Environment-friendly warm mix asphalt regenerant and preparation method thereof

A warm-mix asphalt and regenerant technology, applied in building insulation materials, sustainable manufacturing/processing, climate sustainability, etc., can solve the problems of poor diffusion of asphalt regenerant materials and high mixing temperature

Active Publication Date: 2022-05-27
HARBIN INST OF TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide an environment-friendly warm-mix asphalt rejuvenator and its preparation method in order to solve the problems of poor diffusion effect and high mixing temperature of the existing asphalt rejuvenator materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly warm mix asphalt regenerant and preparation method thereof
  • Environment-friendly warm mix asphalt regenerant and preparation method thereof
  • Environment-friendly warm mix asphalt regenerant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0018] Specific embodiment one: the present embodiment of environmentally friendly warm mix asphalt regeneration agent according to the number of mass parts by 20 ~ 50 parts of biological asphalt, 20 ~ 50 parts of epoxy soybean oil, 10 ~ 15 parts of curing agent, 5 ~ 10 parts of straw fiber and 10 ~ 15 parts of epoxy resin mixed.

specific Embodiment approach 2

[0019] Specific embodiment two: the present embodiment and the specific embodiment of a different biological asphalt is refined vegetable oil production after the production of plant asphalt.

specific Embodiment approach 3

[0020]Specific embodiment three: the present embodiment and the specific embodiment of one or two different is the curing agent is a modified fatty amine curing agent.

[0021] The present embodiment adopts a modified fatty amine curing agent at room temperature can be cured with epoxy resin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an environment-friendly warm-mix asphalt rejuvenator and a preparation method thereof. The invention belongs to the field of road engineering and aims to solve the problems of poor diffusion effect of existing asphalt rejuvenator materials and high mixing temperature. Preparation method: 1. Weigh bio-asphalt, epoxidized soybean oil, curing agent, straw fiber and epoxy resin as raw materials; 2. Put bio-asphalt in the raw material in a reactor, add curing agent, Stir evenly at high temperature to obtain a mixture, add epoxidized soybean oil in the raw material, stir at a temperature of 50-60°C, add straw fiber, and continue stirring at a temperature of 50-60°C to obtain an effective component of the regenerant; The effective components of the agent are mixed with the epoxy resin in the raw material. The invention adopts bio-asphalt and other effective components to restore the performance of aged asphalt, enhances the diffusion effect through epoxy soybean oil, and realizes the warm-mix production of recycled asphalt mixture, and the production process is simple and energy-saving.

Description

Technical field [0001] The present invention belongs to the field of road engineering, specifically relates to an environmentally friendly warm-mix asphalt regeneration agent and a preparation method thereof. Background [0002] By the end of 2018, the total length of China's highways reached 4.8465 million kilometers, of which the highway maintenance mileage accounted for 98.2% of the total highway mileage, while the secondary and above highway mileage reached 647,800 kilometers, of which a considerable part of the use of asphalt concrete pavement, so that tens of millions of tons of waste asphalt mixture (RAP) will be generated every year due to road maintenance and repair projects. At present, the comprehensive disposal of RAP is gradually becoming an important research content for the sustainable development of the transportation field, and the "Outline for the Construction of a Transportation Powerhouse" also points out that "to promote the conservation and intensive utiliza...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L91/00C08L97/02C08L63/00
CPCC08L91/00C08L95/00C08L2205/035C08L2205/16C08L97/02C08L63/00Y02A30/30Y02P20/10
Inventor 冯德成裴忠实易军艳许勐王东升
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com