A dragon bottle, giant technology, applied in the production of large ceramic dragon bottles, can solve problems such as falling off, collapsing, and inability to connect the bottle mud body, so as to achieve bright glaze, improve stability, and improve the problems that the modules cannot be connected Effect

Inactive Publication Date: 2015-02-11
牛继伟
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for the production of giant dragon bottles with a height of more than 3 meters, since the natural drying body cannot be dried in time, the upper part of the bottle body mud body will not be connected, cracked, fallen off, collapsed, etc., and the printed body cannot be completed. production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0027] Embodiment 1: The composition and weight percentage of this embodiment are respectively: 15% of quartz, 20% of porcelain stone, 15% of feldspar powder, 30% of hard clay, 15% of loess powder, 3% of silicon micropowder and feldspar super Micronized 2%.

[0028] The composition and weight percent of described quartz are: SiO 2 98%-99%, Al 2 o 3 1%.

[0029] The composition and weight percent of described feldspar powder are: SiO 2 : 65%, Al 2 o 3 : 17.5%, K 2 O: 5.2%, Na 2 O: 5.8%, Fe 2 o 3 : 0.11%.

[0030] Composition and weight percentage of described loess powder: SiO 2 : 66.08%, Al 2 o 3 : 18.07%, Fe 2 o 2 : 0.08%, CaO: 0.28%, MgO: 0.10%, K 2 O: 13.50%, Na 2 O: 1.30%.

[0031] The composition and weight percent of described hard clay are: SiO 2 : 55%, Fe 2 o 3 : 1.5%, Al 2 o 3 : The content is 40%.

[0032] The composition and weight percentage of described china stone are: SiO 2 : 75%, Al 2 o 3 : 15.5%, K 2 O: 3.0%, Na 2 O: 1.5%, CaO: 0.6...

specific Embodiment approach 2

[0038] Specific embodiment two: the composition and weight percent of this specific embodiment are respectively: quartz 15%, porcelain stone 20%, feldspar powder 15%, hard clay 30%, loess powder 15%, silicon micropowder 3% and feldspar super Micronized 2%.

[0039] The composition and weight percent of described quartz are: SiO 2 98%-99%, Al 2 o 3 1%.

[0040] The composition and weight percent of described feldspar powder are: SiO 2 : 65%, Al 2 o 3 : 17.5%, K 2 O: 5.2%, Na 2 O: 5.8%, Fe 2 o 3 : 0.11%.

[0041] Composition and weight percentage of described loess powder: SiO 2 : 66.08%, Al 2 o 3 : 18.07%, Fe 2 o 2 : 0.08%, CaO: 0.28%, MgO: 0.10%, K 2 O: 13.50%, Na 2 O: 1.30%.

[0042] The composition and weight percent of described hard clay are: SiO 2 : 66%, Fe 2 o 3 : 0.5%, Al 2 o 3 : 30%.

[0043] The composition and weight percentage of described china stone are: SiO 2 : 76%, Al 2 o 3 : 14.5%, K 2 O: 3.6%, Na 2 O: 1.5%, CaO: 0.7%,

[0044] The p...

specific Embodiment approach 3

[0046] Specific embodiment three: the composition and weight percentage of this specific embodiment are: quartz: 18%, porcelain stone: 15%, feldspar powder: 18%, hard clay: 22%, loess powder: 23%, silicon micropowder: 1% and feldspar superfine powder 3%;

[0047] The composition and weight percent of described quartz are: SiO 2 98%-99%, Al 2 o 3 1%.

[0048] The composition and weight percent of described feldspar powder are: SiO 2 : 65%, Al 2 o 3 : 17.5%, K 2 O: 5.2%, Na 2 O: 5.8%, Fe 2 o 3 : 0.11%.

[0049] Composition and weight percentage of described loess powder: SiO 2 : 66.08%, Al 2 o 3 : 18.07%, Fe 2 o 2 : 0.08%, CaO: 0.28%, MgO: 0.10%, K 2 O: 13.50%, Na 2 O: 1.30%.

[0050] The composition and weight percent of described hard clay are: SiO 2 : 43%, Fe 2 o 3 : 0.5%, Al 2 o 3 : The content is 50%.

[0051] The composition and weight percentage of described china stone are: SiO 2 : 72%, Al 2 o 3 : 16.5%, K 2 O: 2.6%, Na 2 O: 1%, CaO: 0.5%.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
heightaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a huge vase with dragon, and its making method, and relates to the technical filed of ceramic. The huge vase with dragon comprises 12-18wt% of quartz, 15-25wt% of porcelain stone, 10-20wt% of feldspar powder, 22-35wt% of hard clay, 10-25wt% of loess powder, 1-4wt% of silicon micro-powder and 2-5wt% of feldspar submicron powder. The making method comprises the following steps: 1, making a large die; 2, making a green bottle body; and 3, sculpturing dragon on the outer side of the bottle by a sculpturer. The vase made in the invention has characteristics of hard porcelain, bright glaze, thickness reaching 0.35, a maximum waist diameter reaching 2.3m, a height reaching 6m and a high yield of 60%. The disadvantages of no bearing of the green body weight and cracking of present ceramic vases are overcome, and the phenomena of no corresponding connection between modules, collapsing and shedding are improved.

Description

Technical field: [0001] The invention belongs to the technical field of ceramics, and in particular relates to a method for making a large ceramic dragon bottle. Background technique: [0002] With the progress and development of society, the improvement of people's increasing cultural level, and the interaction of cultural industries, the art and practicality of garden ceramics are increasingly brought into play, becoming an indispensable cultural feast for garden architecture and satisfying people's viewing desires. [0003] Large-scale ceramic sculpture is a modern art ceramic that integrates viewing and use. It is not afraid of wind and rain, fog and sun, and long-term display, which cannot be replaced by any material. It decorates buildings, parks and public places, adding color to people's lives. Therefore, ceramic sculptures are sold in major cities across the country and abroad, and exported to Japan, the United States, Hong Kong and other countries and regions, wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/24C04B33/02
Inventor 牛继伟
Owner 牛继伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap