TMCP steel plate tail plate shape control method

A shape control, steel plate technology, applied in the direction of contour control, etc., can solve the unfavorable problems such as uniform transition of cooling temperature at the end of the steel plate, bulging, and uneven cooling of the end of the steel plate

Pending Publication Date: 2021-11-09
BAOSTEEL ZHANJIANG IRON & STEEL CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is a phenomenon in the production process. After the steel plate is rolled by the rough and finish rolling mills, and the rolled steel plate is cooled by MULPIC according to the flow rate calculated by the model and the speed of the plate, the tail of the steel plate appears bulging, warping, and down. Buckle and other bad phenomena seriously affect the production efficiency of the finishing line
[0004] In terms of controlling the shape of the tail of the steel plate, the existing methods are mainly: 1) MULPIC adopts the method of micro-acceleration, and the conveying speed of the steel plate in the MULPIC is gradually accelerated, so as to avoid the tail of the steel plate being overcooled, thereby affecting the shape of the tail of the steel plate However, the heating system of the steel plate is different due to different batches. Under the influence of the rapid rolling rhythm, the heating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TMCP steel plate tail plate shape control method
  • TMCP steel plate tail plate shape control method
  • TMCP steel plate tail plate shape control method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment ( 1

[0049] Steel plate specification: 20.28x2447x29554mm, grade: Q420C T, the main process parameters are as follows Table 1:

[0050] Table 1

[0051]

[0052]

Embodiment ( 2

[0054] Steel plate specification: 24.01x3312x26485mm, grade: Q345qD, the main process parameters are as follows Table 2:

[0055] Table 2

[0056]

[0057]

[0058] Through the application of the present invention, the flatness of the tail of the steel plate in embodiment (1) and embodiment (2) is good, and the unevenness of the tail of the steel plate is controlled at 5-10mm / m.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a TMCP steel plate tail plate shape control method. The method comprises the following steps that S1, in a heating process stage, tapping temperature and in-furnace time are set according to the thickness of a steel plate; S2, in the rough rolling process stage, the reduction rate, the rolling speed and the accelerated speed of the final pass are controlled; S3, between the rough rolling process stage and the finish rolling process stage, the temperature waiting time of the steel plate is controlled according to the thickness of the steel plate, the rolling starting temperature of the steel plate in the finish rolling process stage is increased, and the temperature waiting time is shortened; S4, in the finish rolling process stage, the reduction rate, the rolling speed and the accelerated speed of the final pass are controlled; and S5, in the MULPIC online cooling process stage, shielding parameters of the tail of the steel plate are set according to the thickness of the steel plate. Through reasonable steel plate heating, rough rolling process, finish rolling process and MULPIC online cooling process, supercooling of the tail plate shape of the steel plate is avoided, the transition uniformity of the tail temperature of the steel plate is improved, the good tail plate shape of the steel plate is obtained after the steel plate is cooled by the MULPIC, and the influence of the poor tail plate shape on the subsequent production efficiency of the steel plate is reduced.

Description

technical field [0001] The invention belongs to the technical field of shape control of a thick TMCP steel plate, and in particular relates to a method for controlling the shape of a tail of a TMCP steel plate. Background technique [0002] TMCP steel plate is a steel plate produced by TMCP technology, which is one of the microstructure control technologies that combine controlled rolling and controlled cooling to obtain excellent properties of steel plate, such as high strength, excellent toughness and weldability, etc. [0003] At present, the Zhanjiang 4200mm production line is vigorously promoting the "replacing gold with water". In the case of adding a small amount of alloy, the high-temperature plate rolled by the finishing mill is cooled by using the online rapid cooling device (MULPIC). The variable method obtains good comprehensive performance. However, there is a phenomenon in the production process. After the steel plate is rolled by the rough and finish rolling ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21B37/28B21B37/44
CPCB21B37/28B21B37/44
Inventor 薛如锋陈国锋陈建恩
Owner BAOSTEEL ZHANJIANG IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products