A kind of cu-containing microalloy high-strength high-toughness steel and its production method

A high-toughness steel and high-strength technology, applied in the field of microalloyed steel preparation, can solve the problems of increased production costs, large fluctuations in low-temperature impact properties, and easy occurrence of harmful Widmandelsteiner structures, and achieves the effect of saving production costs and reducing content requirements.

Active Publication Date: 2021-08-24
ZENITH STEEL GROUP CORP CO LTD +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the addition of Nb not only effectively improves the performance, but also increases the production cost, and the difficulty of controlling the surface quality of the steel is greatly increased. More importantly, the low-alloy high-strength steel containing Nb is prone to harmful microbeads during subsequent heat treatment. structure, low temperature impact performance fluctuates greatly and poor stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cu-containing microalloy high-strength high-toughness steel and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Adopt the process route of EAF-CONVERTER electric converter smelting→LF furnace refining→VD vacuum treatment→CCM continuous casting to produce Cu-containing micro-alloy high-strength and high-toughness steel,

[0025] Smelting finished product composition control: C: 0.13%, Si: 0.36%, Mn: 1.50%, P: ≤0.010%, S: ≤0.010%, Cr: 0.19%, Cu: 0.25%, Ni: 0.12%, V: 0.09 %, Ti: 0.03%, Al: 0.028%, the balance is Fe,

[0026] The electric converter uses molten iron, pig iron and high-quality steel scrap as raw materials. The total charge is controlled at 100.5 tons, the ratio of molten iron is 93%, the amount of pig iron added is 2.5 tons, and the rest is high-quality steel scrap. %, tapping temperature T: 1634°C, tapping volume 85.9 tons, eccentric bottom tapping and steel retention operation, strictly prohibiting tapping and slag; adding appropriate amount of Al blocks and calcium carbide for deoxidation during tapping, adding low carbon after furnace Ferromanganese, ferrosilicon,...

Embodiment 2

[0034]Adopt the process route of EAF-CONVERTER electric converter smelting→LF furnace refining→VD vacuum treatment→CCM continuous casting to produce Cu-containing micro-alloy high-strength and high-toughness steel,

[0035] Smelting finished product composition control: C: 0.14%, Si: 0.40%, Mn: 1.36%, P: ≤0.010%, S: ≤0.010%, Cr: 0.23%, Cu: 0.26%, Ni: 0.12%, V: 0.12 %, Ti: 0.025%, Al: 0.032%, the balance is Fe,

[0036] The electric converter uses molten iron, pig iron and high-quality steel scrap as raw materials. The total charge is controlled at 102.12 tons, the molten iron ratio is 91%, the pig iron addition is 4.3 tons, and the rest is high-quality steel scrap. The composition of the tapping end point is C: 0.04%, P: 0.005 %, tapping temperature T: 1638°C, tapping volume 87.2 tons, eccentric bottom tapping and steel retention operation, strictly prohibiting tapping and slag; adding appropriate amount of Al block and calcium carbide for deoxidation during tapping, adding lo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of micro-alloy steel preparation, in particular to a Cu-containing micro-alloy high-strength high-toughness steel and a production method thereof. Micro-alloyed high-strength and high-toughness steel components C: 0.10-0.18%, Si: 0.25-0.50%, Mn: 1.00-1.70%, P≤0.020%, S≤0.015%, Cr≤0.30%, Cu≤0.50% , Ni ≤ 0.50%, V ≤ 0.20%, Ti: 0.02~0.20%, Al ≥ 0.015%, the balance is Fe, realizing the design of Nb-free composition, and effectively reducing the Ni content in the steel, making full use of the trace alloy The strong and tough effect can significantly improve the comprehensive mechanical properties of steel.

Description

technical field [0001] The invention belongs to the field of micro-alloy steel preparation, in particular to a Cu-containing micro-alloy high-strength high-toughness steel and a production method thereof. Background technique [0002] Due to its strong formability and good welding performance, micro-alloyed high-strength steel has been widely used as an important material for structural purposes, especially the micro-alloyed high-strength steel with a yield strength above 500Mpa is particularly widely used. At the same time, In recent years, with the rapid development of transportation, construction, engineering machinery and other industries, the toughness and plasticity of the micro-alloyed high-strength steel used have also put forward higher and higher requirements. [0003] In order to improve the comprehensive mechanical properties of microalloyed steels, adding Nb to steel is a very common method at present. However, the addition of Nb not only effectively improves t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/04C22C38/02C22C38/14C22C38/06C22C38/12C22C38/16C22C38/08C22C38/28C22C38/20C22C38/38C22C38/24C22C38/50C22C38/44C22C38/46C22C38/58C21D8/00
CPCC21D8/005C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/14C22C38/16C22C38/20C22C38/24C22C38/28C22C38/38C22C38/44C22C38/46C22C38/50C22C38/58
Inventor 高宇波朱富强万文华
Owner ZENITH STEEL GROUP CORP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com