Flat hammering and drawing formation method for abrasive ball

A technology of flat anvils and grinding balls, which is applied to other household appliances, household appliances, household components, etc., can solve the problems of reduced working life, difficult expansion of production scale, and failure, and achieves uniform and reasonable distribution, reduced size and quantity, and casting The effect of changing the characteristics of the state organization

Inactive Publication Date: 2005-09-07
TAIYUAN UNIV OF TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the 1990s, my country's steel mold ball casting technology made a breakthrough, giving full play to the advantages of high-chromium cast iron materials. Its products have been widely promoted in China, and its impact toughness index has increased to nearly 8 joules / cm 2 , but the investment in the continuous casting-rolling production line is huge, there are many technically influencing factors, the casting defects with many holes and gaps in the center of the product have not been effectively eliminated, the utilization rate of molten iron is not high, and the production scale is difficult to expand
For the alloying ratio of high-chromium as-cast grinding balls, substantial progress has been made in the theoretical and applied research of casting molding and heat treatment, but the impact toughness values ​​of as-cast high-chromium grinding balls are generally low. Cracks often occur and fail, reducing the working life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The present invention relates to a flat anvil extension-forming method of a grinding ball, which is a kind of iron-based high-chromium alloy containing various alloy elements as a raw material, which is gradually formed by casting, forging and heat treatment processes. The mechanical processing method, specifically, is a kind of iron-based high-chromium high-carbon alloy containing chromium, carbon, molybdenum, vanadium, manganese, silicon, rare earth and its alloy elements as raw material, which is first cast into a blank for forging, During the forging process, the billet is subjected to high-temperature thermoplastic deformation to gradually improve the as-cast structure and shape of the billet, and finally formed into a grinding ball whose internal structure is not completely as-cast and whose shape meets the specification requirements. After heat treatment, it is manufactured into a grinding ball for ball mill. The steps of its manufacturing method are:

[0018] ① ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
hardnessaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The present invention discloses a flat hammering and drawing formation process of abrasive ball as a kind of grinding material. Into iron-base material, Cr, C, Mo, V, Mn, Si, RE and other alloy elements are added to form alloy material, which are passed through smelting, casting, cutting, flat hammering and drawing deformation, forging, post-forging treatment to produce the various kinds of abrasive ball. The abrasive ball product has diameter 30-140 mm, ellipticity less than 3 mm, impact toughness over 10 joule / sq cm, and breaking rate less than 0.35%. It is used widely in grinding Fe, Ag, Al, Cu and other metal ore powder as well as coal, quartz, various ceramic powder and other non-metal ore powder with microhardness lower than 1000 Hv.

Description

technical field [0001] The invention belongs to the scope of preparation of grinding materials, in particular to a flat anvil-digging-forming method of grinding balls. Background technique [0002] There are many kinds of grinding balls, and their chemical composition is an important factor to determine their performance. Therefore, they are divided into cast or forged grinding balls made of iron with carbon, silicon, manganese and other elements. The interior of the manganese steel grinding ball mainly made of high manganese steel is mainly Fe-C type carbide, which has low microhardness and poor wear resistance; there are inevitably holes, segregation and shape errors during casting, and it is difficult to achieve broken balls. The requirements for using the two indicators of rate and out-of-roundness. The most popular high-chromium cast iron wear-resistant material is suitable for making industrial ore powder and other industries with impact wear parts, but its impact tou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21K23/00
Inventor 李晋敏张贵成曹晓卿
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap