Stain-resistant scrubbing-resistant colorful ceramic tile joint mixture as well as preparation method and application of mixture

A technology of colored tiles and caulking agent, which is applied in the field of tile caulking agent, can solve the problems of easy leaving traces, difficult cleaning, inconvenient construction, etc., and achieve the effect of avoiding the problem of alkali return

Active Publication Date: 2014-06-04
东方雨虹民用建材有限责任公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the epoxy resin and curing agent used in this solution are solvent-free, which can easily pollute the surface of the tiles during use, making cleaning very difficult and leaving traces. At the same time, the construction equipment is also very difficult to clean, causing inconvenience in construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stain-resistant scrubbing-resistant colorful ceramic tile joint mixture as well as preparation method and application of mixture

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Embodiment 1 (unit Kg, the same below):

[0039] Epoxy resin 130.0

[0040] Epoxy resin curing agent 100.0

[0041] 52.5 Ordinary white Portland cement 140.0;

[0042] Quartz sand 505.0;

[0043] Titanium dioxide 22.0;

[0044] Precipitated barium sulfate 21.8;

[0045] Fumed silica 7.0;

[0046] Pigment 3.5;

[0047] UV absorber 0.42;

[0048] Anti-yellowing agent 0.28.

Embodiment 2

[0050] Epoxy resin 150.0

[0051] Epoxy resin curing agent 100.0

[0052] 52.5 Ordinary white Portland cement 140.0;

[0053] Quartz sand 505.0;

[0054] Titanium dioxide 22.0;

[0055] Precipitated barium sulfate 21.8;

[0056] Fumed silica 7.0;

[0057] Pigment 3.5;

[0058] UV absorber 0.42;

[0059] Anti-yellowing agent 0.28.

Embodiment 3

[0061] Epoxy resin 170.0

[0062] Epoxy resin curing agent 100.0

[0063] 52.5 Ordinary white Portland cement 140.0;

[0064] Quartz sand 505.0;

[0065] Titanium dioxide 22.0;

[0066] Precipitated barium sulfate 21.8;

[0067] Fumed silica 7.0;

[0068] Pigment 3.5;

[0069] UV absorber 0.42;

[0070] Anti-yellowing agent 0.28.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shrinkageaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a stain-resistant and scrubbing-resistant colorful ceramic tile joint mixture which is prepared from epoxy resin, a curing agent and powder, wherein the powder comprises white cement, quartz sand, titanium dioxide, precipitated barium sulphate, gas phase silica, dye, ultraviolet light absorber and yellowing-resistant agent. According to the ceramic tile joint mixture, not only the problem of alkali return of the common cement-base ceramic tile joint mixture can be thoroughly solved, but also the joint mixture is convenient to construct, the redundant joint mixture can be washed by water, and the joint mixture is cured under room temperature, and is stain-resistant and scrubbing-resistant.

Description

technical field [0001] The invention relates to a ceramic tile grout, which belongs to the field of building materials. Background technique [0002] With the development of society, tiles have become one of the most commonly used materials in architectural decoration. At present, the most commonly used filling material for the gap between tiles is cement-based tile grout. This type of cement-based tile grout has been used for a period of time and the surface is very dirty, which affects the aesthetic effect. [0003] In response to such problems, there have been technical solutions in the art that use epoxy resin, curing agent and filler to mix and fill in an attempt to completely solve the above problems. However, the epoxy resin and curing agent used in this solution are all solvent-free, which can easily pollute the surface of the tiles during use, making cleaning very difficult and leaving traces. At the same time, the construction equipment is also very difficult to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04
Inventor 韩朝辉熊卫锋
Owner 东方雨虹民用建材有限责任公司