Low-alloy high-strength large-diameter thick-wall seamless steel pipe and manufacturing method thereof

A low-alloy high-strength, seamless steel pipe technology, applied in the field of metallurgy, can solve the problems of high scrap rate and complex heat treatment process, and achieve the effect of preventing grain growth, reducing production costs, and making grains fine and uniform.

Active Publication Date: 2017-07-07
PANGANG GROUP CHENGDU STEEL & VANADIUM
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a low-alloy high-strength large-diameter thick-walled seamless steel pipe and its manufacturing method, so as to solve the complicated heat treatment process and the scrap rate of the current low-alloy high-strength large-diameter thick-walled seamless steel pipe during manufacture. higher question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-alloy high-strength large-diameter thick-wall seamless steel pipe and manufacturing method thereof
  • Low-alloy high-strength large-diameter thick-wall seamless steel pipe and manufacturing method thereof
  • Low-alloy high-strength large-diameter thick-wall seamless steel pipe and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Embodiment 1 is used to produce a steel pipe with a specification of Φ298.5×70 mm and a steel grade of S355J2H.

[0039] The production process is: electric furnace smelting→LF furnace refining→VD vacuum treatment→ingot casting→forging tube billet→annealing→ring furnace heating→piercing→pipe rolling unit rolling→inspection→normalizing (air cooling + fog cooling)→ Straightening→super detection→inspection→packing.

[0040] The above-mentioned production process will be described in detail below.

[0041] First, the target molten steel is obtained through electric furnace smelting, LF furnace refining, and VD vacuum treatment, and the target molten steel is cast into an ingot to obtain a die-casting steel ingot. The chemical composition of the target molten steel is shown in Table 1. In Table 1, the target molten steel has a carbon equivalent of 0.47% to 0.51%. +Spray cooling" or "air cooling" enhanced cooling to produce large-diameter thick-walled pipes can avoid the si...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of metallurgy, and provides a low-alloy high-strength large-diameter thick-walled seamless steel pipe and a manufacturing method thereof. The method comprises the steps of steelmaking, wherein smelting and refining are performed to obtain target molten steel, and ingot casting is performed on the target molten steel to obtain static ingots; pipe billet forging, wherein forging and annealing are performed on the static ingots to obtain pipe billets; pipe rolling, wherein the pipe billets are heated inside an annular furnace at the temperature of 1230-1270 DEG C, holes are formed after heating is performed, and rolling forming is performed through a pipe mill; normalizing heat treatment, wherein normalizing heat treatment is performed on rolled and formed steel pipes, the normalizing furnace discharge pipe temperature is 920-940 DEG C in the normalizing heat treatment process, and the cooling mode is the air-cooling or air-cooling and mist spraying mode. The steel pipe produced through the manufacturing method is uniform in texture, good in performance and capable of achieving high-strength and excellent subzero 20 DEG C low-temperature toughness, in addition, by adopting the simplified production technology, the production efficiency can be improved, the production cost can be lowered, and meanwhile the steel pipe has the good using safety due to the low yield ratio.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, in particular to a low-alloy, high-strength, large-diameter thick-wall seamless steel pipe and a manufacturing method thereof. Background technique [0002] At present, low-alloy high-strength seamless steel pipes are widely used in construction machinery, grid structures and other industries, especially in the fields of marine engineering equipment and port machinery and equipment, the demand for large-diameter thick-walled seamless steel pipes is increasing. [0003] For low-alloy high-strength seamless steel pipe products, the manufacturing methods are also very different according to different strength level requirements and specifications. For large-diameter thick-walled seamless steel pipes, the general manufacturing method is to select a certain composition, after thermal processing, and then through the quenching and tempering heat treatment process to achieve the required strength lev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/08C22C38/16C22C38/14C22C38/12C22C38/06C22C38/18C21D8/10C21D1/28
CPCC21D1/28C21D8/105C21D2211/002C21D2211/005C21D2211/009C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/14C22C38/16C22C38/18
Inventor 吴红林发驹王洪利白青青王西江陈雨
Owner PANGANG GROUP CHENGDU STEEL & VANADIUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com