Fiber-reinforced composite material molding apparatus and method for manufacturing fiber-reinforced composite material molded article

A composite material, fiber reinforced technology, applied in the direction of coating, can solve the problems of appearance, quality degradation, resin composition curability, heat resistance, adhesion, etc., to achieve excellent mold release, abrasion resistance, etc. Excellent scratch resistance, the effect of suppressing the reduction of mold release properties

Active Publication Date: 2020-11-03
MITSUBISHI CHEM CORP
View PDF14 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the above method is used, there are problems that the release agent transfers to the surface of the molded product, degrading the appearance and quality, and when the adhesive or paint is applied to the molded product, their adhesiveness decreases.
However, when a release agent is added to a fiber-reinforced composite material, the curability and heat resistance of the resin composition decrease

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber-reinforced composite material molding apparatus and method for manufacturing fiber-reinforced composite material molded article
  • Fiber-reinforced composite material molding apparatus and method for manufacturing fiber-reinforced composite material molded article
  • Fiber-reinforced composite material molding apparatus and method for manufacturing fiber-reinforced composite material molded article

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0141] The processed surface of a mirror-finished metal plate (SUS304, thickness 6 mm, 100 mm × 100 mm square) was subjected to surface treatment by implanting fluorine into a chromium nitride film by a plasma-assisted sputtering (PBS) process (TS Nanocoat) ( Surface treatment A1).

Embodiment 2

[0143] Surface treatment (surface treatment B) by CERTESS N-S (registered trademark) coating (manufactured by TS Nanocoat) was performed on the machined surface of a mirror-finished metal plate (SUS304, thickness 6 mm, 100 mm×100 mm square).

Embodiment 3

[0145] The processed surface of a mirror-finished metal plate (SUS304, thickness 6 mm, 100 mm × 100 mm square) was subjected to surface treatment by implanting fluorine into a chromium nitride film by a plasma-assisted sputtering (PBS) process (TS Nanocoat) ( Surface treatment A2).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface free energyaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Login to View More

Abstract

Provided are a molding apparatus and method for manufacturing a fiber-reinforced composite material molded article that exhibits superior molded article releasability and superior abrasion resistancein areas of molded surfaces that have been imparted with releasability, and are capable of suppressing reductions in releasability. The fiber-reinforced composite material molding apparatus (101) comprises a mold (130) for molding a fiber-reinforced composite material, in which a fiber-reinforced base material is impregnated with a resin composition, to obtain a fiber-reinforced composite materialmolded article. Some or all cavity surfaces (113a), (123a) of the mold (13) have a surface free energy of 25.0 mJ / m<2> or less as measured via a three-liquid method. It is preferable that some or allof the cavity surfaces (113a), (123a) be injection surfaces through which fluorine and / or silicon are injected.

Description

technical field [0001] The present invention relates to a molding device of fiber-reinforced composite materials and a method for manufacturing molded articles of fiber-reinforced composite materials. [0002] This application claims priority based on Japanese Patent Application No. 2018-061742 filed in Japan on March 28, 2018, and the contents thereof are incorporated herein. Background technique [0003] For fiber-reinforced composite materials as intermediate materials for lightweight and highly rigid fiber-reinforced composite molded articles, there are known prepregs in which continuous fibers made of carbon fibers are impregnated with a resin composition, dispersed with A sheet molding compound (SMC) or a punched sheet impregnated with a resin composition in a fiber base material of short fibers formed of carbon fibers. [0004] As a method of manufacturing fiber-reinforced composite molded articles, a method of laminating a plurality of prepregs and molding them in a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C70/46B29C70/18B29C70/68C08J5/04
CPCB29C70/46B29C70/54C08J2363/00B29C33/56C08J5/243B29C33/60B29C70/18B29C70/681B29K2063/00B29K2105/0872B29K2307/04B29K2907/00
Inventor 市野正洋高野恒男浅田史朗
Owner MITSUBISHI CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com