A kind of low dielectric loss high frequency transmission lcp film and preparation method thereof

A high-frequency transmission and low-dielectric technology, applied in the field of LCP film production equipment, can solve the problems of inconvenient two-way rotation production, unfavorable processing output, unfavorable production operations, etc., to achieve convenient and fast stretching settings, convenient transmission work, and convenient dislocation output effect

Active Publication Date: 2021-12-24
温州维蒂威科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] There is a phenomenon that it is not convenient to carry out rapid two-way rotation production, which is not conducive to centralized production operations, which will cause certain inconvenience in operation. At the same time, there is also the fact that the inner end is not convenient for the production of the overall output, which is not conducive to the integrated processing output. Improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low dielectric loss high frequency transmission lcp film and preparation method thereof
  • A kind of low dielectric loss high frequency transmission lcp film and preparation method thereof
  • A kind of low dielectric loss high frequency transmission lcp film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A low dielectric loss high-frequency transmission LCP film, prepared from the following raw materials in parts by weight: 90 parts of functional liquid crystal polymers, 14 parts of conductive particles, 17 parts of vinyl ester resin, 56 parts of polyethylene glycol, methyl 32 parts of silicone rubber, 3 parts of dioctyl phthalate, 2 parts of graphene, 1.3 parts of p-phenylenediamine, 0.7 parts of antimony trioxide and 6 parts of γ-aminopropyl triethoxysilane.

[0055] A kind of preparation method of low dielectric loss high-frequency transmission LCP film, such as figure 1 shown, including the following steps:

[0056] a. Prepare functional liquid crystal polymers. The functional liquid crystal polymers are shell-type liquid crystal polymers, the main chain is polyacrylate, and the side groups are phenyl ester mesogens. There is a carbonyl group between the side groups and the flexible side chains. Spacer;

[0057] a. Prepare conductive particles, add the mixed acid ...

Embodiment 2

[0073] On the basis of Example 1, such as Figure 12 As shown, the first workpiece 16 also includes a connecting rod 38 and a contact collar 39, the connecting rod 38 is fixedly connected to the side end position of the material inlet 21, and the side end position of the connecting rod 38 is in phase with the contact collar 39. Fixed connection.

[0074] When this embodiment is in use, the user can help to fix the connecting rod 38 through the setting of the contact collar 39, and the contact collar 39 is used for the side limit work of entering and exiting the membrane body, so as to realize the rapid movement of the membrane body. For production and cooling processing, the connecting rod 38 can help to erect and fix the feeding interface 21, realize mutual connection, and help to perform better processing and production operations.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-dielectric-loss high-frequency transmission LCP film, which is prepared from the following raw materials by weight: 80-120 parts of functional liquid crystal polymer, 12-20 parts of conductive particles, 15-20 parts of vinyl ester resin, 50-60 parts of polyethylene glycol, 30-40 parts of methyl silicone rubber, 2-5 parts of dioctyl phthalate, 1-3 parts of graphene, 1.2-1.6 parts of p-phenylenediamine, antimony trioxide 0.6-0.9 parts and 4-7 parts of γ-aminopropyltriethoxysilane; the low dielectric loss high-frequency transmission LCP film produced by the formula ratio of the present invention has an unusually regular fibrous structure and stable dimensions Excellent performance, low molding shrinkage, very small coefficient of thermal expansion, and low dielectric loss. It has important application value in the fields of electronics, electricity, optical fibers, automobiles and 5G communications.

Description

technical field [0001] The invention relates to the technical field of LCP film production equipment, in particular to a low dielectric loss high-frequency transmission LCP film and a preparation method thereof. Background technique [0002] According to Chinese Patent No. CN111909405A, the present invention relates to the technical field of LCP film, specifically relates to the high-frequency transmission LCP film and its preparation method and application, the preparation method of the high-frequency transmission LCP film comprises the following steps: the processing device (1) will contain Acetylation reaction of hydroxyaromatic monomer and acetic anhydride to obtain acetylated product; connecting device (2) melt polycondensation of acetylated product, aromatic diacid monomer and PET to obtain prepolymer; number average molecular weight is below 10000 ; Stable components (3) add acrylic resin to the prepolymer for solid-state polymerization to obtain liquid crystal polyme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J5/18C08L33/04C08L63/10C08L83/04C08L71/02C08K3/04C08K3/22C08K5/544
CPCC08J5/18C08J2333/04C08J2463/10C08J2483/04C08J2471/02C08K3/042C08K3/2279C08K5/544
Inventor 林钱杰
Owner 温州维蒂威科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap