A kind of modified ethylene-methyl acrylate copolymer and its preparation method and application

A technology of methyl acrylate and copolymer, which is applied in the field of modified ethylene-methyl acrylate copolymer and its preparation, and can solve the problem of the adjustment of the preparation process of ethylene-methyl acrylate copolymer, the difference and influence of product molecular weight and its branching condition Grafting or compounding process can be effectively carried out, etc., to achieve excellent mechanical properties and corrosion resistance, high melting point, and increase the number of effects

Active Publication Date: 2022-06-03
安徽清澜新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the modification method provided by this patent is relatively complicated, and a wide variety of raw materials need to be used, and the products modified according to this method are mainly used in cable sheathing materials. It is necessary to redesign the corresponding modification method so that the prepared modified ethylene-methyl acrylate meets the performance requirements of the reverse osmosis membrane support material
[0004] In addition, the current modification of ethylene-methyl acrylate copolymers is mainly based on the grafting or compounding of existing ethylene-methyl acrylate copolymers, and the preparation process of ethylene-methyl acrylate copolymers has not been adjusted.
However, as a copolymer of ethylene-methyl acrylate, the molecular weight and branching of the product obtained by polymerization under different conditions will have large differences, which will affect the effective progress of the grafting or compounding process, resulting in the actual modification effect not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of modified ethylene-methyl acrylate copolymer and its preparation method and application
  • A kind of modified ethylene-methyl acrylate copolymer and its preparation method and application
  • A kind of modified ethylene-methyl acrylate copolymer and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

Embodiment 1

Embodiment 2~11 and comparative example 1~3

[0071]

[0074]

[0075]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
tensile strengthaaaaaaaaaa
corrosion potentialaaaaaaaaaa
Login to View More

Abstract

The invention provides a modified ethylene-methyl acrylate copolymer and its preparation method and application. The present invention obtains an ethylene-methyl acrylate copolymer by preparing a nickel complex catalyst, and utilizing the catalyst to efficiently catalyze the copolymerization process of ethylene and methyl acrylate; and by combining the ethylene-methyl acrylate copolymer and silicon dioxide The nanoparticles were reacted with vinyltrimethoxysilane and then blended and crosslinked to prepare the modified ethylene-methyl acrylate copolymer. Through the above method, the present invention can utilize the catalyst to regulate and control the structure and performance of the ethylene-methyl acrylate copolymer, so as to promote the modification process to be carried out efficiently, so that the obtained modified ethylene-methyl acrylate copolymer has a higher Melting point, excellent mechanical properties and corrosion resistance, can be applied to reverse osmosis membrane support materials, and has high practical application value.

Description

A kind of modified ethylene-methyl acrylate copolymer and its preparation method and application technical field The present invention relates to the synthesis and modification technical field of multipolymer, relate in particular to a kind of modified ethylene-methyl acrylate Copolymer and its preparation method and application. Background technique Ethylene-methyl acrylate copolymer is to take ethylene as main raw material, and it is copolymerized with polar monomer methyl acrylate The obtained product has excellent thermal stability, filling, flexibility, cohesion and good compatibility. Extrusion, sheet, molding, blow molding, extrusion and other fields are widely used. However, the performance of raw materials in different fields of application The requirements are not consistent, and the ethylene-methyl acrylate copolymer prepared by the general method is difficult to completely match the requirements of various fields. Therefore, it is necessary to modify t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G83/00B01D69/10
CPCC08G83/001B01D69/10Y02P20/52
Inventor 楼钱吴立群游军
Owner 安徽清澜新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products