An asymmetric structure paper-based graphene smart film integrating sensing and driving, preparation method and application

A graphene film and graphene technology, applied in the fields of applications, sensors, medical science, etc., to achieve the effect of good application prospects

Active Publication Date: 2022-06-17
HEFEI UNIV OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the integration problem of existing flexible intelligent sensing and flexible intelligent driving, the present invention proposes an asymmetric structure paper-based graphene intelligent film integrating sensing and driving, a preparation method and an application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An asymmetric structure paper-based graphene smart film integrating sensing and driving, preparation method and application
  • An asymmetric structure paper-based graphene smart film integrating sensing and driving, preparation method and application
  • An asymmetric structure paper-based graphene smart film integrating sensing and driving, preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method when a paper-based graphene film is applied to a flexible actuator, comprising the following steps:

[0031] First, commercial printing paper, paper, was cut into rectangles with dimensions of 75 mm × 25 mm (length × width) and immersed in a petri dish containing an aqueous solution of graphene oxide (1.5 mg / ml, 40 mL) for 5 min. After dipping, it was placed on a glass substrate and dried by heating at 40°C for 1 h. Then, the dried paper is repeatedly dipped into the graphene oxide solution to repeat the above drying process, and after 15 times of dipping, a paper-based graphene oxide film with an asymmetric structure is obtained.

[0032] Then, the film was further put into a hydroiodic acid (HI) solution for 1.5 h in the dark, washed with ethanol and water in turn, and then placed on a heating platform at 30 °C for 1 h to obtain asymmetric paper-based graphene oxide film.

[0033] Finally, it is bonded with an adhesive polyethylene film to prepa...

Embodiment 2

[0042] A preparation method when a paper-based graphene film is applied to a flexible sensor, comprising the following steps:

[0043]First, commercial printing paper was cut into rectangles with dimensions of 75 mm × 25 mm (length × width) and immersed in a petri dish containing an aqueous solution of graphene oxide (1 mg / ml, 40 mL) for 5 min. After dipping, it was placed on a glass substrate and dried by heating at 40°C for 1 h. Then, the dried paper is repeatedly dipped into the graphene oxide solution to repeat the above drying process, and after dipping for 35 times, a paper-based graphene oxide film with an asymmetric structure is obtained.

[0044] Then, the film was further put into a hydroiodic acid (HI) solution for 1.5 h in the dark, washed with ethanol and water in turn, and then placed on a heating platform at 50 °C for 1 h to obtain asymmetric paper-based graphene oxide film.

[0045] Next, the conductive copper foil is bonded to the upper surface of the paper-...

Embodiment 3

[0050] A preparation method of a paper-based graphene film integrating sensing and driving, comprising the following steps:

[0051] First, commercial printing paper, paper, was cut into rectangles with dimensions of 75 mm × 25 mm (length × width) and immersed in a petri dish containing an aqueous solution of graphene oxide (2 mg / ml, 40 mL) for 5 min. After dipping, it was placed on a glass substrate and dried by heating at 40°C for 1 h. Then, the dried paper is repeatedly dipped into the graphene oxide solution to repeat the above drying process, and after 25 times of dipping, a paper-based graphene oxide film with an asymmetric structure is obtained.

[0052] Then, the film was further put into a hydroiodic acid (HI) solution for 1.5 h in the dark, washed with ethanol and water in turn, and then placed on a heating platform at 40 °C for 1 h to obtain asymmetric paper-based graphene oxide film.

[0053] Next, the conductive copper foil is bonded to the upper surface of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

An asymmetric structure paper-based graphene smart film integrating sensing and driving, its preparation method and application, relate to the technical field of flexible smart driving and sensing materials. The paper is soaked in the graphene oxide solution, dried and then soaked repeatedly to obtain the paper-based graphene oxide film; the paper-based graphene film with an asymmetric structure is formed by reduction in hydroiodic acid. The invention can be used for intelligent wearable sensors, bionic flowers, temperature sensors, bionic crawling robots, etc. for detecting human physiological signals. At the same time, it can be prepared as a multi-functional intelligent wearable device integrating sensing and driving, and at the same time, it can be used for human body activities. It has many functions such as perception and photodeformation, and has a good application prospect in the field of flexible intelligent bionic devices.

Description

technical field [0001] The invention relates to the technical field of flexible intelligent drive and sensing materials, in particular to an asymmetric structure paper-based graphene intelligent film integrating sensing and drive, a preparation method and an application. Background technique [0002] At present, smart materials have become a research hotspot in the field of bionics. They are mainly used in the two fields of flexible sensing and bionic driving. They can sense external stimuli and give feedback signals in time. It is a new type of functional material. . Different from the traditional sensing and driving methods, new bionic flexible devices based on smart materials have a simple structure and energy conversion method, thus becoming a research hotspot in the field of bionics. Among them, multifunctional smart materials with sensing and actuating properties are becoming the focus of research, and they have important research value and broad application prospects...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61B5/11A61B5/00D21H17/70
CPCA61B5/1118A61B5/6801D21H17/70
Inventor 胡颖黄马静井壮齐珂杨露露常龙飞刘家琴翟华吴玉程
Owner HEFEI UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com