A kind of rubber composition of leaf spring lug bushing for automobile

A technology of rubber composition and leaf spring, which is applied in the field of rubber chemical industry, can solve the problems of poor extrusion resistance, easy failure and damage, etc., and achieve the effect of better surface brightness, low price, and convenient use and installation

Inactive Publication Date: 2016-05-04
SHANGHAI ZHONGLI AUTO PARTS
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] What the present invention aims to solve is the technical problem that the existing automotive leaf spring lug bushings have poor extrusion resistance and are prone to failure and damage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of rubber composition of leaf spring lug bushing for automobile
  • A kind of rubber composition of leaf spring lug bushing for automobile
  • A kind of rubber composition of leaf spring lug bushing for automobile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A rubber composition for a leaf spring lug bushing for automobiles, comprising the following components in parts by weight:

[0027] SCR5: 50 copies;

[0028] SBR1502: 50 copies;

[0029] Active zinc oxide: 8 parts;

[0030] Stearic acid: 2 parts;

[0031] Anti-aging agent 4010NA: 3 parts;

[0032] Anti-aging agent RD: 2 parts;

[0033] ANTILUX654: 4 copies;

[0034] Coumarone: 6 copies;

[0035] STRUKTOLWB215: 4 copies;

[0036] Black ointment: 3 parts;

[0037] CrodamidesVRX: 8 copies;

[0038] N-330: 40 copies;

[0039] N-774: 30 copies;

[0040] Aromatic oil: 5 parts;

[0041] Accelerator CZ: 1.5 parts;

[0042] Accelerator DM: 0.4 parts;

[0043] And IS60: 1.6 copies.

[0044] The preparation method uses a kneader to mix, and the steps are as follows:

[0045] Raise the temperature of the kneader to 110°C, put the rubber into the mixing chamber and knead for 40s, then lift the top plug to add a section of fine materials: active agent, stearic acid, antioxidant, microcrystalline wax, resin...

Embodiment 2

[0047] A rubber composition for a leaf spring lug bushing for automobiles, comprising the following components in parts by weight:

[0048] SCR5: 60 copies;

[0049] SBR1502: 40 copies;

[0050] Active zinc oxide: 7 parts;

[0051] Stearic acid: 1.5 parts;

[0052] Anti-aging agent 4010NA: 2 parts;

[0053] Anti-aging agent RD: 3 parts;

[0054] ANTILUX654: 5 copies;

[0055] Coumarone: 5 copies;

[0056] STRUKTOLWB215: 5 copies;

[0057] Black ointment: 5 parts;

[0058] CrodamidesVRX: 7 copies;

[0059] N-330: 50 copies;

[0060] N-774: 40 copies;

[0061] Aromatic oil: 10 parts;

[0062] Accelerator CZ: 1.6 parts;

[0063] Accelerator DM: 0.5 parts;

[0064] And IS60: 1.8 copies.

[0065] The preparation method is the same as in Example 1.

Embodiment 3

[0067] A rubber composition for a leaf spring lug bushing for automobiles, comprising the following components in parts by weight:

[0068] SCR5: 70 copies;

[0069] SBR1502: 30 copies;

[0070] Active zinc oxide: 6 parts;

[0071] Stearic acid: 1.5 parts;

[0072] Anti-aging agent 4010NA: 2 parts;

[0073] Anti-aging agent RD: 2 parts;

[0074] ANTILUX654: 3 copies;

[0075] Coumarone: 4 copies;

[0076] STRUKTOLWB215: 3 copies;

[0077] Black ointment: 3 parts;

[0078] CrodamidesVRX: 5 copies;

[0079] N-330: 30 copies;

[0080] N-774: 30 copies;

[0081] Aromatic oil: 5 parts;

[0082] Accelerator CZ: 1.2 parts;

[0083] Accelerator DM: 0.3 parts;

[0084] And IS60: 1.5 copies.

[0085] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rubber composition for a leaf spring lug bushing for an automobile. The rubber composition is characterized by comprising the following components in parts by weight: 100 parts of rubber, 1.5-3 parts of a p-phenylenediamine type anti deteriorant, 1.5-3 parts of a hydrogenated quinoline type anti deteriorant, 3-5 parts of microcrystalline wax, 5-8 parts of an active agent, 1-2 parts of stearic acid, 3-6 parts of resin, 3-5 parts of a processing addition agent, 5-8 parts of a slipping agent, 3-5 parts of a fatty oil plastifier, 5-10 parts of a petroleum plastifier, 60-95 parts of carbon black, 1.5-2.1 parts of an accelerant, and 1.5-1.8 parts of a vulcanizing agent. Through the adoption of the rubber composition disclosed by the invention, the lubricating property between the lug bushing and a bearing is improved, the friction noise is reduced, and the abrasion resistance is improved, so that the lug bushing is not invalid under the long-term use state, under the circumstance that the cost is not increased, the fabrication process is simple, and the lug bushing is convenient to use and mount.

Description

Technical field [0001] The invention relates to a rubber composition of a leaf spring lug bushing for automobiles, and belongs to the technical field of rubber chemicals. Background technique [0002] Automobile leaf spring lug bushing such as figure 1 As shown, the leaf spring lug bushings used in minivans and trucks are indispensable vibration damping and buffering parts. In the course of its use, especially on bumpy roads after loading, the lug bushings are carrying the deformation and wear of the extrusion force given in different directions. Many car owners often use the lug bushings when they use 2000 kilometers. The squeeze failure and damage caused the vehicle chassis to squeak abnormally during driving, and the vibration damping and cushioning effects also failed. Summary of the invention [0003] The invention aims to solve the technical problems that the existing automobile leaf spring lug bushing has poor extrusion resistance and is prone to failure and damage. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L9/06C08L45/02C08L91/02C08K13/02C08K3/04C08K5/09C08K3/22C08K5/18C08K5/3437C08K3/06C08K5/01
CPCC08K2201/014C08L7/00C08L9/06C08L2205/02C08L2205/035C08L45/02C08L91/02C08L91/00C08L91/06C08K13/02C08K2003/2296C08K5/09C08K3/04
Inventor 李庆团陈清明田中龙
Owner SHANGHAI ZHONGLI AUTO PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap