Super-tough nylon and preparation method thereof

A nylon and super-tough technology, which is applied in the field of preparing the above-mentioned super-tough nylon, can solve problems such as difficult to meet the requirements of dimensional stability and easy to produce deformation, so as to improve dimensional stability, reduce molding shrinkage, increase rigidity and dimensional stability Effect

Active Publication Date: 2011-07-20
广东顺威赛特工程塑料开发有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When preparing products with relatively large wall thickness or large pieces, deformation is easy to occur, and it is difficult to meet the occasions that require high dimensional stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super-tough nylon and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Take the following components by weight percentage:

[0021] Nylon 6 55%

[0022] Ultra-fine barium sulfate 20%

[0023] POE-g-MAH 24%

[0024] Antioxidant 1010 0.1%

[0025] Antioxidant 168 0.5%

[0026] Lubricant TAF 0.4%

[0027] Mix nylon 6 resin, ultra-fine barium sulfate, POE-g-MAH, antioxidant 1010, antioxidant 168, and lubricant TAF fully and evenly under a high-speed mixer. The speed of the high-speed mixer is 300 rpm. The final material is put into the twin-screw extruder, the screw speed is 200 rpm, the material is fully melted and compounded in the twin-screw extruder, extruded through the head, drawn, cooled in the cooling tank, and passed through the cutting machine Cut into pellets and dry in a vacuum box at 80°C for 24 hours to obtain the product of the present invention.

Embodiment 2

[0029] Take the following components by weight percentage:

[0030] Nylon 6 64%

[0031] Ultra-fine barium sulfate 15%

[0032] POE-g-MAH 20%

[0033] Antioxidant 1010 0.2%

[0034] Antioxidant 168 0.3%

[0035] Lubricant TAF 0.5%

[0036] Mix nylon 6 resin, ultra-fine barium sulfate, POE-g-MAH, antioxidant 1010, antioxidant 168, and lubricant TAF fully and evenly under a high-speed mixer. The speed of the high-speed mixer is 300 rpm. The final material is put into the twin-screw extruder, the screw speed is 200 rpm, the material is fully melted and compounded in the twin-screw extruder, extruded through the head, drawn, cooled in the cooling tank, and passed through the cutting machine Cut into pellets and dry in a vacuum box at 80°C for 24 hours to obtain the product of the present invention.

[0037] Example 2

[0038] Take the following components by weight percentage:

[0039] Nylon 6 75%

[0040] Ultra-fine barium sulfate 5%

[0041] POE-g-MAH 19%

[0042] Ant...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses super-tough nylon. The super-tough nylon is characterized by comprising the following components by weight: 55 to 75 percent of nylon 6, 5 to 15 percent of ultra-fine barium sulfate, 10 to 20 percent of POE-g-MAH, 0.1 to 0.3 percent of antioxidant 1010, 0.2 to 0.5 percent of antioxidant 168, and 0.3 to 0.7 percent of lubricant TAF. A method for preparing the super-tough nylon is characterized by comprising the following steps that the nylon 6 resin, the ultra-fine barium sulfate, the POE-g-MAH, the antioxidant 1010, the antioxidant 168 and the lubricant TAF are mixed well, put into a double-screw extruder, fully melted and compounded in the double-screw extruder, extruded through a nose, pulled into strips, cooled, palletized, dried and packaged. The invention aimsto overcome the deficiencies of the prior art and provide the super-tough nylon with low mold shrinkage and good dimensional stability. Another aim of the invention is to provide a method for preparing the super-tough nylon.

Description

technical field [0001] The invention relates to a super-tough nylon, in particular to a super-tough nylon with low molding shrinkage and good dimensional stability, and also relates to a method for preparing the super-tough nylon. Background technique [0002] Polyamide (commonly referred to as nylon) is the base resin with the largest output, the most variety, the widest application and excellent comprehensive performance among the five general-purpose engineering plastics. Nylon has outstanding performance in terms of bending strength, wear resistance, creep resistance, electrical properties, etc., but most nylon varieties are not ideal in low temperature resistance and toughness, so it affects the application in outdoor applications such as railway equipment and auto parts. . [0003] As a major variety of modified nylon, super-tough nylon is mainly prepared by adding rubber elastomer, thermoplastic elastomer, metallocene polyolefin, etc., and blending through a twin-scr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K3/30B29B9/06C08L77/00C08K13/02
Inventor 王成望汪克风陶巍刘志忠
Owner 广东顺威赛特工程塑料开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com