TMCP-state low-cost high-strength ship plate steel for high-heat input welding and manufacturing method of TMCP-state low-cost high-strength ship plate steel

A high-energy-input welding and low-cost technology, applied in the field of metallurgy, can solve the problems of decreased mechanical properties of welded joints, deterioration of low-temperature toughness, and high cost, and achieve the effects of stable production process, improved toughness, and reasonable composition

Active Publication Date: 2017-05-31
NANJING IRON & STEEL CO LTD
View PDF9 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] When the welding heat input is greater than 50kJ/cm, it is called large input energy welding. When the welding heat input of traditional steel plates is greater than 50kJ/cm, due to the excessive coarsening of the structure of the welding heat-affected zone, the mechanical properties of the welded joint will be seriously reduced, and even It is lower than the standard requirements of the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TMCP-state low-cost high-strength ship plate steel for high-heat input welding and manufacturing method of TMCP-state low-cost high-strength ship plate steel
  • TMCP-state low-cost high-strength ship plate steel for high-heat input welding and manufacturing method of TMCP-state low-cost high-strength ship plate steel

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example

[0029] Examples 1-3 are the manufacturing method of high-strength ship plate steel for 60mm thick E40 high heat input welding, using low-carbon niobium-free, oxide metallurgical process, adding trace elements Ni and V, and using controlled rolling and controlled cooling technology.

[0030] The main chemical components of Examples 1-3 are shown in Table 1:

[0031] Table 1 The main chemical composition of the embodiment of the present invention (wt%)

[0032] ExampleC Si MnPS AltV Ti Ni Ceq Example 10.080.241.520.0080.00100.0220.0300.0120.330.36 Example 20.100.201.400.0100.00180.0250.0450.0220.250.36 Example 30.050.281.600.0140.00200.0400.0500.0200.280.35

[0033] The rolling cooling process parameters of each embodiment are shown in Table 2:

[0034] Table 2 Rolling cooling process parameters

[0035] Example Thickness mm Rough rolling final rolling temperature℃ Finish rolling opening temperature ℃ Final rolling temperature℃ Redness temperature ℃ Example 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses TMCP-state low-cost high-strength ship plate steel for high-heat input welding. The TMCP-state low-cost high-strength ship plate steel comprises the chemical components in percentage by weight: 0.04-0.12% of C, 0.15-0.35% of Si, 1.10-1.70% of Mn, less than or equal to 0.020% of P, less than or equal to 0.0030% of S, 0.030-0.060% of V, 0.005-0.060% of Alt, 0.32-0.41% of Ceq, 0.005-0.030% of Ti, 0.0005-0.0040% of Ca, 0.05-0.40% of Ni and the balance of Fe and unavoidable impurities. The steel plate disclosed by the invention has the yield strength of larger than or equal to 400MPa and the tensile strength of larger than or equal to 510MPa, is suitable for high-strength ship plate steel with welding heat input being within the range of 150-250kJ/cm, the average impact power of HAZ of the steel plate under 40 DEG C is higher than 150J under the high-heat input welding conditions of 150kJ/cm and 250kJ/cm, heat treatment is not needed, and the production cost is low.

Description

Technical field [0001] The invention belongs to the technical field of metallurgy, and relates to a high-strength ship plate steel for welding with large heat input and a manufacturing method thereof, specifically, a high-strength ship plate steel for welding with a 60mm thick E40 grade TMCP state low-cost and large heat input and its manufacturing method. Background technique [0002] High heat input welding steel is widely used. For example, in the shipbuilding industry, the shipbuilding efficiency of ordinary ship plates is only one-fourth of that of high heat input welding ship plates. When domestic production is not possible, it can only be imported from abroad, but the price is expensive. The high heat input welding method is the most practical way to improve the efficiency of welding construction and reduce the cost. The "Guide to the Development of Science and Technology of China's Iron and Steel Industry from 2006 to 2020" proposes that high heat input welding steel is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/04C22C38/02C22C38/12C22C38/06C22C38/14C22C38/08C22C33/04C21C7/10C21C7/00C21D8/02
CPCC21C7/0006C21C7/10C21D8/0226C22C33/04C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/14
Inventor 赵晋斌付军邱永清
Owner NANJING IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap