Luminous artificial slabstone and its production process

A technology for plate production and artificial stone, which is applied in the field of building decoration materials to achieve the effects of wide application, simple process and low manufacturing cost

Inactive Publication Date: 2003-11-05
上海康尔家具材料有限公司
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing light storage powder is generally mixed with paint, ink, and resin, and is not used on artificial boards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] Luminous artificial stone plate and production method thereof, taking the production of white corn-colored plate as an example, first make color granules according to the existing technology for use;

[0009] The second step is to make light-storing luminescent particles: 20kg of unsaturated resin, 27kg of aluminum hydroxide powder, 7kg of colored light-storing luminescent powder, and 650g of composite color paste. The amount of composite color paste can be determined according to the color of the color particles in the required board. , the amount of addition can be more or less; according to the temperature and humidity requirements, the accelerator cobalt naphthenate is 0.5-1.8% (accounting for the amount of resin), the curing agent methyl ethyl ketone peroxide is 0.6-2% (accounting for the amount of resin), stirring and mixing for 5 minutes, Put it upside down on the mold, enter the vacuum box to vacuum, leave the box for 5 minutes, let it completely solidify, about ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention belongs to building decorating material and is especially one kind of luminous artificial slabstone material and its production process. The production process has one increased light accumulating luminous particle making step, and the luminous artificial slabstone material is produced with unsaturated resin, aluminum hydroxide powder, color light accumulating luminous powder, composite color slurry, promoter and cure agent, and through mixing, vacuum molding for complete curing, crushing and sieving. Artificial slabstone made of the said material can glow with rather bright light for several hours after being irradiated for decades minutes.

Description

technical field [0001] The invention belongs to a building decoration material, in particular to a self-storing luminous artificial stone plate and a production method thereof. Background technique [0002] The production process of the existing artificial marble slabs is as follows: firstly, granulation: use 17-20kg of unsaturated resin, 25-30kg of talc powder and aluminum hydroxide powder, 1-3000g of composite color paste, and according to the requirements of temperature and humidity, accelerator (Cobalt naphthenate) accounts for 0.5-1.8% of the unsaturated resin, curing agent (methyl ethyl ketone peroxide) accounts for 0.6-2% of the unsaturated resin, mix and stir the above, pour it on the mold after five minutes, and enter the vacuum box Carry out overall vacuum and evacuation, leave the box in five minutes, let it completely solidify and reach a Barcol hardness of 35-40°, then crush and sieve to make granules of various colors and sizes for use. The particles are 4-8 m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J5/18
Inventor 詹永柳
Owner 上海康尔家具材料有限公司