A kind of sunshade fabric and preparation method thereof

A fabric and rectangle technology, applied in the direction of fabric surface trimming, fire-retardant and flame-retardant filament manufacturing, woven fabrics, etc., can solve the problems of cumbersome technical process and weakened self-cleaning performance.

Active Publication Date: 2021-04-23
NINGBO XIANFENG NEW MATERIAL
View PDF16 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] Disclosed as publication number CN103757876A is a kind of self-cleaning waterproof sunshade fabric and preparation method thereof, but this technical process is comparatively loaded down with trivial details, and because traditional self-cleaning property paint is difficult to and sunshade material base material (polyester or polyvinyl chloride material) Compatibility, after a long time, the self-cleaning performance of this surface treatment will gradually weaken

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of sunshade fabric and preparation method thereof
  • A kind of sunshade fabric and preparation method thereof
  • A kind of sunshade fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0075] a kind of like Figure 1-3 The sunshade fabric shown includes fiber threads forming a double warp and double weft structure, including rectangular voids in the structure, and the fiber threads are made of halogen-free polyolefin composite materials through the following methods:

[0076] S1: Weigh raw materials by weight: 60 parts of linear low density polyethylene, 15 parts of ethylene-vinyl acetate copolymer, 20 parts of halogen-free flame retardant, 3 parts of expandable graphite, 3 parts of flame retardant synergist, 15 parts of flow modifier, 2 parts of polyvinylidene fluoride, 1 part of nano-titanium dioxide, 3 parts of compatibilizer, 1.5 parts of PE wax, 0.3 parts of 2-hydroxy-4-octyloxybenzophenone, hindered phenolic anti 0.3 parts of oxygen agent, 0.4 parts of toner, wherein the compatibilizer is maleic anhydride grafted high-density polyethylene, polymethyl methacrylate, γ-methacryloxy Propyltrimethoxysilane and ethylene-methyl acrylate copolymer, and the ma...

Embodiment 2

[0081] a kind of like Figure 1-3 The sunshade fabric shown includes fiber threads forming a double warp and double weft structure, including square voids in the structure, and the fiber threads are made of halogen-free polyolefin composite materials through the following methods:

[0082] S1: Weigh raw materials by weight: 60 parts of linear low density polyethylene, 15 parts of ethylene-vinyl acetate copolymer, 23 parts of halogen-free flame retardant, 4 parts of expandable graphite, 4 parts of flame retardant synergist, 17 parts of flow modifier, 2 parts of polyvinylidene fluoride, 1 part of nano-titanium dioxide, 4 parts of compatibilizer, 1.6 parts of PP wax, 0.3 parts of 2-hydroxy-4-octyloxybenzophenone, hindered phenolic anti 0.3 parts of oxygen agent, 0.4 parts of toner, wherein the compatibilizer is maleic anhydride grafted high-density polyethylene, polymethyl methacrylate, γ-methacryloxy Propyltrimethoxysilane and ethylene-methyl acrylate copolymer, and the maleic ...

Embodiment 3

[0087] The only difference from Example 1 is that the raw materials of Example 3 are: 60 parts of linear low density polyethylene, 15 parts of ethylene-vinyl acetate copolymer, 25 parts of halogen-free flame retardant, 4.5 parts of expandable graphite, flame retardant 4.5 parts of synergist, 17 parts of flow modifier, 2 parts of polyvinylidene fluoride, 1 part of nano-titanium dioxide, 4.5 parts of compatibilizer, 1.6 parts of PP wax, 0.3 parts of 2-hydroxy-4-octyloxybenzophenone 0.3 parts, 0.3 parts of hindered phenolic antioxidant, 0.4 parts of toner, wherein the compatibilizer is maleic anhydride grafted high-density polyethylene, polymethyl methacrylate, γ- Methacryloxypropyltrimethoxysilane and ethylene-methyl acrylate copolymer, and maleic anhydride grafted high-density polyethylene copolymer with a maleic anhydride graft rate of 3%, ethylene-vinyl acetate copolymer The content of vinyl acetate in the product is 25%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Basis weightaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a sunshade fabric and a preparation method thereof, in particular to a halogen-free, flame-retardant and self-cleaning sunshade fabric and a preparation method thereof, which belong to the technical field of polymer materials. The sunshade fabric includes: forming a double warp and double weft structure Fiber strands, the structure includes rectangular or square voids, the fiber strands are made of halogen-free polyolefin composite materials, wherein, the halogen-free polyolefin composite materials, by weight parts, include: linear low-density poly 50-70 parts of ethylene, 15-20 parts of ethylene-vinyl acetate copolymer, 20-30 parts of halogen-free flame retardant, 3-5 parts of expandable graphite, 1-5 parts of flame retardant synergist, flow modifier 10‑20 parts, 1‑3 parts of polyvinylidene fluoride, 1‑3 parts of nano-titanium dioxide, 3‑8 parts of compatibilizer, 2‑5 parts of other additives, the sunshade fabric has high flame resistance and self-cleaning function.

Description

technical field [0001] The invention relates to a sunshade fabric, in particular to a halogen-free, flame-retardant and self-cleaning sunshade fabric and a preparation method thereof, belonging to the technical field of polymer materials. Background technique [0002] The sunshade fabric is a kind of fabric obtained by covering yarn (the fiber thread obtained by covering the surface of polyester fiber, polypropylene fiber, glass fiber, etc. with polymer plastic) or directly using various fiber threads through weaving. Most of the covered yarn fabrics. At present, most of the fiber threads used in traditional sunshade fabrics on the market are polyvinyl chloride (PVC) coated polyester fibers, which are mainly used in the building sunshade industry. PVC is a widely used general-purpose high-halogen polymer plastic with excellent processing performance. Its high halogen content makes it have good flame retardant performance, but its harm to the environment is also huge: haloge...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D03D9/00D03D1/00D03D15/283D03D15/292D03D15/513D03D13/00D06C7/02D01F8/06D01F1/07
CPCD01F1/07D01F8/06D03D1/0035D03D9/00D03D13/00D03D15/00D06C7/02D10B2321/021D10B2401/22D10B2505/18
Inventor 熊圣东俞月卫
Owner NINGBO XIANFENG NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com