Graphene fiber-containing blended fabric and preparation method thereof

A technology of graphene fibers and blended fabrics, applied in animal fibers, fiber processing, textiles and papermaking, etc., can solve problems such as poor antibacterial performance, achieve low yarn CV value, good antibacterial and antistatic properties, strength and good gloss effect

Pending Publication Date: 2021-12-07
广东云裳科技有限公司 +1
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Silk fiber has a wide range of applications in the textile field, but its strength and antibacterial properties are poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene fiber-containing blended fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A blended fabric containing graphene fibers in this embodiment, the fabric is prepared from silk fibers and graphene fibers, wherein the silk fibers are pretreated, and the pretreatment is to mix polyether Nonionic antistatic agent solution is evenly sprayed on the silk fiber, the quality of antistatic agent is 0.3% of silk fiber, the quality of water in antistatic agent solution is 4% of silk fiber, according to mass percentage, silk fiber 70%, graphite 30% vinyl fiber, stacked for 24 hours.

[0054] The preparation method of the blended fabric containing graphene fiber of the present embodiment, comprises the steps:

[0055] (1) according to mass percentage, take silk fiber and graphene fiber, silk fiber is carried out pretreatment according to described method;

[0056] (2) the pretreated silk fiber is made into sliver by CZ231 type stretching machine, CZ241 type sliver making machine, CZ251 type drawing frame and carry out merging, carding, obtain the first kind of...

Embodiment 2

[0060] A blended fabric containing graphene fibers in this embodiment, the fabric is prepared from silk fibers and graphene fibers, wherein the silk fibers are pretreated, and the pretreatment is to mix polyether Nonionic antistatic agent solution is evenly sprayed on the silk fiber, the quality of antistatic agent is 0.4% of silk fiber, the quality of water in antistatic agent solution is 5% of silk fiber, according to mass percentage, silk fiber 80%, graphite 20% vinyl fiber, stacked for 36 hours.

[0061] The preparation method of the blended fabric containing graphene fibers of this embodiment is the same as that of Example 1.

Embodiment 3

[0063] A blended fabric containing graphene fibers in this embodiment, the fabric is prepared from silk fibers and graphene fibers, wherein the silk fibers are pretreated, and the pretreatment is to mix polyether Nonionic antistatic agent solution is evenly sprayed on the silk fiber, the quality of antistatic agent is 0.5% of silk fiber, the quality of water in the antistatic agent solution is 6% of silk fiber, according to mass percentage, silk fiber 90%, graphite 10% vinyl fiber, stacked for 48 hours.

[0064] The preparation method of the blended fabric containing graphene fibers of this embodiment is the same as that of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a graphene fiber-containing blended fabric and a preparation method thereof. The fabric is prepared from silk fibers and graphene fibers, wherein the silk fibers are pretreated, and the pretreatment comprises the steps of uniformly spraying an antistatic agent solution on the silk fibers and stacking for 24-48 hours. The prepared blended fabric has the characteristics of real silk and also has the good antibacterial property and antistatic property of the graphene fibers; due to the fact that the graphene fibers have a certain color, the fabric can no longer be dyed, various properties of the fabric are still obvious after the fabric is washed for multiple times, and meanwhile, the elasticity, the comfort level and the health care effect are improved; a drawing frame is adopted for multiple times, so that the fibers in the fabric are evenly mixed, the CV value of yarn is low, and the luster is even; and a compact spinning frame, an automatic winder and a singeing frame are adopted, so that hairiness and defects in the fabric are few, and the strength and luster of the fabric are good.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a blended fabric containing graphene fibers and a preparation method thereof. Background technique [0002] Blended or blended chemical fiber fabrics are textile products made of chemical fibers mixed with other cotton wool, silk, hemp and other natural fibers. It has both the style of polyester and the advantages of cotton fabrics, such as polyester cotton cloth and polyester wool gabardine. Blending is divided into wool-viscose blending, sheep and rabbit wool spinning, TR fabrics, high-density NC fabrics, 3M waterproof mousse fabrics, TENCEL fabrics, Rousai silk, TNC fabrics, composite fabrics, etc. [0003] Nanoscale graphene oxide sheets can be spun into macroscopic graphene fibers several meters long. The resulting fibers are not only strong but also tough enough to be knotted or woven into conductive mats. Such fibers could be a key material for realizing the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/14D06M15/53D06M101/10
CPCD04B1/14D06M15/53D10B2211/04D10B2101/12D06M2101/10
Inventor 杨玉杰赖伟彬
Owner 广东云裳科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com