Viscous medium external pressing forming method for large-curvature thin-wall component

A technology of thin-walled components and viscous media, which is applied in the field of forming large-curvature thin-walled components. It can solve the problems of easy instability and wrinkling of formed parts, thinning of the wall thickness of formed parts, and poor forming accuracy, so as to avoid wall thickness reduction. and wrinkling, large diameter reduction, and strong strain rate sensitivity

Active Publication Date: 2014-12-24
HARBIN INST OF TECH
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention solves the simple external pressure forming of large-curvature thin-walled components. When the two ends of the blank are constrained, the wall thickness of the formed part is severely reduced or even broken; , also in order to solve the problems of complex mold, frequent forming, poor forming precision and high cost in multi-pass forming, a viscous medium external pressure forming method for large curvature thin-walled components is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Viscous medium external pressing forming method for large-curvature thin-wall component
  • Viscous medium external pressing forming method for large-curvature thin-wall component
  • Viscous medium external pressing forming method for large-curvature thin-wall component

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0027] Specific implementation mode one: combine Figure 1 to Figure 8 Describe this implementation mode, this implementation mode is realized through the following steps:

[0028] Step 1, making the tube blank 2: roll and weld the plate to form a cylinder, see figure 1 , the material flow control rib 2-1 is arranged symmetrically on the cylinder wall with the cylinder length center M-M as the reference, the distance s between the material flow control rib 2-1 and the entrance of the variable diameter area is 5 mm to 30 mm, see figure 2 ; The structural shapes of the material flow control ribs 2-1 at both ends of the billet 2 can be different. Through the resistance of the material flow control rib 2-1, the inflow of the material at the end is adjusted and controlled, so that the wall thickness of the formed part is less thinned and wrinkle-free.

[0029] Step 2, the tube blank 2 is loaded into the external pressure forming mold: the tube blank 2 is loaded into the core mo...

specific Embodiment approach 2

[0033] Specific implementation mode two: combination figure 2 To describe this embodiment, the distance s between the material flow control rib 2 - 1 and the entrance of the variable diameter area in Step 1 of this embodiment is 20 mm. For general large-curvature external pressure parts, the forming quality is better, and for special formed parts, it is necessary to reasonably adjust and control the distance s between the ribs and the entrance of the mandrel. Other steps are the same as in the first embodiment.

specific Embodiment approach 3

[0034] Specific implementation mode three: combination Figure 1 to Figure 8 To illustrate this embodiment, the material of the tube blank 2 in step 1, step 2 and step 3 of this embodiment is stainless steel or superalloy. For external pressure forming of large curvature parts, if control ribs are not used, the diameter reduction is small, and it is difficult to form large curvature parts. However, if the control ribs are used for forming, the diameter reduction is large, and larger curvature parts can be formed. Other steps are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to an external pressing forming method for large-curvature thin-wall components, in particular to a viscous medium external pressing forming method for a large-curvature thin-wall component. The viscous medium external pressing forming method for the large-curvature thin-wall component aims to solve the problems that under the condition that pure external pressing forming is conducted on the large-curvature thin-wall component, when the two ends of a blank are restrained, the wall thickness of a formed component is greatly reduced, and even the wall of the formed component fractures; when the two ends of the blank are not restrained, the formed component is prone to being instable and wrinkling. The viscous medium external pressing forming method for the large-curvature thin-wall component comprises the steps that firstly, a plate is coiled and welded into a cylinder, and material flow control ribs are symmetrically arranged on the wall of the cylinder with the length center of the cylinder as the datum; secondly, the cylinder blank is installed in an external pressing forming die; thirdly, a plunger is pushed so that viscous soft die materials are injected in through an injecting channel from the outer side of the part, shrinkage deformation of a part of the cylinder blank occurs until the cylinder blank is attached to a core die; fourthly, the die is opened, an external pressing formed part is taken out, the viscous soft die materials are removed, and then the formed component is obtained; the material flow control ribs at the two ends are removed, and a finished product is obtained. The viscous medium external pressing forming method is applied to large-curvature thin-wall components.

Description

technical field [0001] The invention relates to a method for forming a thin-walled component with large curvature, in particular to a method for forming a thin-walled component with large curvature by external pressure with a viscous medium. Background technique [0002] A thin-walled member with large curvature is a typical shell structure, such as Figure 9 shown. At present, the methods commonly used to process such parts are: 1. Perform simple soft mold compression molding on the deformation zone: when there are no constraints at both ends of the blank, the forming principle is as follows: Figure 10 As shown, since the two ends of the billet are in a free state, the material of the tube blank flows to the deformation zone under the action of the adhesive stress of the viscous soft mold material. Defects such as instability and wrinkling seriously reduce the surface quality of the formed part; when there are constraints 8 at both ends of the blank, the forming principle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21D26/033
Inventor 王忠金相楠易军程超
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com