Waterborne high temperature resistant paint and preparation method thereof

A high-temperature-resistant, water-based technology, applied in the direction of anti-corrosion coatings, fire-resistant coatings, coatings, etc., can solve the problems of high-temperature resistance that needs to be further improved, poor thermal hardness and other physical properties, and serious environmental pollution, so as to alleviate VOC volatilization problems, excellent corrosion resistance, and the effect of improving the atmospheric environment

Inactive Publication Date: 2018-12-07
HEBEI BIERNIKE CO LTD
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, high-temperature-resistant paints are all oil-based products, which cannot meet the strict requirements of the country on VOC emissions, are highly toxic, and cause serious environmental pollution. Therefore, the use of water-based paints with high-temperature resistance has become an inevitable choice.
However, although the few existing water-based paints with high temperature resistance have good decorative effects, they have poor stability, poor corrosion resistance, relatively poor hot hardness and other physical properties, especially high temperature resistance. to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne high temperature resistant paint and preparation method thereof
  • Waterborne high temperature resistant paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0091] The preparation method of the present invention not only has the advantages of cleanliness, high efficiency, and low cost, but also has good stability of the prepared product, and is easy to operate, environmentally friendly, mild in preparation conditions, low in investment, low in energy consumption, and does not need to use complicated equipment systems, and is easy to It realizes industrialized mass production and has industrial applicability.

[0092] In a preferred embodiment, the preparation method of this water-based high temperature resistant paint comprises the following steps:

[0093] Take each component according to the mass parts;

[0094] First put the water-based modified silicone resin and water-based aluminum silver paste in the reaction kettle, and stir at a low speed; then add deionized water into the reaction kettle, and stir at a low speed; then add other additives into the reaction kettle, and stir and mix evenly. The water-based high temperature...

Embodiment 1

[0098] A water-based heat-resistant paint, comprising the following components in parts by mass:

[0099] 65 parts of water-based modified silicone resin, 16 parts of water-based aluminum silver paste, 6 parts of drier, 2 parts of leveling agent, 2 parts of dispersant and 9 parts of water.

Embodiment 2

[0101] A water-based heat-resistant paint, comprising the following components in parts by mass:

[0102] 56 parts of water-based modified silicone resin, 28 parts of water-based aluminum silver paste, 1 part of drier, 2 parts of leveling agent, 2 parts of dispersant and 11 parts of water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of coatings, and relates to a waterborne high temperature resistant paint and a preparation method thereof. The waterborne high temperature resistant paintcomprises the following components in parts by mass: 55-65 parts of waterborne modified silicone resin, 15-30 parts of waterborne aluminium silver paste, 1-8 parts of a drier, 2-7 parts of a levelingagent, 2-7 parts of a dispersant and 8-15 parts of water. The waterborne high temperature resistant paint has excellent high temperature resistance and excellent corrosion resistance, adhesive forceand impact-resistant strength.

Description

technical field [0001] The invention belongs to the technical field of coatings, and relates to water-based coatings, in particular to a water-based high-temperature-resistant paint and a preparation method thereof. Background technique [0002] In recent years, due to the deterioration of the ecological environment, environmental protection has attracted more and more attention from the world. Various countries have formulated relevant regulations to strictly limit the emission of volatile organic compounds (VOC) in coatings. Solvent-based coatings contain a large amount of VOC components, which not only pollute the environment and waste resources, but also endanger people's health. With the development of the coating industry and painting towards low pollution, low-pollution water-based coatings, light-cured coatings, powder coatings and high-solid coatings have become the development direction of coatings. Among them, compared with other low-pollution coatings, water-ba...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D183/06C09D183/08C09D5/10C09D7/20
CPCC08K2003/0812C09D5/103C09D5/18C09D7/20C09D183/06C09D183/08C08K9/10C08K3/08
Inventor 袁洪青
Owner HEBEI BIERNIKE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com