A kind of addition mold glue suitable for making crystal diamonds and its preparation method

A technology of additive molding and mold glue, which is applied in the field of crystal diamonds, can solve the problems of affecting the service life of mold glue and short service life, and achieve the effects of optimization of curing temperature and time, long service life and high economic value

Active Publication Date: 2016-05-11
惠州市永卓科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the inventors have found in research that the existing addition mold glue used to make crystal diamonds has a short service life, because at high temperatures, the mold glue will react with products (such as epoxy resin, etc.), so It affects the service life of the mold glue, resulting in only about 20 times of overturning of the existing mold glue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of addition mold glue suitable for making crystal diamonds and its preparation method
  • A kind of addition mold glue suitable for making crystal diamonds and its preparation method
  • A kind of addition mold glue suitable for making crystal diamonds and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A kind of addition mold glue that is suitable for making crystal diamond of the present embodiment, its raw material formula is made up of each component of following parts by weight:

[0038]

[0039]

[0040] The structural formula of the above-mentioned component A is shown in the general formula (I):

[0041]

[0042] In the above formula (I), m=1000 and n=10.

[0043] The above component B is composed of two substances with general formula (II) and general formula (III):

[0044]

[0045] In the above formula (II), a=10.

[0046] In the above formula (III), b=5 and c=12.

[0047] In the above component B, the weight ratio of the compound of general formula (II) to the compound of general formula (III) is 1:1.

[0048] The above-mentioned catalyst is a Castel platinum catalyst with a platinum content of 3000pmm; the inhibitor 1 is 1-butyn-3-ol.

[0049] The structural formula of the above-mentioned inhibitor 2 is shown in the general formula (IV):

...

Embodiment 2

[0057] A kind of addition mold glue that is suitable for making crystal diamond of the present embodiment, its raw material formula is made up of each component of following parts by weight:

[0058]

[0059] The structural formula of the above-mentioned component A is shown in the general formula (I):

[0060]

[0061] In the above formula (I), m=1000 and n=10.

[0062] The above component B is composed of two substances with general formula (II) and general formula (III):

[0063]

[0064] In the above formula (II), a=13.

[0065] In the above formula (III), b=8 and c=15.

[0066] In the above component B, the weight ratio of the compound of general formula (II) to the compound of general formula (III) is 1:1.

[0067] The above-mentioned catalyst is a Castel platinum catalyst with a platinum content of 3000pmm; the inhibitor 1 is 1-hexyn-3-ol.

[0068] The structural formula of the above-mentioned inhibitor 2 is shown in the general formula (IV):

[0069]

[...

Embodiment 3

[0076] A kind of addition mold glue that is suitable for making crystal diamond of the present embodiment, its raw material formula is made up of each component of following parts by weight:

[0077]

[0078] The structural formula of the above-mentioned component A is shown in the general formula (I):

[0079]

[0080] In the above formula (I), m=1000 and n=10.

[0081] The above component B is composed of two substances with general formula (II) and general formula (III):

[0082]

[0083] In the above formula (II), a=15.

[0084] In the above formula (III), b=10 and c=10.

[0085] In the above component B, the weight ratio of the compound of general formula (II) to the compound of general formula (III) is 1:1.

[0086] The above-mentioned catalyst is a Castel platinum catalyst with a platinum content of 3000pmm; the inhibitor 1 is 2-propyn-1-ol.

[0087] The structural formula of the above-mentioned inhibitor 2 is shown in the general formula (IV):

[0088] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses addition type mold rubber suitable for manufacturing a crystal drill and a preparation method of the addition type mold rubber. The addition type mold rubber is prepared from the following raw materials in parts by weight: 85-90 parts of a component A, 10-15 parts of a component B, 0.5-1.0 part of a catalyst, 0.06-0.08 part of an inhibitor 1 and 25-30 parts of an inhibitor 2. The addition type mold rubber disclosed by the invention has excellent tensile strength, tear strength and hardness, the number of mold rolling-over times is as high as 35-50, and the service life is long.

Description

technical field [0001] The invention relates to the technical field of crystal drills, in particular to the technology of mold glue used in the manufacture of crystal drills, in particular to an addition-type mold glue specially suitable for manufacturing crystal drills and a preparation method thereof. Background technique [0002] At present, the commonly used mold glue for crystal diamonds is addition-type mold silicone, because the addition-type mold silicone has the advantages of high transparency and good mold release. Compared with plastic, addition mold plastic has better dimensional stability, linear shrinkage rate is less than 0.1%, heat resistance can reach above 250 ℃, and it will not restore when heated in a sealed environment. [0003] However, the inventors have found in research that the existing addition mold glue used to make crystal diamonds has a short service life, because at high temperatures, the mold glue will react with products (such as epoxy resin,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C08L83/07C08L83/04
Inventor王细平
Owner惠州市永卓科技有限公司