Ceramic tile with natural granular sensation and preparation method thereof

A grainy, ceramic tile technology, applied in the field of building materials, can solve the problems that affect people's use experience and insufficient tactile feeling, and achieve the effect of good tactile feeling, good anti-skid effect and high friction coefficient

Active Publication Date: 2020-12-22
GUANGDONG OVERLAND CERAMICS CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the ceramic tiles on the market are not enough to touch, which seriously affects people's use experience

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic tile with natural granular sensation and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A ceramic brick with a natural granular feel, made of the following raw materials in parts by weight: 18 parts of mullite, 12 parts of cordierite, 9 parts of granular composition, 8 parts of kaolin, 6 parts of modified coal gangue powder, 5 parts Wollastonite, 4 parts of α-alumina, 4 parts of calcium oxide, 3 parts of calcium silicate, 2.5 parts of boron trioxide, 2 parts of silica sol, 1.5 parts of methyl cellulose.

[0032] The granular composition is made of the following raw materials in parts by weight: 15 parts of calcite, 12 parts of pyrophyllite, and 8 parts of silicon micropowder.

[0033] The preparation method of described modified coal gangue powder is:

[0034] Add 30 parts of coal gangue powder to 170 parts of nitric acid solution, stir at 80°C at 100 rpm for 45 minutes, filter, and dry to obtain pretreated coal gangue powder;

[0035] Take 15 parts of pretreated coal gangue powder and add them to 185 parts of deionized water, add 0.2 parts of silane coup...

Embodiment 2

[0045] A ceramic brick with a natural granular feel, made of the following raw materials in parts by weight: 15 parts of mullite, 8 parts of cordierite, 8 parts of granular composition, 6 parts of kaolin, 4 parts of modified coal gangue powder, 4 parts Wollastonite, 2 parts of α-alumina, 2 parts of calcium oxide, 2 parts of calcium silicate, 1 part of boron trioxide, 1 part of silica sol, 0.5 part of methyl cellulose.

[0046] The granular composition is made of the following raw materials in parts by weight: 15 parts of calcite, 12 parts of pyrophyllite, and 8 parts of silicon micropowder.

[0047] The preparation method of described modified coal gangue powder is:

[0048] Add 30 parts of coal gangue powder to 170 parts of nitric acid solution, stir at 80°C at 100 rpm for 45 minutes, filter, and dry to obtain pretreated coal gangue powder;

[0049] Take 15 parts of pretreated coal gangue powder and add them to 185 parts of deionized water, add 0.2 parts of silane coupling a...

Embodiment 3

[0059] A ceramic tile with a natural granular feel, made of the following raw materials in parts by weight: 25 parts of mullite, 15 parts of cordierite, 15 parts of granular composition, 12 parts of kaolin, 8 parts of modified coal gangue powder, 8 parts Wollastonite, 6 parts of α-alumina, 6 parts of calcium oxide, 5 parts of calcium silicate, 4 parts of boron trioxide, 4 parts of silica sol, and 2 parts of methyl cellulose.

[0060] The granular composition is made of the following raw materials in parts by weight: 15 parts of calcite, 12 parts of pyrophyllite, and 8 parts of silicon micropowder.

[0061] The preparation method of described modified coal gangue powder is:

[0062] Add 30 parts of coal gangue powder to 170 parts of nitric acid solution, stir at 80°C at 100 rpm for 45 minutes, filter, and dry to obtain pretreated coal gangue powder;

[0063] Take 15 parts of pretreated coal gangue powder and add them to 185 parts of deionized water, add 0.2 parts of silane cou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic tile with natural granular sensation and a preparation method thereof. The ceramic tile is prepared from the following raw materials in parts by weight: 15-25 parts of mullite, 8-15 parts of cordierite, 8-15 parts of granular composition, 6-12 parts of kaolin, 4-8 parts of modified coal gangue powder, 4-8 parts of wollastonite, 2-6 parts of alpha- aluminum oxide,2-6 parts of calcium oxide, 2-5 parts of calcium silicate, 1-4 parts of diboron trioxide, 1-4 parts of silica sol and 0.5-2 part of methyl cellulose. The ceramic tile disclosed by the invention has the advantages of natural granular sensation, good touch feeling, high friction coefficient, good anti-skid effect and very high breaking strength.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a ceramic brick with natural graininess and a preparation method thereof. Background technique [0002] The emergence of ceramics is one of the important processes in the history of human civilization. It is the first time that human beings borrowed natural objects and created a new tool that can be used according to individual will. With the continuous progress of society, people's living standards continue to improve. , people's demand for ceramics is not only satisfied with the level of function and value, more and more consumers focus on the tactile experience. At present, the ceramic tiles on the market have insufficient tactility, which seriously affects people's use experience. Contents of the invention [0003] The invention provides a ceramic brick with a natural grainy feel and a preparation method thereof. The ceramic brick has a natural grainy feel, good touch and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/185C04B35/622C04B35/626C04B35/636
CPCC04B35/185C04B35/622C04B35/62204C04B35/626C04B35/62605C04B35/636C04B35/6365C04B2235/3208C04B2235/3217C04B2235/3409C04B2235/3418C04B2235/3454C04B2235/3481C04B2235/349C04B2235/6562C04B2235/6567C04B2235/96
Inventor 麦文英汪加武叶建明王礼石献忠卢佩玉
Owner GUANGDONG OVERLAND CERAMICS CO LTD