Cured type waterproof protective and thermochromic paint and preparation method thereof

A thermochromic, curing technology, applied in the field of building exterior wall waterproofing and protective coatings, can solve problems such as poor weather resistance, and achieve the effect of reducing eye glare, isolating corrosion, and obvious thermochromic effects

Inactive Publication Date: 2015-12-09
深圳大禹建设实业有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims to overcome the defects of poor weather resistance of the existing exterior wall coatings, and provides a new type of waterproof protective coating and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cured type waterproof protective and thermochromic paint and preparation method thereof
  • Cured type waterproof protective and thermochromic paint and preparation method thereof
  • Cured type waterproof protective and thermochromic paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 3

[0053] The third group (embodiment 3.1-3.3)

[0054] In component A Hardener Epoxy resin (trade name 637E-35); Thinner to ethyl acetate.

[0055] Put the curing agent into the reaction kettle with agitator, raise the temperature of the material to 120°C under stirring, and vacuumize to reduce the pressure in the reaction kettle to -0.09MPa, so that the moisture content brought by the raw materials is reduced to Below 0.05% of the total amount of materials added, after cooling down to 45°C, add 10 parts of diluent, mix under normal pressure for 30 minutes, cool down to below 35°C, and obtain A component.

[0056] In component B waterproof film former It is a two-terminal amino polyether (trade name PEA), and its molecular weight is 2000±200; UV blocker It is yellow or red or green transparent nanometer ferric oxide; the nanometer ferric oxide is also thermochromic agent , due to the certain complexation of yellow or red or green transparent nanometer ferric oxide an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of manufacturing of exterior wall waterproof and protective paints for buildings and specifically discloses a cured type waterproof protective and thermochromic paint and a preparation method thereof. The cured type waterproof protective and thermochromic paint is prepared from a component A and a component B; the component A is prepared from 50-90 parts of curing agent and 0-100 parts of diluent in parts by weight; the component B is prepared from 100 parts of waterproof film forming agent, 0.5-40 parts of ultraviolet separant, 0-25 parts of thermochromic color-changing agent and 0-5 parts of dispersant in parts by weight. The cured type waterproof protective and thermochromic paint has the capabilities of effectively isolating moisture from seeping into a protected inkjet decoration coating and effectively isolating the corrosion of acid rain to the inkjet decoration coating, is remarkable and adjustable in thermochromic effect and has the isolation rate to ultraviolet up to 83%. The preparation method disclosed by the invention is simple and feasible and can be applied to industrial production.

Description

【Technical field】 [0001] The invention relates to the technical field of waterproof and protective coatings for exterior walls of buildings, in particular to a curing type waterproof protective and thermochromic coating and a preparation method thereof. 【Background technique】 [0002] With the acceleration of urbanization, the increasing scale of cities and the increasing density of buildings not only bring convenience to life, but also make people's living environment and visual space oppressive, and have a negative impact on people's mental health. . [0003] For this reason, architects strive to improve the engineering aesthetics structure. However, these current methods have insurmountable defects, such as: glass curtain wall, although beautiful, is prone to sunlight reflection and focus pollution; covered tiles, although the beautification effect is good But it is easy to weather and fall off, causing safety hazards. [0004] Color coatings have attracted much attenti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D171/00C09D183/04C09D175/04C09D7/12C09D5/08C09D5/26
Inventor 梁江华郭倩李淑兆梁卫民
Owner 深圳大禹建设实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap