A kind of PBT composite material and preparation method thereof

A composite material and compound technology, which is applied in the field of PBT composite materials and its preparation, can solve the problems of poor compatibility and difficulty in guaranteeing the low temperature resistance of PBT composite materials, and achieve the effects of enhanced low temperature resistance, high production efficiency, and simple process

Active Publication Date: 2016-03-23
SHENZHEN YATAIXING IND
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the compatibility between flame retardants and PBT resins is poor
After adding flame retardants, the low temperature resistance of PBT composites will be more difficult to guarantee

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of PBT composite material and preparation method thereof
  • A kind of PBT composite material and preparation method thereof
  • A kind of PBT composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment PB

[0022] The embodiment of the present invention PBT composite material, comprises the component of following parts by weight:

[0023] 5 parts of thermoplastic polyester elastomer (TPEE7246); 5 parts of PBT110082; 5 parts of glass fiber; 3 parts of compatibilizer (SMA); 0.1 parts of KH-5600, 0.1 parts of ADR-43700; ) 0.1 parts. Among them, KH-560 is compounded with ADR-4370 to form a coupling agent, and OP1240 is compounded with MR01 to form a halogen-free flame retardant.

[0024] The preparation method of the PBT composite material of the embodiment of the present invention comprises the following steps:

[0025] a: Weigh each component according to the above parts by weight, first dry the thermoplastic polyester elastomer and compatibilizer in a vacuum oven at 45°C for 3-4 hours;

[0026] b: uniformly mixing the halogen-free flame retardant and the coupling agent in a high-speed mixer to obtain the first mixture;

[0027] c: Add the PBT resin, dispersant, thermoplastic poly...

Embodiment 2

[0030] The embodiment of the present invention PBT composite material, comprises the component of following parts by weight:

[0031] 15 parts of thermoplastic polyester elastomer (TPEE6356); 45 parts of PBT110045 parts; 10 parts of glass fiber; 4 parts of compatibilizer (SMA); 0.3 parts of KH-5600, 0.6 parts of ADR-43700; MB50-007) 0.5 parts. Among them, KH-560 is compounded with ADR-4370 to form a coupling agent, and OP1240, 300A is compounded with MR01 to form a halogen-free flame retardant.

[0032] The preparation method of the PBT composite material of the embodiment of the present invention comprises the following steps:

[0033] a: Weigh each component according to the above parts by weight, first dry the thermoplastic polyester elastomer and compatibilizer in a vacuum oven at 45°C for 3-4 hours;

[0034] b: uniformly mixing the halogen-free flame retardant and the coupling agent in a high-speed mixer to obtain the first mixture;

[0035] c: Add the PBT resin, dispe...

Embodiment 3

[0038] The embodiment of the present invention PBT composite material, comprises the component of following parts by weight:

[0039] Thermoplastic polyester elastomer (TPEE6356) 25 parts; PBT110028 parts; glass fiber 20 parts; compatibilizer (SMA) 5 parts; KH-5600.5 parts, ADR-43700.5 parts; 300A18 parts, MR012 parts; ) 1 part. Among them, KH-560 is compounded with ADR-4370 to form a coupling agent, and 300A is compounded with MR01 to form a halogen-free flame retardant.

[0040] The preparation method of the PBT composite material of the embodiment of the present invention comprises the following steps:

[0041] a: Weigh each component according to the above parts by weight, first dry the thermoplastic polyester elastomer and compatibilizer in a vacuum oven at 45°C for 3-4 hours;

[0042] b: uniformly mixing the halogen-free flame retardant and the coupling agent in a high-speed mixer to obtain the first mixture;

[0043] c: Add the PBT resin, dispersant, thermoplastic po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention is applicable to the technical field of composite materials and provides a PBT (polybutylece terephthalate) composite material and a preparation method thereof. The polybutylece terephthalate composite material comprises the following components in parts by weight: 5 to 35 parts of an TPEE (Thermoplastic Polyeher Ester Elastomer), 10 to 82 parts of PBT, 5 to 35 parts of a reinforcing agent, 5 to 25 parts of a flame retardant, 3 to 7 parts of a compatilizer and 0.1 to 2 parts of a coupling agent. According to the invention, the low-temperature resistance of the PBT composite material can be enhanced remarkably through adding the TPEE, and meanwhile, the consistency of the TPEE, the PBT, the reinforcing agent and the flame retardant is modified through the compatilizer and the coupling agent, so that the influence of the reinforcing agent and the flame retardant to the low-temperature resistance of the composite material can be eliminated effectively, and the purpose that the PBT composite material has low-temperature resistance, flame retardancy and high intensity at the same time can be achieved. In addition, when the PBT composite material is prepared, all that is needed is to perform melt extrusion after the corresponding components are mixed step by step. The method is simple in process, low in cost, high in productivity effect and very suitable for industrial production.

Description

technical field [0001] The invention belongs to the technical field of composite materials, and in particular relates to a PBT composite material and a preparation method thereof. Background technique [0002] Polybutylene terephthalate (PBT) has the characteristics of excellent thermal stability, creep resistance, electrical insulation and flame retardancy. It is a general-purpose engineering plastic with excellent performance. The country has formed industrialized production, and the technology continues to develop. The performance of unmodified PBT is not good, and PBT needs to be modified for practical application. Among them, glass fiber reinforced modified grades account for more than 70% of PBT. PBT reinforced materials have excellent performance and are currently widely used. It is mainly used to make parts of electronic appliances, automobiles, mechanical equipment and precision instruments, and has replaced metal materials such as copper, zinc, aluminum and iron ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L67/00C08K9/04C08K9/06C08K7/14B29C47/92B29C48/92
CPCB29C48/92B29C48/875B29C2948/92514B29C2948/92704B29C2948/92895
Inventor 徐东徐永谢建达
Owner SHENZHEN YATAIXING IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap