A mold for processing a gear bushing and a method for processing a gear bushing using the mold

A gear bushing and mold processing technology, which is applied in the direction of shafts and bearings, bearing components, mechanical equipment, etc., can solve the problems of affecting the comprehensive performance of finished products, poor powder fluidity, and easy breakage of gear bushings, etc., to achieve uniform density, Good compression performance, not easy to break

Active Publication Date: 2016-08-24
宁波金钟粉末冶金有限公司
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at present, the density of the gear sleeve that can be cold pressed is generally up to 6.5g / cm 3 , and because the gear surface is at the bottom when pressing, and the powder fluidity is poor, the middle part of the gear sleeve is easy to break, which affects the overall performance of the finished product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A mold for processing a gear bushing and a method for processing a gear bushing using the mold
  • A mold for processing a gear bushing and a method for processing a gear bushing using the mold
  • A mold for processing a gear bushing and a method for processing a gear bushing using the mold

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043]A gear bushing, the gear bushing is formed by machining a gear bushing blank 1, the outer surface of the gear bushing blank 1 is a gear surface 2, an outer ring connected in sequence from top to bottom Mesa 3, outer peripheral surface 4, the diameter of the addendum circle of the gear surface 2 is smaller than the cross-sectional diameter of the outer peripheral surface 4, and the inner surface of the gear sleeve blank 1 is the first inner surface connected sequentially from top to bottom. Circumferential surface 5, first inner circumferential surface 6, second inner circumferential surface 7, second inner circumferential surface 8, third inner circumferential surface 9, said first inner circumferential surface 5, second inner circumferential surface 7, The cross-sectional circle diameter of the third inner peripheral surface 9 gradually increases. The upper end surface and the lower end surface of the gear sleeve blank 1 are respectively a torus, wherein the outer porti...

Embodiment 2

[0047] A kind of mold that is used to process the gear bushing of embodiment 1, it comprises female die 11, an upper punching die 12, two upper punching dies 13, one punching die 14, two lower punching dies 15, three lower punching dies 16, mandrel 17.

[0048] The female mold 11 is a cylindrical body with a continuous cylindrical cavity (inner hole), which is formed by the interference and thermal sleeve of the inner mold core 11.1 and the outer mold sleeve 11.2, wherein the material of the mold core 11.1 is hard Quality alloy, the material of the mold cover 11.2 is 40Cr steel. The diameter of the inner hole of the female mold 11 is equal to the cross-sectional circle diameter of the outer peripheral surface 4 of the gear sleeve blank 1 . The outer periphery of the female mold 11 is provided with a first protrusion 21 for fixed connection with the lower punching plate of the press.

[0049] The inside of the first upper die 12 has a through circular cavity for socketing the ...

Embodiment 3

[0054] The method for the gear bushing of embodiment 1 according to the mold processing embodiment 1 of embodiment 2, it comprises the following steps:

[0055] (1) Weigh each component of formula content, fully mix uniformly, form stamping material;

[0056] (2) In the loose state of the press, the stamping material is added through the feeding channel into the material cavity formed by the mandrel 17, the first punch 14, the second lower punch 15, the third lower punch 16, and the female mold 11;

[0057] (3) Then the press enters the pressing state, and the stamping material is cold-pressed;

[0058] (4) Finally, the press enters the demoulding state, and the formed gear sleeve blank 1 is output;

[0059] (5) machining the obtained gear shaft sleeve blank 1, specifically including:

[0060] (a) CNC lathe processing, large inner hole Φ7.984±0.009, Φ12.98±0.009, steps 8.7±0.15, 5±0.15, 16.8±0.10,

[0061] (b) The large chamfering angle is 30°, the car chamfering angle is R...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a gear shaft sleeve which is formed by machining gear shaft sleeve blank (1). The gear shaft sleeve is formed by the following components in a cold pressing mode, the ingredients comprise 0.6%-1.2% of carbon, 1.3%-1.7% of copper, 1.55%-1.95% of nickel, 0.4%-0.6% of molybdenum, 0.3%-0.5% of AncorMax200 and the balance iron. The machining method of the gear shaft sleeve includes the steps that the components required by a formula are weighed and mixed evenly; when a pressing machine is in a loose state, materials to be pressed are added into a material cavity, the size of the material cavity is three times of the size of the gear shaft sleeve blank (1); when the pressing machine is in a pressing state, the materials to be pressed are formed in a cold pressing mode; when the pressing machine is in a demoulding state, the finished gear shaft sleeve blank (1) is output; machining such as numerical control lathe machining, 30-degree big chamber chambering, large outer circle clamping and small outer circle turning is conducted. The density of the gear shaft sleeve obtained through the method can reach 6.9-7.0 g / cm<3>, and the overall quality is high.

Description

technical field [0001] The invention relates to the technical field of mechanical parts processing, in particular to a gear bushing and a processing method for the gear bushing. Background technique [0002] Gear bushings are important components in mechanical design. In the early days, the gear sleeves were all formed by stamping. This processing method not only wastes material seriously, but also has limited accuracy. [0003] One-time cold pressing of powder is a more and more commonly used gear bushing processing method. This method not only has a short process chain, but also saves materials, does not waste, and the overall manufacturing cost is low. But at present, the density of the gear sleeve that can be cold pressed is generally up to 6.5g / cm 3 , and because the gear surface is at the bottom during pressing, and the powder fluidity is poor, the middle part of the gear sleeve is easy to break, which affects the overall performance of the finished product. Conten...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F5/08F16C33/04C22C38/16B22F3/03
Inventor 蔡健瀚
Owner 宁波金钟粉末冶金有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com