A special midsole for molded shoes made of straw and its preparation method

A molding and straw technology, which is applied to the special midsole for molded shoes and its preparation field, can solve the problems of polluting the environment, difficult to handle, increase weight, etc., and achieve the effects of being beneficial to environmental protection, low cost, and using less glue brushing personnel.

Inactive Publication Date: 2018-05-08
JIHUA 3515 LEATHER & SHOES
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Every year, a large amount of waste crop stalks are burned or discarded, which not only pollutes the environment, but also causes huge waste
[0003] The midsole of traditional molded shoes is made of natural bottom leather, synthetic leather and other sheets. After punching and forming, it is glued and vulcanized during use. Difficult to handle, causing pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A special midsole for molded shoes made of straw and its preparation method
  • A special midsole for molded shoes made of straw and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A special midsole for molded shoes made of straw is prepared from the following raw materials in parts by weight: 60-70 parts of straw, 2.5-3.5 parts of waterproofing agent, and 25-35 parts of molding rubber. The waterproofing agent is preferably an acrylic resin with waterproof function. The molded rubber can be used in the prior art to make molded rubber for the sole of molded shoes. The vulcanizing agent and vulcanization accelerator in the molded rubber preferably have good post-vulcanization properties. performance. Preferably, the molding compound is composed of natural rubber, anti-aging agent, auxiliary agent, solvent oil, vulcanizing agent and vulcanization accelerator. The anti-aging agent is preferably used in combination with anti-aging agent MB and anti-aging agent 4010NA. The auxiliary agent is composed of activator stearic acid, Composed of zinc oxide, reinforcing agent white smoke, tackifier yellow coumarone, solvent oil is preferably No. 120 solvent oil...

Embodiment 2

[0035] A special midsole for molded shoes made of straw is prepared from the following raw materials in parts by weight: 70 parts of straw, 3 parts of acrylic resin waterproofing agent, and 30 parts of molding rubber. The molding compound is composed of the following raw materials in parts by weight: 65 parts of natural rubber, 1.2 parts of anti-aging agent MB, 1.3 parts of anti-aging agent 4010NA, 0.5 parts of stearic acid, 8.5 parts of zinc oxide, 1.1 parts of white smoke, 2.6 parts of yellow coumarone 25 parts of solvent oil, 2.0 parts of sulfur, 1.1 parts of accelerator CZ, and 1.1 parts of accelerator DM.

[0036] The method for preparing the midsole for molded shoes made of straw includes the following steps:

[0037] (1) Straw treatment: Wash and dry the straw, remove debris and straw branches and leaves, leaving only the wooden poles to be crushed through a 100-mesh sieve;

[0038] (2) Production of masticated rubber material: masticate the natural rubber, then add th...

Embodiment 3

[0046] A special midsole for molded shoes made of straw is prepared from the following raw materials in parts by weight: 60 parts of straw, 2.5 parts of acrylic resin waterproofing agent, and 25 parts of molding rubber. The molding compound is composed of the following raw materials in parts by weight: 65 parts of natural rubber, 1.25 parts of anti-aging agent MB, 1.3 parts of anti-aging agent 4010NA, 0.41 parts of stearic acid, 8.34 parts of zinc oxide, 1.21 parts of white smoke, 2.50 parts of yellow coumarone 25 parts of solvent oil, 2.0 parts of sulfur, 1.06 parts of accelerator CZ, and 1.1 parts of accelerator DM.

[0047] The method for preparing the midsole for molded shoes made of straw includes the following steps:

[0048] (1) Straw treatment: Wash and dry the straw, remove debris and straw branches and leaves, leaving only the wooden poles to be crushed through a 100-mesh sieve;

[0049] (2) Production of masticated rubber material: masticate the natural rubber, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a special midsole for molded shoes made of straw and a preparation method thereof, which is prepared from the following raw materials in parts by weight: 60-70 parts of straw, 2.5-3.5 parts of waterproofing agent, and 25-35 parts of molding rubber . The special midsole for molded shoes of the present invention utilizes the discarded straw of crops, removes its attached leaves, and only uses its stalk, which is crushed, mixed with molding rubber, and pressed. The crop straw is inexhaustible and the weight Lightweight, so the special midsole for molded shoes is low in cost and light in weight, which can reduce the cost and weight of finished shoes.

Description

technical field [0001] The invention belongs to the technical field of shoe processing, and in particular relates to a special midsole for molded shoes made of straw and a preparation method thereof. Background technique [0002] Every year, a large amount of waste crop stalks are burned or discarded, which not only pollutes the environment, but also causes huge waste. [0003] The midsole of traditional molded shoes is made of natural bottom leather, synthetic leather and other sheets. After punching and forming, it is glued and vulcanized during use. Difficult to handle and cause pollution. Contents of the invention [0004] The object of the present invention is to provide a special midsole for molded shoes made of straw and a preparation method thereof in order to solve the deficiencies of the prior art. [0005] The purpose of the present invention is achieved with the following technical solutions: [0006] A special midsole for molded shoes made of straw is prepa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L97/02C08L7/00C08L33/00C08K13/02C08K5/09C08K3/22C08K3/06A43B13/04
CPCA43B13/04C08L97/02C08L2201/06C08L2205/035C08L7/00C08L91/00C08L45/02C08L33/00C08K13/02C08K5/09C08K2003/2296C08K3/06
Inventor 肖慧
Owner JIHUA 3515 LEATHER & SHOES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap