A kind of gh4098 alloy plate and its preparation method

An alloy sheet and alloy technology, applied in the field of GH4098 alloy sheet and its preparation

Active Publication Date: 2022-05-03
PANGANG GROUP JIANGYOU CHANGCHENG SPECIAL STEEL
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the performance of GH4098 alloy plate still needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of gh4098 alloy plate and its preparation method
  • A kind of gh4098 alloy plate and its preparation method
  • A kind of gh4098 alloy plate and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0059] The invention provides a method for preparing a GH4098 alloy plate, comprising:

[0060] Carry out vacuum induction melting and vacuum self-consumption melting of alloy raw materials to obtain steel ingots;

[0061] Forging, rolling and heat treating the steel ingot to obtain GH4098 alloy plate;

[0062] The composition of the alloy raw material is:

[0063] 0.02-0.04wt% C;

[0064] 17.5-19.5wt% Cr;

[0065] 6-6.5wt% W;

[0066] 4~5wt% Mo;

[0067] 2.5-3.0wt% Al;

[0068] 1.0-1.5wt% Ti;

[0069] 6~7wt% Co;

[0070] 0.65-0.85wt% Nb;

[0071] 0.03~0.05wt% Mg;

[0072] ≤0.35wt% Si;

[0073] ≤0.30wt% Mn;

[0074] ≤0.015wt% S;

[0075] ≤0.015wt% of P;

[0076] ≤0.7wt% Fe;

[0077] 0.003~0.005wt% B;

[0078] 0.01-0.02wt% Ce;

[0079] ≤0.07wt% Cu;

[0080] The balance is Ni.

[0081]In the present invention, the composition of the alloy raw material is the composition of the alloy raw material after batching. The mass content of C in the alloy raw material is...

Embodiment 1

[0163] Prepare a GH4098 alloy plate with a thickness of 1.0 mm according to the following method:

[0164] Vacuum induction melting and vacuum self-consumption melting of alloy raw materials in sequence to obtain steel ingots;

[0165] Forging, rolling and heat treating the steel ingot to obtain GH4098 alloy plate;

[0166] The composition after described alloy raw material batching is:

[0167]

[0168]

[0169] During the vacuum induction smelting process, the vacuum degree of the vacuum induction furnace is less than 1Pa, and the electric chemical material can only be fed when the equipment is operating normally; the power can be adjusted at any time according to the situation in the furnace during melting, and the samples are analyzed after Al, Ti, J-Nb are added. The composition is adjusted according to the optimal requirements. Before adding J-Ce, electrolytic Mn and Ni-Mg, it needs to be properly adjusted and filled with argon;

[0170] Pouring after the vacuum ...

Embodiment 2

[0184] Prepare a GH4098 alloy plate with a thickness of 2.0 mm according to the following method:

[0185] Vacuum induction melting and vacuum self-consumption melting of alloy raw materials in sequence to obtain steel ingots;

[0186] Forging, rolling and heat treating the steel ingot to obtain GH4098 alloy plate;

[0187] The composition after described alloy raw material batching is:

[0188]

[0189]

[0190] During the vacuum induction smelting process, the vacuum degree of the vacuum induction furnace is less than 1Pa, and the electric chemical material can only be fed when the equipment is operating normally; the power can be adjusted at any time according to the situation in the furnace during melting, and the samples are analyzed after Al, Ti, J-Nb are added. The composition is adjusted according to the optimal requirements. Before adding J-Ce, electrolytic Mn and Ni-Mg, it needs to be properly adjusted and filled with argon;

[0191] Pouring after the vacuum ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a GH4098 alloy plate, which comprises: vacuum induction melting and vacuum consumable melting of alloy raw materials to obtain a steel ingot; forging, rolling and heat treatment of the steel ingot to obtain a GH4098 alloy plate. The invention adopts a new preparation method of GH4098 (GH98) alloy, so that the performance of GH4098 (GH98) alloy plate is qualified, meets the standard requirements, improves product quality, creates more economic benefits for enterprises, and makes greater contributions to national defense. . The invention also provides a GH4098 alloy plate.

Description

technical field [0001] The invention belongs to the technical field of alloy plates, in particular to a GH4098 alloy plate and a preparation method thereof. Background technique [0002] Due to the accelerated upgrading of the aviation industry, high-temperature alloy plates with better performance are required to replace old alloy grades such as GH3044, GH3128, GH536, etc. When GH4098 (GH98) is used below 950°C, it has high strength and plasticity, and is mainly used as a load-bearing part for working conditions below 950°C. But the performance of GH4098 alloy plate still needs to be further improved. Contents of the invention [0003] In view of this, the object of the present invention is to provide a GH4098 alloy plate and a preparation method thereof. The GH4098 alloy plate prepared by the method provided by the present invention has better properties. [0004] The invention provides a method for preparing a GH4098 alloy plate, comprising: [0005] Vacuum induction...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/02C22C19/05B21C37/02B21J5/00C22F1/10
CPCC22C1/023C22C19/056B21C37/02B21J5/002C22F1/10
Inventor 魏育君裴丙红何云华付建辉王正虎江敦超孙永福韩福柳滢
Owner PANGANG GROUP JIANGYOU CHANGCHENG SPECIAL STEEL
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com