Method for ozonizing organic matters in wastewater by using activated carbon structured catalyst

A technology of structured catalyst and activated carbon, applied in physical/chemical process catalysts, chemical instruments and methods, metal/metal oxide/metal hydroxide catalysts, etc. Problems such as large pressure drop in the bed

Pending Publication Date: 2021-02-26
BEIJING UNIV OF CHEM TECH
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The present invention aims to provide a method for ozonating organic matter in waste water with activated carbon structured cataly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for ozonizing organic matters in wastewater by using activated carbon structured catalyst
  • Method for ozonizing organic matters in wastewater by using activated carbon structured catalyst
  • Method for ozonizing organic matters in wastewater by using activated carbon structured catalyst

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0038]Example 1

[0039]This embodiment provides a method for preparing the activated carbon structured catalyst C1.

[0040]Step (1): Take 5 cylindrical honeycomb activated carbons with a diameter of 50 mm and a length of 100 mm, and wash them with deionized water to remove the floating dust on the surface. Put the washed honeycomb activated carbon into an oven and dry it at 110°C for 6 hours. Here, the wall thickness of the honeycomb activated carbon is 1mm, the shape of the honeycomb pores is square, and the volume density is 0.35g / cm3~0.60g / cm3, The specific surface area is 500m2 / g.

[0041]Step (2): Load 1 wt% Zr and 1 wt% Ce based on the quality of honeycomb activated carbon. The weight of the dried honeycomb activated carbon was weighed to be 291.22 g, and 1 mL of solution was absorbed per 1 g of honeycomb activated carbon, and 39.73 g of zirconium nitrate pentahydrate and 26.16 g of cerium nitrate hexahydrate were weighed to prepare 850 mL of impregnating solution.

[0042]Step (3): Imm...

Example Embodiment

[0043]Example 2

[0044]This embodiment provides a method for preparing the activated carbon structured catalyst C2.

[0045]Step (1): Take 5 cylindrical honeycomb activated carbons with a diameter of 50 mm and a length of 100 mm, and wash them with deionized water to remove the floating dust on the surface. Put the washed honeycomb activated carbon into an oven and dry it at 110°C for 6 hours. Here, the wall thickness of the honeycomb activated carbon is 1mm, the shape of the honeycomb pores is square, and the volume density is 0.35g / cm3~0.60g / cm3, The specific surface area is 500m2 / g.

[0046]Step (2): Load 2wt% Zr and 2wt% Ce based on the quality of honeycomb activated carbon. The weight of the dried honeycomb activated carbon was weighed to be 290 g, and 1 mL of solution was absorbed per 1 g of honeycomb activated carbon, and 79.13 g of zirconium nitrate pentahydrate and 52.10 g of cerium nitrate hexahydrate were weighed out to prepare 850 mL of impregnation solution.

[0047]Step (3): Imme...

Example Embodiment

[0048]Experimental example 1

[0049]The activated carbon structured catalysts C1 and C2 prepared in Example 1 and Example 2 were used to catalyze the ozone oxidation of methylene blue wastewater.

[0050]Before the experiment, the activated carbon structured catalyst was immersed in wastewater to make it fully absorbed and reduce the influence of activated carbon adsorption on the experimental results. The activated carbon structured catalysts C1 and C2 were respectively filled into the ozone reaction column, the filling volume was 980 mL, and the filling height was 50 cm (the inner diameter of the reactor is 5 cm, the overall diameter of the honeycomb catalyst is 5 cm, and the porous block catalyst is placed axially. Wastewater and ozone are continuously added from the bottom at the same time, and continuously flowed out from the upper outlet), the methylene blue wastewater concentration is 500mg / L, the influent volume is 2L / h, the ozone concentration of the influent is changed, and the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for ozonizing organic matters in wastewater by using an activated carbon structured catalyst, and belongs to the technical field of sewage purification. The catalyst is composed of a carrier, an active component and an auxiliary agent, the carrier is honeycomb activated carbon, the active component is one or more of Mn, Fe, Co, Ni, Cu, Zn, Y and Zr, and the auxiliary agent is one or more of La and Ce. The preparation method comprises the following steps: (1) washing and drying the carrier; (2) preparing an impregnation liquid containing the active component andthe auxiliary agent; (3) placing the carrier in the impregnation liquid for impregnation to obtain a catalyst precursor; and (4) washing, drying and calcining the catalyst precursor to obtain the activated carbon structured catalyst. The catalyst is applied to treatment of organic wastewater, has the characteristics of small bed pressure drop, uniform gas distribution, small internal diffusion resistance, high COD removal rate and the like, and has a good application prospect.

Description

technical field [0001] The invention relates to the field of wastewater treatment and catalysts, and mainly relates to a method for using an activated carbon structured catalyst to ozonate organic matter in wastewater, belonging to the technical field of sewage purification. [0002] technical background [0003] In the process of social development, a large amount of wastewater will inevitably be produced, and some wastewater will be discharged into surrounding rivers and underground without treatment, causing serious pollution to water bodies. The types and contents of organic matter in different types of wastewater are different. Compared with other pollutants, the treatment process of organic matter in wastewater is more difficult and complicated. At present, the commonly used wastewater organic matter treatment methods include biological and chemical methods. The biological method can use organisms to degrade the organic matter in the wastewater into small molecular sub...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J23/10B01J35/04C02F1/72C02F1/78C02F101/38
CPCB01J23/10B01J35/04C02F1/78C02F1/725B01J35/1071B01J35/1066C02F2209/08C02F2101/40C02F2101/30
Inventor 雷志刚朱吉钦王乐超桂成敏易珊
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap