Splitting method for electronic-grade glass fiber cloth and product thereof

A glass fiber cloth, electronic-grade technology, applied to the fiber-opening method of electronic-grade glass fiber cloth and its product field, can solve the problems that the thickness cannot be further reduced, the number of defective products increases, the texture of glass fiber yarn is brittle, etc. Reduced defective products, reduced pressure required for spunlace, and high fluidity

Pending Publication Date: 2022-01-18
SHANGHAI GRACE FABRIC
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the brittle texture of the glass fiber yarn, the excessive water pressure of the spray will cause the yarn to break and burr, and there will also be obvious strip marks on the surface of the glass fiber cloth, resulting in an increase in the number of defective products, and the thickness cannot be further reduced.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Splitting method for electronic-grade glass fiber cloth and product thereof
  • Splitting method for electronic-grade glass fiber cloth and product thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] This example provides an electronic-grade glass fiber cloth, which adopts the technical means of combining liquid carbon dioxide pre-fiber opening and hydroentanglement fiber opening. The specific preparation method is as follows:

[0053] Step S0: Install the 1080 glass fiber cloth on the sending end of the machine, click the start button, and the glass fiber cloth starts to be conveyed forward;

[0054] Step S1: Glass fiber cloth enters liquid CO 2 Pre-opening area, open liquid CO 2 Jet pump switch, liquid CO 2 The liquid carbon dioxide injection rod 1 is evenly distributed between the glass fiber cloth yarn bundles, and starts to gasify and expand, and the suction pipe 5 also starts to work, extracting the volatilized CO 2 The gas will pass through the compression equipment and become liquid CO again 2 And store it up, then the glass fiber cloth passes through the constant temperature water bath 2 along the first guide roller 3 and the second guide roller 4, so th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a glass yarn splitting method for electronic-grade glass fiber cloth and a product thereof. The splitting method comprises the following steps of S1, uniformly spraying liquid carbon dioxide on the glass fiber cloth, and obtaining pre-split glass fiber cloth through a constant-temperature water bath; and S2, carrying out spunlace splitting treatment on the pre-split glass fiber cloth to obtain the split glass fiber cloth. According to the splitting method for the electronic-grade glass fiber cloth provided by the invention, liquid carbon dioxide pre-splitting is applied before a spunlace splitting method, so that the surface of the glass fiber cloth is uniform and flat, and the thickness is greatly reduced.

Description

technical field [0001] The invention relates to the technical field of electronic grade non-alkali glass fiber cloth, in particular to a fiber opening method for electronic grade glass fiber cloth and its products. Background technique [0002] With the advent of the 5G era, the electronics industry is developing very rapidly, and electronic product terminals are becoming smaller and thinner. Therefore, the PCB circuit boards used in the production of electronic products must also be thinner and better, and the production of PCB circuit boards is the most The original electronic material is electronic-grade glass fiber cloth, so the glass fiber cloth should be made lighter and thinner, with a smoother appearance. [0003] In the existing production process of electronic grade glass fiber cloth, the original cylindrical glass yarn is hit and dispersed into a flat ribbon structure by the high-pressure water jet ejected from the jet plate, thereby reducing the thickness of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D02J1/18D04H18/04
CPCD02J1/18D04H18/04
Inventor 张驰刘名金李云华
Owner SHANGHAI GRACE FABRIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products