Multifunctional putty cream for tile-like paints and preparation method thereof

A multi-functional, putty paste technology, applied in the direction of filling slurry, etc., can solve the problems of time-consuming, material-consuming, labor-intensive, easy to crack, strong rigidity of putty, etc., and achieve the effect of reducing procedures, saving costs, and simple construction

Inactive Publication Date: 2016-12-21
鳄鱼制漆(上海)有限公司 +1
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] From the above traditional construction techniques, it can be seen that three materials such as putty, primer and intermediate paint need to be applied before the imitation brick coating is applied, which is time-consuming, material-intensive and labor-intensive.
Moreover, the putty of inorganic gelling material has strong rigidity and is easy to crack

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional putty cream for tile-like paints and preparation method thereof
  • Multifunctional putty cream for tile-like paints and preparation method thereof
  • Multifunctional putty cream for tile-like paints and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029]

[0030] The multifunctional putty paste used for brick imitation paint in this embodiment is a black putty paste. The particle size of each component of the filler is reasonable, easy to scrape and level the base layer, and the color is black. It can be used in the black line imitation brick paint system. use. The construction process is reduced from the original 4 to 2.

[0031] Preparation:

[0032] After adding fungicides, dispersants, defoamers, and alcohol ester twelve into the water, add hydroxypropyl methylcellulose, titanium dioxide and 300 mesh heavy calcium carbonate under stirring conditions, stir at high speed for 15 minutes, and then add elastic Acrylic emulsion, 80-120 mesh quartz sand and 2mm polypropylene short fiber, stir for 5-10 minutes, finally add carbon black slurry, mix well and then discharge.

[0033] Construction methods for imitation brick coatings:

[0034] Direct scraping construction on the wall surface, one or two layers can be appl...

Embodiment 2

[0036]

[0037] The multifunctional putty paste used for imitation brick paint in this embodiment is a yellow putty paste. The particle size of each component of the filler is relatively large, which is easy to scratch and is used for the base layer with poor flatness. The color is yellow and can be used on the yellow line Used in faux brick paint systems.

[0038] Preparation:

[0039] After adding bactericide, dispersant, defoamer, and alcohol ester twelve into the water, add hydroxypropyl methylcellulose, titanium dioxide and 200 mesh heavy calcium carbonate under stirring conditions, stir at high speed for 15 minutes, and then add elastic Acrylic emulsion, 50-80 mesh quartz sand and 3mm polypropylene short fiber, stir for 5-10 minutes, finally add iron yellow slurry, mix well and then discharge.

[0040] Construction methods for imitation brick coatings:

[0041] Direct scraping construction on the wall surface, one or two layers can be applied to make the flatness of...

Embodiment 3

[0043]

[0044] The multifunctional putty paste for imitation brick coating of this embodiment is a brown putty paste, the particle size of each component of the filler is small, good flexibility, easy to scrape and used for the better base layer of flatness, the color is brown, It can be used in brown line imitation brick paint system.

[0045] Preparation:

[0046] After adding bactericide, dispersant, defoamer, and alcohol ester twelve into the water, add hydroxypropyl methylcellulose, titanium dioxide and 800 mesh heavy calcium carbonate under stirring conditions, stir at high speed for 15 minutes, and then add elastic Acrylic emulsion, 120-180 mesh quartz sand and 1mm polypropylene short fiber, stir for 5-10 minutes, finally add iron yellow, iron red, carbon black slurry, mix well and then discharge.

[0047] Construction methods for imitation brick coatings:

[0048] Direct scraping construction on the wall surface, one or two layers can be applied to make the flatn...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a multifunctional putty cream for tile-like paints. The multifunctional putty cream is prepared from water, a bactericide, a dispersing agent, a defoaming agent, a film forming aid, hydroxypropyl methylcellulose, an acrylic acid emulsion, titanium white, ground calcium carbonate, quartz sand, polypropylene staple fibers and a water-based color paste. The invention also discloses a preparation method of the multifunctional putty cream for tile-like paints. The multifunctional putty cream for tile-like paints has the comprehensive characteristics of the putty, primer and middle paint, integrates the three procedures into one procedure, and is an effective anti-cracking material. The multifunctional putty cream for tile-like paints is applicable to construction matched with the tile-like paint technique, can be subjected to color modulation, and can substitute forthe putty primer and tile-like striper paint in the original system. The multifunctional putty cream for tile-like paints has favorable flexibility, can effectively shield fine cracks in the substrate, and saves the working hours and cost.

Description

technical field [0001] The invention relates to a multifunctional putty paste, which is used as a supporting material for imitation brick effect paint, and belongs to the field of building materials, in particular to a multifunctional putty paste for imitation brick paint and a preparation method thereof Background technique [0002] The brick-like effect paint is a common decoration method on the wall at present. The conventional construction technology is leveling putty, alkali-resistant primer, rolling line color intermediate paint, and brick-like texture paint. The main component of putty is inorganic gel material-cement. After the inorganic gel material encounters water, the hydration reaction starts, and the calcium hydroxide solution reaches saturation and precipitates crystals, which causes the surface of the base layer to show high alkalinity after construction (pH value> 12) Excessive alkalinity will easily cause the color paste of the latex paint on the surface...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 王律胡晓龙项继红
Owner 鳄鱼制漆(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com