating liquid for stamping, stretching and forming a cell phone battery shell, a preparation method and an application method thereof. The lubricating liquid comprises the following raw materials: 45# transformer oil, a non-ionic emulsifying agent, aqueous extreme-pressure lubricant, boric acid, an aluminum powder sinking agent, triethanolamine, isopropanolamine, synthetic petroleum sodium sulfonate, a branched chain phosphate aluminum protecting agent, a dicarboxylate based composite anti-rust agent, a butyl ether coupling agent, a hard water resistant agent, a defoaming agent and distilled water; the lubricating liquid is excellent in lubricating performance, anti-rust performance and settling performance, and the lubricating performance, the anti-corrosion performance and the cleaning performance are matched and stabilized for a long time, the antibacterial performance is good and the service life is long, the working liquid can be circularly added, the emission of the waste liquid is reduced, the environment cannot be polluted, and all indexes of 5% of diluent reach or exceed relative indexes of GB6144-2010.

Description

technical field [0001] The invention relates to a metal processing lubricating fluid, in particular to a water-based mobile phone battery case stamping and stretching forming lubricating liquid used for lubricating, cleaning, cooling and the like during the processing of the mobile phone battery case, a preparation method and a use method. Background technique [0002] The aluminum shell of the mobile phone battery is formed by rolling, stamping, and stretching the aluminum plate through a core-pulling die for many times. During the forming process, due to the large amount of deformation of the aluminum plate, a lot of heat and aluminum powder are generated, resulting in the surface of the aluminum shell. The temperature is extremely high. This requires that the lubricating oil used for stretching must have excellent cooling lubricity and settling performance on aluminum powder, so as to ensure that there are no scratches and strains on the surface of the workpiece; while tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M173/00C10M169/04C10N40/24C10N30/06C10N30/12C10N30/18
Inventor 陈战汪小龙
Owner AMER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap