X70QS seamless line pipe with HIC (Hydrogen Induced Cracking) resistance

A seamless line pipe, performance technology, applied in the field of corrosion-resistant materials and seamless pipes, can solve the problems of undefined steel grades and wide composition ranges, and achieve good HIC resistance, high strength, and low yield ratio Effect

Active Publication Date: 2012-06-20
TIANJIN STEEL PIPE MFG CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN1914341A discloses "Pipeline steel with excellent HIC resistance and pipeline pipe made of this steel". In this invention, the composition range of C, Mn, etc. affecting strength is too wide, and there is no clear steel grade
High-strength (≥485MPa) seamless line pipes with HIC resistance have not been reported yet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • X70QS seamless line pipe with HIC (Hydrogen Induced Cracking) resistance
  • X70QS seamless line pipe with HIC (Hydrogen Induced Cracking) resistance
  • X70QS seamless line pipe with HIC (Hydrogen Induced Cracking) resistance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The X70QS seamless line pipe with anti-HIC performance of the present invention will be described with reference to the drawings and examples.

[0012] The X70QS seamless line pipe with HIC resistance performance of the present invention, the composition weight % of the seamless line pipe is C 0.06-0.14%, Si 0.20-0.45%, Mn 1.00-1.30%, P≤0.015%, S≤ 0.003%, Ni≤0.10%, Cu≤0.20%, Cr 0.05~0.30%, Mo0.05~0.30%, Al 0.015~0.060%, N 0.003~0.010%, Nb 0.030~0.050%, V0.05~0.09% , Ca≤0.060%, the balance is Fe and impurities; carbon equivalent CEpcm≤0.22%, CEIIW≤0.39%.

[0013] Cr and Mo in the composition are alloying elements and V and Nb are microalloying elements, and the addition amount is Cr+Mo≥0.15%, Cr+Mo+Mn≤1.80%, V+Nb≥0.09%.

[0014] It has good HIC resistance under yield strength ≥ 485MPa, crack sensitivity rate CSR ≤ 2%, crack length rate ≤ 10%, crack thickness rate CTR ≤ 3%.

[0015] The specific optimized chemical composition of the present invention is described as fol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides an X70QS seamless line pipe with HIC (Hydrogen Induced Cracking) resistance, comprising the following components in weight by percentage: 0.06%-0.14% of C, 0.20%-0.45% of Si, 1.00%-1.30% of Mn, P not more than 0.015%, S not more than 0.003%, 0.05%-0.30% of Cr, 0.05%-0.30% of Mo, 0.015%-0.060% of Al, 0.003%-0.010% of N, 0.030%-0.050% of Nb, 0.05%-0.09% of V, not more than 0.10% of Ni, not more than 0.20% of Cu and the balance of Fe and impurities, wherein Ni and Cu which have limited content are residual element in the steel, the carbon equivalent CEpcm is not more than 0.22%, and CEIIW is not more than 0.39%. The X70QS seamless line pipe has the advantages of high strength and excellent impact performance and can ensure the impact power to be greater than 150J at -40 DEG C, which is much higher than the impact power standard values of the API (American Petroleum Institute) and the ISO (International Standards Organization); by controlling the CE and the PCM (Pulse-Code Modulation), the X70QS seamless line pipe qualitatively ensures better welding performance; the X70QS seamless line pipe has the advantages of high ductility, low yield ratio and high elongation; and the X70QS seamless line pipe has favorable HIC resistance, thereby ensuring that when the yield strength is greater than 485 MPa, the crack-sensitive rate CSR is not greater than 2%, the crack-length rate is not greater than 10%, and the crack-thickness rate CTR is not greater than 3%.

Description

technical field [0001] The invention relates to the field of corrosion-resistant materials and seamless pipes, in particular to high-grade, high-strength (≥485MPa) seamless line pipes with HIC resistance. Background technique [0002] In recent years, with the increasingly harsh conditions of oil and gas exploitation, the requirements for gathering and transportation pipelines necessary for exploitation have been continuously improved, not only the requirements for steel grades have increased, but also the properties of materials have been improved to meet the requirements of conveying media and processes. Variety. Pipelines with HIC resistance are the materials with the highest performance requirements among pipeline steels. The products are required to have ultra-low sulfur content, shape control of inclusions, uniform structure, and low hardness. The composition process design of this type of steel, Both the control level of smelting and rolling put forward very high req...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/48C22C38/26
Inventor 李艳许文妍李毅孙宇郑飞王庆国赵兴亮吕传涛
Owner TIANJIN STEEL PIPE MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com