Glass forming device and forming method of large-diameter neodymium-doped phosphate laser glass

A technology of glass forming and neodymium phosphate, applied in glass forming, glass manufacturing equipment, manufacturing tools, etc., can solve problems such as glass surface cracks, and achieve the effect of preventing excessive temperature

Active Publication Date: 2022-02-15
CDGM GLASS LLC
View PDF18 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a glass forming device, which aims to solve the problem that the moisture in the air is easily converted into OH in the process of forming large-diameter neodymium-doped phosphate laser glass in the existing glass forming device. - The form enters the surface and subsurface layers of the glass, causing cracks on the glass surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass forming device and forming method of large-diameter neodymium-doped phosphate laser glass
  • Glass forming device and forming method of large-diameter neodymium-doped phosphate laser glass
  • Glass forming device and forming method of large-diameter neodymium-doped phosphate laser glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] A large-diameter neodymium-doped phosphate laser glass is formed, and the process is as follows:

[0058] Firstly, the above-mentioned glass forming device is selected as the equipment for forming large-diameter neodymium-doped phosphate laser glass 800;

[0059] Secondly, the discharge end of the glass leaking tube 700 is penetrated into the forming cavity 600 through the leaking tube hole 410 and corresponds to the rear guide surface of the plug 300; then the annealing furnace is set on the rear side of the glass forming device , and corresponds to the rear end of the molding cavity 600;

[0060] Next, the protective gas is continuously introduced into the molding cavity 600 through the protective gas pipeline 500, and the flow rate of the introduced protective gas is controlled at 40L / h;

[0061] Next, the molten glass at 990°C in the discharge tank is sent into the molding cavity 600 through the glass leaking tube 700, the temperature of the molten glass flowing ou...

Embodiment 2

[0065] A large-diameter neodymium-doped phosphate laser glass is formed, and the process is as follows:

[0066] Firstly, the above-mentioned glass forming device is selected as the equipment for forming large-diameter neodymium-doped phosphate laser glass 800;

[0067] Secondly, the discharge end of the glass leaking tube 700 is inserted into the molding cavity 600 through the leaking tube hole 410 and corresponds to the rear guide surface of the plug 300;

[0068] Next, the protective gas is continuously introduced into the molding cavity 600 through the protective gas pipeline 500, and the flow rate of the introduced protective gas is controlled at 90L / h;

[0069] Then, through the glass leakage pipe 700, the glass liquid at 980°C in the discharge tank is sent into the molding cavity 600, and the temperature of the glass liquid flowing out of the glass leakage pipe 700 is 930°C, and the temperature on the left and right sides of the forming chamber 600 Heating is carried o...

Embodiment 3

[0073] A large-diameter neodymium-doped phosphate laser glass is formed, and the process is as follows:

[0074] Firstly, the above-mentioned glass forming device is selected as the equipment for forming large-diameter neodymium-doped phosphate laser glass 800;

[0075] Secondly, the discharge end of the glass leaking tube 700 is penetrated into the forming cavity 600 through the leaking tube hole 410 and corresponds to the rear guide surface of the plug 300; then the annealing furnace is set on the rear side of the glass forming device , and corresponds to the rear end of the molding cavity 600;

[0076] Next, the protective gas is continuously introduced into the molding cavity 600 through the protective gas pipeline 500, and the flow rate of the introduced protective gas is controlled at 60L / h;

[0077] Next, the molten glass at 990°C in the discharge tank is sent into the molding cavity 600 through the glass leaking tube 700, and the temperature of the molten glass flowin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of glass forming, and specifically discloses a glass forming device and a forming method of large-diameter neodymium-doped phosphate laser glass, aiming at ensuring the glass forming effect and basically avoiding glass surface cracks caused by moisture in the air. The glass forming device can make the surrounding forming cavity as closed as possible by setting the cover plate, and the protective gas can be introduced into the forming cavity through the set protective gas pipeline to drive away the air in the forming cavity and form a protection for the glass liquid to be formed. prevent moisture in the air from OH ‑ The form re-enters the surface and sub-surface layers of the glass, basically avoiding the occurrence of cracks on the glass surface; at the same time, by distributing the preheating pipe section of the protective gas pipeline on the surface of the cover plate, the heat transmitted by the cover plate can be used Preheat the protective gas to prevent the temperature of the protective gas from being too low to cause a large disturbance to the molding temperature in the molding cavity and affect the normal molding of the glass.

Description

technical field [0001] The invention belongs to the technical field of glass forming, and in particular relates to a glass forming device and a forming method of large-diameter neodymium-doped phosphate laser glass. Background technique [0002] Neodymium-doped phosphate laser glass is a glass-based solid-state laser material, which is widely used in various types of solid-state lasers, and is the main laser material for high-power and high-energy lasers. In order to improve the fluorescence lifetime and quantum rate, reduce the non-radiative energy transition, and improve the system gain capability, the OH in the glass needs to be eliminated during the Nd-doped phosphate laser glass melting process. - . [0003] At present, Nd-doped phosphate laser glass is formed by glass forming equipment. Existing glass forming device generally comprises bottom mold, two side molds that are respectively arranged on the left and right sides of bottom mold, and the plug that is arranged ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03B19/00
CPCC03B19/00
Inventor 苏学剑莫大洪原保平于天来
Owner CDGM GLASS LLC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap