A polyurethane hot-melt adhesive humidifying agent and a film-attaching method using the humidifying agent

A technology of hot melt adhesive and wetting agent, applied in the direction of adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of difficult to guarantee humidity through control measures, reduced bonding strength, failure of cross-linking reaction, etc. , to shorten the cross-linking reaction time, reduce the self-solidification phenomenon, and ensure the effect of bonding strength

Active Publication Date: 2018-09-14
黑龙江林海华安新材料股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Once the humidity or temperature fluctuates greatly during the reaction process, the cross-linking reaction will slow down, the cross-linking reaction will fail, the bonding strength will be greatly reduced, and the film will fall off.
[0005] Due to the vast territory of our country, the climate in the north is dry, the humidity is extremely low, and the ambient temperature and day and night changes greatly in the four seasons. Under such unfavorable climatic conditions, the application of moisture-responsive PUR hot-melt adhesives is greatly restricted. In the actual production environment, the continuous temperature can be maintained by compulsory means, but the persistent humidity is difficult to be guaranteed by control measures, which is very unfavorable for the application of moisture-responsive PUR hot melt adhesives in decorative materials. Impact

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A polyurethane hot-melt adhesive humidifying agent and a film-attaching method using the humidifying agent
  • A polyurethane hot-melt adhesive humidifying agent and a film-attaching method using the humidifying agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] Starting from the specific working scheme, the technical scheme of the present invention will be further described in conjunction with the accompanying drawings.

[0027] A moisture-responsive PUR hot-melt adhesive humidifying agent, which is composed of demineralized water, anionic surfactant and powdery diatomite adsorbent. Add the anionic surfactant at a ratio of 0.2 liters of water, and add powdered diatomite adsorbent at a ratio of 0.6 kg per 100 liters of demineralized water.

[0028] The preparation method of the moisture-responsive PUR hot-melt adhesive humidifying agent is to take the amount of demineralized water, add the above-mentioned corresponding proportion of 800-1000 mesh powdery diatomite adsorbent, stir for 10 minutes, and then let it stand for 20 minutes , and then put the suspended liquid in another container, and then add the above-mentioned corresponding proportion of anionic surfactant to the suspended liquid, stir for 3 minutes, and prepare the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a moisture reactive PUR (polyurethane resin) hot melt adhesive wetting agent and a preparation method thereof and a PUR film sticking method using the moisture reactive PUR (polyurethane resin) hot melt adhesive wetting agent. The moisture reactive PUR (polyurethane resin) hot melt adhesive wetting agent comprises softening water, a wetting agent and a powdery adsorbent, the softening water is a basic component, and 0.05-0.5 liter of the wetting agent and 0.1-1 kg of the powdery adsorbent are added into every 100 liters of the softening water. The PUR film sticking method is as follows: a certain amount of moisture reactive PUR (polyurethane resin) hot melt adhesive wetting agent with affinity water molecules is forcibly replenished into a dry basic material, the hot melt adhesive wetting agent can be uniformly sufficiently blended into an adhesive film in a short period of time so as to promote initiation of crosslinking curing reaction of the sticky adhesive film as soon as possible, self solidification phenomenon of the PUR hot melt adhesive film is reduced, cross-linking reaction time is reduced, product processing cycle is shortened, bonding strength is ensured, and product quality is improved.

Description

technical field [0001] The present invention relates to a polyurethane (PUR) hot melt adhesive humidifying agent and a film sticking method using the humidifying agent, in particular to a moisture-responsive PUR hot-melt adhesive humidifying agent and the use of the moisture-reactive PUR hot-melt adhesive to humidify Agent PUR film method. Background technique [0002] At present, the moisture-responsive polyurethane hot-melt adhesive is the first choice in the film-sticking process of interior decoration materials as the adhesive for plastic films, that is, a moisture-responsive PUR hot-melt adhesive. This hot-melt adhesive does not need to add any solvents during use. And polar strong oxidation initiator, with high initial bond strength, safe and non-toxic, easy to operate and so on. [0003] The gluing reaction mechanism of the moisture-responsive PUR hot-melt adhesive is as follows: the NCO functional group at the end of the molecular chain of the hot-melt adhesive reac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J11/00C09J11/04C08G18/30
CPCC08G18/307C08K3/34C09J11/00C09J11/04
Inventor 宋月成张济民王本永宋希民佘庆涛左迅宇
Owner 黑龙江林海华安新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com